A high-pressure fuel injection pipe of doubled type, comprising: a thick outer tube; and an inner tube of made a metal and fitted in the outer tube to form a doubled pipe which is formed at its end portion with a connecting head having a face to be fitted on a seat of a mating partner. The outer tube is made of stainless steel or titanium, and the inner tube is formed of a thin metal having a high corrosion-resistance and a high strength and is doubled on the inner circumference of the outer tube throughout its entire length.

Description

11 parts

›This application is a continuation of application Ser…

This application is a continuation of application Ser. No. 08/614,947, filed Mar. 11, 1996, now abandoned which is continuation of Ser. No. 08/337,316 filed Nov. 10, 1994, which is a continuation of Ser. No. 08/043,350 filed Apr. 6, 1993 now abandoned.

›BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a high-pressure, fuel injection pipe having a relatively small diameter such as 15 mm or less, which is to be connected to the individual nozzle holders of a cylinder head for a fuel passage and a fuel pump.

2. Description of the Prior Art

The prior art includes a high-pressure fuel injection pipe which is doubled by fitting an inner tube of stainless steel on the inner circumference of a thick steel tube throughout the whole length, with a view to preventing cavitation erosion or corrosion (as will be shortly called the “erosion”) on the inner circumference, which erosion is caused by the injection pressure of the fuel which has become higher in recent years. The pipe material thus prepared is formed at its end portion with a connecting head for providing a face to be fitted on the seat of a mating partner, thus producing the injection pipe.

In the prior art described above, the erosion on the inner circumference can be prevented by the construction of the inner tube of stainless steel fitted on the inner circumference of the thick steel pipe. However, the fitted face formed on the connecting head is not sufficiently kept away from the erosion. Especially in case of using methanol as the fuel in recent years, the fitted face is chemically corroded. On the other hand, the outer circumference is plated with zinc for preventing it from being rusted. Especially the internal combustion engine using methanol has to anticipate frequent assemblies and disassemblies for its maintenance. As a result, there arises a problem that the plated metal film is peeled or that the fitted face is damaged or deformed by the more or less forcible assembly.

›SUMMARY OF THE INVENTION

The present invention has been conceived in view of the above-specified problems accompanying the prior art and has an object to provide a high-pressure fuel injection pipe which is enabled to prevent any erosion effectively not only on the inner circumference but also on the fitted face, to free the fitted face from being damaged or deformed by the forced assembly, to eliminate any plating treatment of the outer circumference of the injection pipe for the rust prevention, and to free the fitted face from any chemical corrosion even if methanol is used as the fuel, by fitting an inner tube of a highly corrosion resisting and highly strong metal on the inner circumference of a thick outer metal and by making the outer tube of a metal having a corrosion resistance, a high strength and an excellent fatigue resistance such as stainless steel or titanium.

In order to achieve the above-specified object, according to the present invention, there is provided a high-pressure fuel injection pipe of doubled type, comprising: a thick outer tube; and an inner tube of made a metal and fitted in said outer tube to form a doubled pipe which is formed at its end portion with a connecting head having a face to be fitted on a seat of a mating partner, wherein the improvement resides: in that said outer tube is made of stainless steel or titanium; and in that said inner tube is formed of a thin metal having a high corrosion-resistance and a high strength and is doubled on the inner circumference of said outer tube throughout its entire length. The metal inner tube is made of stainless steel, a nickel based alloy, titanium or a titanium alloy.

According to the present invention, the thick outer tube of stainless steel or titanium and the metal inner tube of high corrosion resistance and high strength are doubly drawn by an integral reduction, with the inner tube being loosely fitted in the inner circumference of the outer tube, so that they are diametrically reduced in their entirety and are fixedly doubled. After this, this doubled pipe is formed at its end portion with a connecting head. For these treatments, the outer tube is made of a metal having a corrosion resistance, a strength and an excellent fatigue resistance such as stainless steel or titanium, and the inner tube is made of a material having a high corrosion resistance and a high strength such as: stainless steel; a nickel based alloy such as Inconel, Incoloy or Hastelloy; titanium; or a titanium alloy. As a result, the erosion can be prevented not only on the inner circumference but also on the fitted face of the connecting head at the end portion even if an alcohol fuel having a low boiling point and liable to cause an erosion is injected under a high pressure. Moreover, the fitted face can be freed from being damaged or deformed even if the injection pipe is more or less forcibly assembled. At the same time, the outer face as the injection pipe need be neither made corrosion-resistant nor plated in the least. Moreover, not only the inner circumference but also the fitted face is freed from any chemical corrosion even if the fuel used is methanol. Thus, the connection can be stabilized and ensured for a long time, and the vibration resistance can be drastically improved to provide a injection pipe for a long use.

In case the outer tube is made of titanium, the injection pipe can find a suitable use in a marine Diesel engine which is required to have a corrosion resistance to seawater and which has its natural frequency (or resonant point) increased to have a wide range of using R.P.M. and a high load fluctuation.

›BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 ( a ) is a section showing one embodiment of a high-pressure fuel injection pipe according to an embodiment of the present invention;

FIG. 1 ( b ) is a partially cut-away side elevation showing another embodiment; and

FIG. 2 is a partially cut-away longitudinal section for explaining one doubling drawing step of a method for manufacturing an injection pipe of the present invention.

›DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention will be described in the following in connection with its embodiments with reference to FIGS. 1 and 2. Designated at reference numeral 1 is an outer tube which has a thick wall and a relatively small diameter of about 15 mm or less and which is made stainless steel or titanium. In this outer tube 1 , there is fitted a metal inner tube 3 which is extended throughout the whole length of the circumference of the whole of the outer tube 1 having a diameter of about 4 mm or less, to form a doubled pipe. This inner tube 3 is made of a highly corrosion resisting and highly strong metal such as: stainless steel having a thickness of about 0.3 mm to 1.2 mm; a nickel based alloy such as Inconel, Incoloy or Hastelloy; titanium; or a titanium alloy such as 6Al4V, 6Al6V2Sn, 6Al2Sn4Zr2Mo or 8Al1Mo1V. The pipe material has its end portion pressed, as customary, to form a connecting head 2 thereby to construct the high-pressure fuel injection pipe. This connecting head 2 is given a frusto-conical shape (as shown in FIG. 1 ( a )), an arcuate shape or a diamond shape (as shown in FIG. 1 ( b )).

Designated at reference numeral 4 is a sleeve washer which is fitted, if necessary, on the neck of the connecting head 2 at the end portion. At the same time, there is assembled with the back of the sleeve washer 4 a fastening nut 5 for fastening the connecting head 2 into abutment against with the seat of a mating injection nozzle injection holder or the like (although not shown).

›Examples6

›EXAMPLE 1

An outer tube of SUS304 (having an external diameter of 15.0 mm, an internal diameter of 10.2 mm and a thickness of 2.4 mm) was cleaned by a pretreatment and cut to a length of 3,200 mm. A metal inner tube of SUS304 (having an external diameter of 9.0 mm, an internal diameter of 7.8 mm and a thickness of 0.6 mm) was also cleaned by a pretreatment and cut to a length of 3,200 mm. The inner tube.thus prepared was inserted and fitted in the outer tube. Next, as shown in FIG. 2, a fixed die 6 was used to perform a doubling drawing two times by an integral reduction in one direction, as indicated by arrow, to reduce the entire assembly diametrically of its whole length. After this, a correction was performed to manufacture an injection pipe material having an external diameter of 8.0 mm, an internal diameter of 2.8 mm, a thickness of 2.6 mm and a hardness of about 350 Hv at its inner circumference. After this, the injection pipe material was cut to a product length of 750 mm. This injection pipe was pressed at its end portion to form a frusto-conical connecting head (having an external diameter of 11.5 mm, a height of 7.0 mm and an angle of cone of 58 degrees). Then, the product including its face to be fitted was bent with the metal outer tube covering, to produce the fuel injection pipe.

›EXAMPLE 2

An outer tube of SUS304 (having an external diameter of 12.0 mm, an internal diameter of 7.0 mm and a thickness of 2.5 mm) and an inner tube of Inconel 601 (having an external diameter of 6.8 mm, an internal diameter of 5.8 mm and a thickness of 0.5 mm) were subjected to the pretreatment of Example 1 and were cut to an equal length. Those outer tube and inner tube were subjected to a treatment similar to that of Example 1 to produce an injection pipe material having an external diameter of 7.0 mm, an internal diameter of 2.2 mm, a thickness of 2.4 mm and a hardness of about 380 Hv at its inner circumference.

After this, a connecting head was formed like Example 1, and the intermediate product was bent to produce a fuel injection pipe.

›EXAMPLE 3

An outer tube of pure titanium (having an external diameter of 9.3 mm, an internal diameter of 5.3 mm and a thickness of 2.0 mm) was cleaned by a pretreatment and cut to a length of 2,000 mm. A metal inner tube of a titanium alloy 6Al4V (having an external diameter of 4.5 mm, an internal diameter of 3.5 mm and a thickness of 0.5 mm) was also cleaned by a pretreatment and cut to a length of 2,500 mm. The inner tube thus prepared was inserted and fitted in the outer tube. Next, as shown in FIG. 2, the fixed die 6 was used to perform a doubling drawings two times by an integral reduction in one direction, as indicated by arrow, to reduce the entire assembly diametrically of its whole length. After this, a correction was performed to manufacture an injection pipe material having an external diameter of 6.4 mm, an internal diameter of 2.0 mm, a thickness of 2.2 mm and a hardness of about 340 Hv at its inner circumference. After this, the injection pipe material was cut to a product length of 830 mm. This injection pipe was pressed at its end portion to form a diamond-shaped connecting head (having an external diameter of 8.7 mm, a height of 4.8 mm and an angle of cone of 58 degrees). Then, the product including its face to be fitted was bent with the metal outer tube covering, to produce the fuel injection pipe.

