Liquid crystal composition and liquid crystal display device thereof

This application claims priority to and benefit of Chinese Patent Application No. 202010413412.3 filed on May 15, 2020. The contents of the above application are hereby expressly incorporated by reference in its entirety into the present application, including the contents and teachings of any references contained therein.

The present invention relates to the field of liquid crystal, in particular to a liquid crystal composition and a liquid crystal display device comprising the liquid crystal composition.

Up to now, liquid crystal has been widely used in the field of information display, and has also made some progresses in the application of optical communication. In recent years, the application of liquid crystal compounds has been significantly expanded to display devices, electro-optical devices, electronic elements, sensors and so on.

Based on the types of display mode, liquid crystal display elements can be classified into PC (phase change), TN (twisted nematic), STN (super twisted nematic), ECB (electrically controlled birefringence), OCB (optically compensated bend), IPS (in-plane switching), VA (vertical alignment), FFS (fringe field switching), FPA (field-induced photo-reactive alignment) and so forth. Based on the driving modes of elements, liquid crystal display elements can be classified into PM (passive matrix) type and AM (active matrix) type. PM is classified into the static type, multiplex type and so forth. AM is classified into TFT (thin film transistor) type, MIM (metal insulator metal) type and so forth. The types of TFT comprise amorphous silicon and polycrystal silicon. The latter is classified into a high-temperature type and a low-temperature type according to the manufacturing process. Based on the types of light source, liquid crystal display elements can be classified into a reflection type utilizing a natural light, a transmission type utilizing a backlight, and a semi-transmission type utilizing both the natural light and the backlight.

Liquid crystal materials need to have appropriately high dielectric anisotropy and optical anisotropy as well as a good low-temperature mutual solubility. Besides, liquid crystal materials also should have a low viscosity, a shorter response time, a low threshold voltage and an appropriately high contrast ratio. Performances of the liquid crystal composition would be further explained according to the market selling liquid crystal display elements. The temperature range of nematic phase temperature range is associated with the operating temperature range of the elements. A preferred upper limit temperature of the nematic phase is 70° C. or higher and a preferred lower limit temperature of the nematic phase is about −10° C. or lower. The viscosity of the liquid crystal composition is associated with response times of the elements. It is preferred that the response time is short so as to display dynamic images. Therefore, a liquid crystal composition with a faster response speed, especially a faster response speed at low temperature, is preferred.

Response speed is an important evaluation index of liquid crystal display device. If response speed is too slow, ghosting phenomenon will occur on the display panel, especially in applications with low temperature use requirements of end customers, such as cell phones, tablet computers, display devices for outdoor work (electricity meters), aerospace display devices and light valves. And in the applications of these aspects, a widest possible use temperature range with the center of room temperature is further required. Therefore, it is also required the liquid crystal composition has a higher clearing point and a faster response at low temperature.

From the perspective of the preparation of liquid crystal materials, the performances of liquid crystal materials are interdependent, and the improvement of one performance index may make other performances change. Therefore, the preparation of liquid crystal materials with suitable performances in all aspects often requires creative labor.

Objects: In view of the deficiencies in the prior art, it is an object of the present invention to provide a liquid crystal composition having a smaller voltage change rate at high and low temperatures and a shorter low temperature response time while maintaining an appropriate optical anisotropy, an appropriate clearing point and an appropriate absolute value of dielectric anisotropy.

Another object of the present invention is to provide a liquid crystal display device comprising the above liquid crystal composition, which is especially applicable to VA, IPS or FFS display elements.

Technical Solutions

To realize the above invention objects above, the present invention provides a liquid crystal composition comprising:

at least one compound of general formula I

and

at least one compound of general formula II

in which,

R 1 and R 2 each independently represents —H, halogen, C 1-12 linear or branched alkyl,

wherein one or more nonadjacent —CH 2 — in the C 1-12 linear or branched alkyl can each be independently replaced by —CH═CH—, —C≡C—, —O—, —CO—, —CO—O— or —O—CO—, and one or more —H in aforementioned groups can each be independently substituted by —F or —Cl;

