U.S. Pat. No. 5,310,808 to R. A. Grey describes various vinyl phosphonate derivatives which are useful in the manufacture of flame retarded thermoplastic copolymers. Various aryl group-containing vinylphosphonate species are embraced by a formula depicted at col. 3, lines 14-26 of this patent in which a linear or branched divalent hydrocarbyl radical, B, is depicted as being bonded at either end thereof to the two oxygen atoms of the moiety

with the structures —CH 2 —CH 2 — and —CH(CH 3 ) —CH 2 — being given as examples of preferred groups for B.

›SUMMARY OF THE INVENTION

The present invention are certain novel neopentylene phosphonate compounds containing, as the type of divalent group B shown in both the compounds of U.S. Pat. No. 5,310,808 and intermediates thereof, the novel divalent linkage —CH 2 —C(CH 3 ) 2 —CH 2 —.

›DESCRIPTION OF PREFERRED EMBODIMENTS

The compounds of the present invention are, for example, embraced by the formula

where: Ar is substituted or unsubstituted phenyl;

A is selected from the group consisting of hydrogen and, if conjoint with B, CH 2 ; and

B is selected from the group consisting of hydroxy, oxyacyl, and, if conjoint with A, CH 2 . It will be appreciated that having A and B conjoint as CH 2 makes the entire grouping C<A(B) a vinyl group.

A particularly preferred embodiment of the present invention relates to final compounds where the group C<A(B) does form a vinyl structure having A and B being conjoint as the moiety CH 2 . This type of compound class is exemplified by the compound neopentylene 1-phenylvinylphosphonate which has the formula:

Another embodiment of the present invention is exemplified by the class of novel intermediates for the previously described vinyl group-containing compound. One specific compound of this type is neopentylene 1-acetoxy-1-phenylethylphosphonate which is of the formula:

Yet another embodiment of the present invention is the novel intermediate compounds for the previously described 1-acetoxy containing compounds. These compounds are exemplified by the compound neopentylene 1-hydroxy-1-phenylethylphosphonate which is of the formula:

The process for forming the desired final products of the type exemplified by (I) involves the reaction of neopentylene hydrogen phosphonate with acetophenone to yield compounds as exemplified by (III) followed by acetylation with acetic anhydride to form the type of compound exemplified by (II) followed by acid-catalyzed deacetylation of (II) to form the final desired compound (I).

›Examples3

›EXAMPLE 1

This Example illustrates the synthesis of neopentylene 1-hydroxy-1-phenylethylphosphonate.

Neopentylene hydrogenphosphonate (16.0 gm, 0.107 mole), acetophenone (12.8 gm, 0.107 mole), and 16 gm of V&MP Naphtha were placed into a 100 cc nitrogen-blanketed flask. Then, 1,1,3,3-tetramethylguanidine (0.74 gm) was added at 30° C. to 50° C. in several aliquots over a period of eight hours and forty-five minutes. Crystals of the desired hydroxy adduct formed as the reaction proceeded and another 26.5 additional grams of V&MP Naphtha were added to make the slurry stirrable. The reaction mixture was then filtered, and the solid was washed two times with hexane. The yield of crystals was 90.3%, they had a melting point of 157° C. to 161.5° C., a purity of 95.2% by 31 P nmr, and δ 16.0 d 6 -DMSO.

›EXAMPLE 2

This Example shows the synthesis of neopentylene 1-acetoxy-1-phenethylphosphonate.

Initially, neopentylene 1-hydroxy-1-phenylethylphosphonate, from Example 1 (10.0 gm, 0.037 mole) and acetic anhydride (32 gm, 0.313 mole) were placed into a nitrogen blanketed reaction flask. The slurry was then vigorously stirred, and 5.4 gm of strongly acidic ion exchange resin (AMBERLYST 15 brand from Rohm & Haas Co.) were added in a single aliquot. The initially exothermic reaction (maximum temperature of 43° C.) was then allowed to cool and stand overnight. Assay of the neopentylene 1-acetoxy-1-phenylethylphosphonate in the final mixture was 88.1% by 31 P nmr and δ 10.7 d 6 -DMSO.

›EXAMPLE 3

This Example illustrates synthesis of neopentylene 1-phenylvinylphosphonate.

The crude reaction mixture from Example 2 was stirred and heated for thirty minutes at 79° C. to 90° C. The resulting slurry contained 86.9% of the desired neopentylene 1-phenylvinylphosphonate by 31 P nmr analysis. The final slurry was washed two times with 15 gm of water and filtered. The yield of air dried crystals was 75.8%, 99% purity by 31 P nmr, and δ 10.4 d 6 -DMSO.

Claims as granted

1 claim

Classifications

3 codes

IPC · International Patent Classification

Section C — Chemistry; metallurgy

C07F9/6571
C08K5/5333

USPC · US Patent Classification

525/285

Claim changes

Soon

Coming soonHow the claims changed between publication and grant

See which claims were amended, added or cancelled during examination, with every added and removed word marked.

AmendedAddedCancelledUnchanged

The published claims of this application are not paired with the granted ones in what we hold.

File wrapper

⤢ drag to zoom

USPTOApplicanthover for detail · click to open

Pendency

8.7 y

3,161 days filing → grant

Office actions

non-final + final

Responses

no RCE

Appeals

notices of appeal

Examiner

Marjorie Moran

art unit 1631 · TC 1600

Law firm

Law firm · Log in to unlock

Citations: 4 back · 0 forward

See the full prosecution history — every USPTO and applicant action on this file, in order.

Documents

Log in to open the documents of this file: the application as filed, every office action and response, the notice of allowance.

Chain of title

⤢ drag to zoom

TitleLienReleasehover for detail · click to open

See the full assignment history — every owner this patent has passed through, with recordation dates and reel/frame numbers.