›EXAMPLE 4

An outer tube of pure titanium and an inner tube of pure titanium, both having an equal size and cut to an equal length to those of Example 3, were subjected to the pretreatment of Example 3 and then to a treatment similar to that of Example 3 to produce an injection pipe material having an external diameter of 6.4 mm, an internal diameter of 2.0 mm, a thickness of 2.2 mm and a hardness of about 280 Hv at its inner circumference.

After this, a connecting head was formed like Example 3, and the intermediate product was bent to produce a fuel injection pipe.

›EXAMPLE 5

An outer tube of SUS316 (having an external diameter of 10.0 mm, an internal diameter of 5.5 mm and a thickness of 2.25 mm) was cleaned by a pretreatment and cut to a length of 2,300 mm. A metal inner tube of Hastelloy C-276 (having an external diameter of 4.8 mm, an internal diameter of 3.8 mm and a thickness of 0.5 mm) was also cleaned by a pretreatment and cut to a length of 3,000 mm. The inner tube thus prepared was inserted and fitted in the outer tube. Next, as shown in FIG. 2, a fixed die 6 was used to perform a doubling drawings two times by an integral reduction in one direction, as indicated by arrow, to reduce the entire assembly diametrically of its whole length. After this, a correction was performed to manufacture an injection pipe material having an external diameter of 7.0 mm, an internal diameter of 2.2 mm, a thickness of 2.4 mm and a hardness of about 390 Hv at its inner circumference. After this, the injection pipe material was cut to a product length of 1080 mm. This injection pipe was pressed at its end portion to form a frusto-conical connecting head (having an external diameter of 9.5 mm, a height of 4.0 mm and an angle of cone of 58 degrees). Then, the product including its face to be fitted was bent with the metal outer tube covering, to produce the fuel injection pipe.

›EXAMPLE 6

An outer tube of SUS316 and an inner tube of pure titanium were subjected to the pretreatment of Example 5 and were cut to an equal size and an equal length to those of Example 5. Those outer tube and inner tube were subjected to a treatment similar to that of Example 5 to produce an injection pipe material having an external diameter of 7.0 mm, an internal diameter of 2.2 mm, a thickness of 2.4 mm and a hardness of about 270 Hv at its inner circumference.

After this, a connecting head was formed like Example 5, and the intermediate product was bent to produce a fuel injection pipe.

The six samples thus produced according to the above-described six Examples and one injection pipe of the prior art having an inner tube of stainless steel fitted in a thick steel tube were prepared and were run in a special mode with 100% of methanol. The states after the run of 1,200 hours were observed.

As a result, in the pipe of the prior art, a leakage due to erosion and rust were observed on the face to be fitted. In any of the Examples of the present invention, on the contrary, neither the leakage due to erosion nor the rust was observed.

Even in case the high-pressure fuel injection pipe according to the present invention is used to inject such a fuel, e.g., alcohol fuel under a high pressure as has a low boiling point and will cause erosion, this erosion can be prevented not only on the inner circumference of the injection pipe but also on a face 2 ′ to be fitted on the mating seat. Moreover, the face to be fitted can be free from being damaged or deformed even by a forced fitting. At the same time, the injection pipe need not have its outer circumference subjected to a rust-preventing or plating treatment. Even if methanol is used as the fuel, the face 2 ′ to be fitted is freed from any chemical corrosion, and the connection can be stabilized and ensured to improve the vibration or fatigue resistance. Thus, the fuel injection pipe of the present invention can be used for a long time.

1 of 11 part labels are ours — the grant heads the rest

Claims as granted

14 claims

Classifications

5 codes

IPC · International Patent Classification

Section F — Mechanical engineering; lighting; heating; weapons

F16L58/08
F16L19/025
F02M55/02
F02B3/06

USPC · US Patent Classification

285/55

Claim changes

Soon

Coming soonHow the claims changed between publication and grant

See which claims were amended, added or cancelled during examination, with every added and removed word marked.

AmendedAddedCancelledUnchanged

The published claims of this application are not paired with the granted ones in what we hold.

File wrapper

⤢ drag to zoom

USPTOApplicanthover for detail · click to open

Pendency

6.0 y

2,185 days filing → grant

Office actions

non-final + final

Responses

3 RCE

Interviews

examiner interview summaries

Examiner

Thomas B. Will

art unit 3671 · TC 3600

Law firm

Law firm · Log in to unlock

Citations: 16 back · 7 forward

See the full prosecution history — every USPTO and applicant action on this file, in order.

Documents

Log in to open the documents of this file: the application as filed, every office action and response, the notice of allowance.

Chain of title

No assignments have been recorded for this application yet.