R 3 and R 4 each independently represents C 1-12 linear or branched alkyl,

wherein one or more nonadjacent —CH 2 — in the C 1-12 linear or branched alkyl can each be independently replaced by —CH═CH—, —C≡C—, —O—, —CO—, —CO—O— or —O—CO—;

ring

and ring

each independently represents

wherein one or more —CH 2 — in

can be replaced by —O—, and one or more single bond in the rings can be replaced by double bond, wherein one or more —H on

can each be independently substituted by —F, —Cl, —CN, —CH 3 or —OCH 3 , and one or more —CH═ in the rings can be replaced by —N═;

X 1 represents —O—, —S—, —CO—, —CF 2 —, —NH— or —NF—; Y 1 , Y 2 , Y 3 , Y 4 , Y 5 and Y 6 each independently represents —H, halogen, C 1-3 halogenated or unhalogenated alkyl, or C 1-3 halogenated or unhalogenated alkoxy; Z 1 and Z 2 each independently represents single bond, —O—, —S—, —CO—O—, —O—CO—, —CH 2 O—, —OCH 2 —, —CH═CH—, —C≡C—, —CH 2 CH 2 —, —CF 2 CF 2 —, —(CH 2 ) 4 —, —CF 2 O— or —OCF 2 —; and n 1 and n 2 each independently represents 0, 1 or 2, wherein when n 1 =2, ring

can be same or different, Z 1 can be same or different; wherein when n 2 =2, ring

can be same or different, Z 2 can be same or different.

In some embodiments of the present invention, preferably, X 1 represents O, S, CO or —NH—; further preferably, X 1 represents —O—, —S— or —CO—.

In some embodiments of the present invention, preferably, Y 1 and Y 2 each independently represents —H, —F, —Cl, —CH 3 , —OCH 3 , —CF 3 or —OCF 3 ; further preferably, Y 1 and Y 2 each independently represents —H, —F or —Cl.

In some embodiments of the present invention, preferably, Z 1 and Z 2 each independently represents single bond, —O—, —S—, —CO—O—, —O—CO—, —CH 2 O—, —OCH 2 —, —CH 2 CH 2 —, —CF 2 CF 2 —, —CF 2 O— or —OCF 2 —.

In some embodiments of the present invention, preferably, ring

and ring

each independently represents

In some embodiments of the present invention, the compound of general formula I is selected from a group consisting of the following compounds:

in which,

ring

is defined the same as ring

Z 1 ′ is defined the same as Z 1 ;

X 1 represents —O—, —S— or —CO—.

In some embodiments of the present invention, preferably, R 1 and R 2 each independently represents halogen, C 1-10 halogenated or unhalogenated linear or branched alkyl, C 1-9 halogenated or unhalogenated linear or branched alkoxy, C 2-10 halogenated or unhalogenated linear or branched alkenyl; further preferably, R 1 and R 2 each independently represents halogen, C 1-8 halogenated or unhalogenated linear or branched alkyl, C 1-7 halogenated or unhalogenated linear or branched alkoxy, C 2-8 halogenated or unhalogenated linear or branched alkenyl; more further preferably, R 1 and R 2 each independently represents halogen, C 1-5 halogenated or unhalogenated linear or branched alkyl, C 1-4 halogenated or unhalogenated linear or branched alkoxy, C 2-5 halogenated or unhalogenated linear or branched alkenyl.

In some embodiments of the present invention, preferably, R 1 and R 2 each independently represents —F, —Cl, C 1-5 halogenated or unhalogenated linear or branched alkyl, C 1-4 halogenated or unhalogenated linear or branched alkoxy, C 2-5 halogenated or unhalogenated linear or branched alkenyl.

In some embodiments of the present invention, in order to keep good thermal stability and light stability, R 1 and R 2 are preferably alkyl; in order to improve the dielectric anisotropy, R 1 and R 2 are preferably alkoxy; in order to keep smaller viscosity and faster response speed, R 1 and R 2 are preferably alkenyl; in order to keep smaller viscosity, wider nematic phase temperature range and faster response speed, the terminal groups of R 1 and R 2 are preferably not alkenyl, and further preferably, R 1 and R 2 are alkenyl and the terminal groups of R 1 and R 2 are alkyl.

The lower limit of the weight percentage of the compound of general formula I is 0.1%, 0.5%, 1%, 1.5%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 12%, 14% or 15%, relative to the total weight of the liquid crystal composition of the present invention; and the upper limit of the weight percentage of the compound of general formula I is 40%, 38%, 36%, 34%, 32%, 30%, 28%, 26%, 25%, 24%, 20%, 18%, 16%, 15%, 14%, 12% or 10%, relative to the total weight of the liquid crystal composition of the present invention.

In some embodiments of the present invention, the compound of general formula I provides 0.1-40 wt. % of the total weight of the liquid crystal composition; preferably, the compound of general formula I provides 0.1-25 wt. % of the total weight of the liquid crystal composition.

In some embodiments of the present invention, Y 3 , Y 4 , Y 5 and Y 6 each independently represents —H, —F, —Cl, —CH 3 , —OCH 3 , —CF 3 or —OCF 3 ; preferably, Y 3 , Y 4 , Y 5 and Y 6 each independently represents —H, —F, —Cl, —CH 3 ; further preferably, Y 3 , Y 4 , Y 5 and Y 6 each independently represents —H, —F, or —Cl.

In some embodiments of the present invention, the compound of general formula II is selected from a group consisting of the following compounds:

In some embodiments of the present invention, preferably, R 3 and R 4 each independently represents C 1-10 linear or branched alkyl, C 1-9 linear or branched alkoxy, or C 2-10 linear or branched alkenyl; further preferably, R 3 and R 4 each independently represents C 1-8 linear or branched alkyl, C 1-7 linear or branched alkoxy, or C 2-8 linear or branched alkenyl; more further preferably, R 3 and R 4 each independently represents C 1-5 linear or branched alkyl, C 1-4 linear or branched alkoxy, or C 2-5 linear or branched alkenyl.

The lower limit of the weight percentage of the compound of general formula II is 0.1%, 0.5%, 1%, 2%, 4%, 6%, 8%, 9%, 10%, 12%, 14%, 16%, 20%, 25%, 28% or 30%, relative to the total weight of the liquid crystal composition of the present invention; and the upper limit of the weight percentage of the compound of general formula II is 70%, 68%, 65%, 60%, 58%, 55%, 50%, 48%, 45%, 40%, 38%, 35%, 30%, 28% or 25%, relative to the total weight of the liquid crystal composition of the present invention.

In some embodiments of the present invention, the compound of general formula II provides 0.1-70 wt. % of the total weight of the liquid crystal composition; preferably, the compound of general formula II provides 0.1-40 wt. % of the total weight of the liquid crystal composition.

In some embodiments of the present invention, the liquid crystal composition of the present invention further comprises at least one compound of general formula III:

in which,

R 5 and R 6 each independently represents halogen, C 1-12 linear or branched alkyl,

wherein one or more nonadjacent —CH 2 — in the C 1-12 linear or branched alkyl can each be independently replaced by —CH═CH—, —C≡C—, —O—, —CO—, —CO—O— or —O—CO—, and one or more —H in aforementioned groups can each be independently substituted by —F or —Cl;

ring

and ring

each independently represents

wherein one or more —H on

and

can each be independently substituted by —F, —Cl, —CN, —CH 3 or —OCH 3 , and one or more —CH═ in the rings can be replaced by —N═;

T 1 , T 2 , T 3 , T 4 , T 5 , T 6 , T 7 and T 8 each independently represents —H, —F, —Cl, —CN, —CH 3 or —OCH 3 .

In some embodiments of the present invention, the compound of general formula III is selected from a group consisting of the following compounds:

in which,

R 5 and R 6 each independently represents C 1-10 linear or branched alkyl,

C 1-9 linear or branched alkoxy, or C 2-10 linear or branched alkenyl;

T 9 , T 10 and T 11 each independently represents —H, —F, —Cl, —CN, —CH 3 or —OCH 3 ; and X 2 represents —F, —CF 3 , —OCF 3 or —CH 2 CH 2 CH═CF 2 .

In some embodiments of the present invention, R 5 and R 6 each independently represents C 1-8 linear or branched alkyl,

C 1-7 linear or branched alkoxy, or C 2-8 linear or branched alkenyl; preferably, R 5 and R 6 each independently represents C 1-5 linear or branched alkyl,

C 1-4 linear or branched alkoxy, or C 2-5 linear or branched alkenyl.

The lower limit of the weight percentage of the compound of general formula III is 0.1%, 0.5%, 1%, 1.5%, 2%, 4%, 6%, 8%, 10%, 12%, 14%, 18%, 20% or 25%, relative to the total weight of the liquid crystal composition of the present invention; and the upper limit of the weight percentage of the compound of general formula III is 50%, 45%, 40%, 35%, 30%, 28%, 26%, 24%, 20%, 18%, 16% or 15%, relative to the total weight of the liquid crystal composition of the present invention.

In some embodiments of the present invention, the compound of general formula III provides 0.1-50 wt. % of the total weight of the liquid crystal composition; preferably, the compound of general formula III provides 0.1-30 wt. % of the total weight of the liquid crystal composition.

In some embodiments of the present invention, the liquid crystal composition further comprises at least one compound of general formula M:

in which,

R M1 and R M2 each independently represents C 1-12 linear or branched alkyl,

wherein one or more nonadjacent —CH 2 — in the C 1-12 linear or branched alkyl can each be independently replaced by —CH═CH—, —C≡C—, —O—, —CO—, —CO—O— or —O—CO—;

ring

ring

and ring

each independently represents

wherein one or more —CH 2 — in

can be replaced by —O—, one or more single bond in the ring can be replaced by double bond, wherein at most one —H on

can be substituted by halogen;

Z M1 and Z M2 each independently represents single bond, —CO—O—, —O—CO—, —CH 2 O—, —OCH 2 —, —C≡C—, —CH═CH—, —CH 2 CH 2 — or —(CH 2 ) 4 —; and n M represents 0, 1 or 2, wherein when n M =2, ring

can be same or different, Z M2 can be same or different; and

when n M =1 or 2, at least one of ring

ring

and ring

is non-aromatic ring.

The alkenyl group in the present invention is preferably selected from the groups represented by any one of formula (V1) to formula (V9), particularly formula (V1), formula (V2), formula (V8) or formula (V9). The groups represented by formula (V1) to formula (V9) are as follows:

in which, * represents bound carbon atom in the ring structure.

The alkenoxy group in the present invention is preferably selected from the groups represented by any one of formula (OV1) to formula (OV9), particularly formula (OV1), formula (OV2), formula (OV8) or formula (OV9). The groups represented by formula (OV1) to formula (OV9) are as follows:

in which, * represents bound carbon atom in the ring structure.

In some embodiments of the present invention, the compound of general formula M is selected from a group consisting of the following compounds:

In some embodiments of the present invention, preferably, R M1 and R M2 each independently represents C 1-10 linear alkyl, C 1-9 linear alkoxy, or C 2-10 linear alkenyl; further preferably, R M1 and R M2 each independently represents C 1-8 linear alkyl, C 1-7 linear alkoxy, or C 2-8 linear alkenyl; more further preferably, R M1 and R M2 each independently represents C 1-5 linear alkyl, C 1-4 linear alkoxy, or C 2-5 linear alkenyl.

In some embodiments of the present invention, preferably, R M1 and R M2 each independently represents C 2-8 linear alkenyl; further preferably, R M1 and R M2 each independently represents C 2-5 linear alkenyl.

In some embodiments of the present invention, preferably, one of R M1 and R M2 represents C 2-5 linear alkenyl and the other represents C 1-5 linear alkyl.

In some embodiments of the present invention, preferably, R M1 and R M2 each independently represents C 1-8 linear alkyl, or C 1-7 linear alkoxy; further preferably, R M1 and R M2 each independently represents C linear alkyl, C 1-4 linear alkoxy.

In some embodiments of the present invention, preferably, one of R M1 and R M2 represents C linear alkyl, and the other represents C linear alkyl, or C 1-4 linear alkoxy; further preferably, R M1 and R M2 each independently represents C linear alkyl.

In some embodiments of the present invention, the content of the compound of general formula M must be appropriately adjusted depending on the required performance such as low temperature solubility, transition temperature, electrical reliability, birefringence index, process adaptability, drop trace, “burn-in”, dielectric anisotropy and so on.

The lower limit of the weight percentage of the compound of general formula M is 20%, 22%, 24%, 26%, 28%, 30%, 35%, 40%, 45% or 50%, relative to the total weight of the liquid crystal composition of the present invention; and the upper limit of the weight percentage of the compound of general formula M is 70%, 65%, 60%, 58%, 56%, 55.5%, 54%, 52%, 50%, 45.5%, 45%, 40.5%, 40%, 38.5%, 37.5%, 36.5%, 35%, 30%, 28% or 25%, relative to the total weight of the liquid crystal composition of the present invention.

In some embodiments of the present invention, the compound of general formula M provides 20-70 wt. % of the total weight of the liquid crystal composition; preferably, the compound of general formula M provides 20-55 wt. % of the total weight of the liquid crystal composition.

The lower limit and the upper limit of the content of the compound of general Formula M are preferably higher when it is desired to maintain the liquid crystal composition of the present invention with a lower viscosity and a shorter response time. Further, the lower limit and the upper limit of the content of the compound of general Formula M are preferably higher when it is desired to maintain the liquid crystal composition of the present invention with a higher clearing point and a good temperature stability. In addition, the lower limit and the upper limit of the content of the compound of general Formula M are preferably decreased in order to maintain the driving voltage lower and make the absolute value of the dielectric anisotropy larger.

In some embodiments of the present invention, with emphasis in reliability, both R M1 and R M2 are preferably each independently alkyl; with emphasis in reducing the volatility of the compound, both R M1 and R M2 are preferably each independently alkoxy; and with emphasis in reducing the viscosity, at least one of R M1 and R M2 is preferably alkenyl.

In some embodiments of the present invention, the liquid crystal composition further comprises at least one compound of general formula N:

in which,

R N1 and R N2 each independently represents C 1-12 linear or branched alkyl,

wherein one or more nonadjacent —CH 2 — in the C 1-12 linear or branched alkyl can each be independently replaced by —CH═CH—, —C≡C—, —O—, —CO—, —CO—O— or —O—CO—;

ring

and ring

each independently represents

wherein one or more —CH 2 — in

can be replaced by —O—, and one or more single bond in the ring can be replaced by double bond, wherein one or more —H on

can each be independently substituted by —F, —Cl, —CN, —CH 3 or —OCH 3 , and one or more —CH═ in the ring can be replaced by —N═;

Z N1 and Z N2 each independently represents single bond, —CO—O—, —O—CO—, —CH 2 O—, —OCH 2 —, —CH═CH—, —C≡C—, —CH 2 CH 2 —, —CF 2 CF 2 —, —(CH 2 ) 4 —, —CF 2 O— or —OCF 2 —; L N1 and L N2 each independently represents —H, C 1-3 alkyl or halogen; n N1 represents 0, 1, 2 or 3, n N2 represents 0 or 1 and 0≤n N1 +n N2 ≤3, wherein when n N1 =2 or 3, ring

can be same or different, Z N1 can be same or different;

when 0≤n N1 +n N2 ≤2, compounds of general formula N do not comprise terphenyl structure; and when n N1 +n N2 =3, compounds of general formula N do not comprise quaterphenyl structure.

In some embodiments of the present invention, preferably, ring

and ring

each independently represents

In some embodiments of the present invention, the compound of general formula N is selected from a group consisting of the following compounds:

The lower limit of the weight percentage of the compound of general formula N is 1%, 2%, 4%, 6%, 8%, 10%, 15%, 16%, 18%, 20%, 22%, 23.5%, 24%, 26%, 28%, 30%, 35%, 37.5%, 40% or 45%, relative to the total weight of the liquid crystal composition of the present invention; and the upper limit of the weight percentage of the compound of general formula N is 60%, 58%, 56%, 54.5%, 54%, 53.5%, 52%, 50%, 49.5%, 45.5%, 45%, 40%, 37.5%, 36.5%, 35%, 30%, 28%, 25%, 24%, 23.5%, 22%, 20%, 18% or 15%, relative to the total weight of the liquid crystal composition of the present invention.

In some embodiments of the present invention, the compound of general formula N provides 1-60 wt. % of the total weight of the liquid crystal composition; preferably, the compound of general formula N provides 3-60 wt. % of the total weight of the liquid crystal composition; further preferably, the compound of general formula N provides 5-60 wt. % of the total weight of the liquid crystal composition.

In some embodiments of the present invention, the lower limit and the upper limit of the content of the compound of general Formula N are preferably lower when it is desired to maintain the liquid crystal composition of the present invention with a lower viscosity and a shorter response time. Further, the lower limit and the upper limit of the content of the compound of general Formula N are preferably lower when it is desired to maintain the liquid crystal composition of the present invention with a higher clearing point and a good temperature stability. In addition, the lower limit and the upper limit of the content of the compound of general Formula N are preferably increased in order to maintain the driving voltage lower and make the absolute value of the dielectric anisotropy larger.

In some embodiments of the present invention, preferably, R N1 and R N2 each independently represents C 1-10 linear or branched alkyl, C 1-9 linear or branched alkoxy, or C 2-10 linear or branched alkenyl; further preferably, R N1 and R N2 each independently represents C 1-8 linear or branched alkyl, C 1-7 linear or branched alkoxy, or C 2-8 linear or branched alkenyl; more further preferably, R N1 and R N2 each independently represents C 1-5 linear or branched alkyl, C 1-4 linear or branched alkoxy, or C 2-5 linear or branched alkenyl.

In some embodiments of the present invention, R N1 is further preferably C 1-5 linear or branched alkyl, or C 2-5 linear or branched alkenyl; and more further preferably C 2-5 linear or branched alkyl, or C 2-3 linear or branched alkenyl; R N2 is further preferably C 1-5 linear or branched alkoxy.

In some embodiments of the present invention, the liquid crystal composition further comprises at least one compound selected from a group consisting of compounds of general formula A-1 and general formula A-2:

in which,

R A1 and R A2 each independently represents C 1-12 linear or branched alkyl,

wherein one or more nonadjacent —CH 2 — in the C 1-12 linear or branched alkyl can each be independently replaced by —CH═CH—, —C≡C—, —O—, —CO—, —CO—O— or —O—CO—, and one or more —H in the C 1-12 linear or branched alkyl,

can each be independently substituted by —F or —Cl;

ring

ring

ring

and ring

each independently represents

wherein one or more —CH 2 — in

can be replaced by —O—, and one or more single bond in the rings can be replaced by double bond, wherein one or more —H on

can each be independently substituted by —F, —Cl, —CN, —CH 3 or —OCH 3 , and one or more —CH═ in the rings can be replaced by —N═;

Z A11 , Z A21 and Z A22 each independently represents single bond, —CH 2 CH 2 —, —CF 2 CF 2 —, —CO—O—, —O—CO—, —O—CO—O—, —CH═CH—, —CF═CF—, —CH 2 O— or —OCH 2 —; L A11 , L A12 , L A13 , L A21 and L A22 each independently represents —H, C 1-3 alkyl or halogen; X A1 and X A2 each independently represents halogen, C 1-5 linear or branched halogenated alkyl or halogenated alkoxy, or C 2-5 linear or branched halogenated alkenyl or halogenated alkenoxy; n A11 represents 0, 1, 2 or 3, wherein when n A11 =2 or 3, ring

can be same or different, and Z A11 can be same or different; and

n A12 represents 1 or 2, wherein when n A12 =2, ring

can be same or different;

n A2 represents 1, 2 or 3, wherein when n A2 =2 or 3, ring

can be same or different, and Z A21 can be same or different; and

when n A2 =2, compounds of general formula A-2 do not comprise quaterphenyl structure.

In some embodiments of the present invention, the compound of general formula A-1 is selected from a group consisting of the following compounds:

in which,

R A1 represents C 1-8 linear or branched alkyl,

wherein one or more nonadjacent —CH 2 — in the C 1-8 linear or branched alkyl can each be independently replaced by —CH═CH—, —C≡C—, —O—, —CO—, —CO—O— or —O—CO—, and one or more —H in the C 1-8 linear or branched alkyl can each be independently substituted —F or —Cl;

R v and R w each independently represents —CH 2 — or —O—; L A11 , L A12 , L A11 ′, L A12 ′, L A14 , L A15 and L A16 each independently represents —H or —F; L A13 and L A13 ′ each independently represents —H or —CH 3 ; X A1 represents —F, —CF 3 or —OCF 3 ; and v and w each independently represents 0 or 1.

The lower limit of the weight percentage of the compound of general formula A-1 is 0%, 1%, 2%, 4%, 6%, 8%, 10%, 12%, 14%, 16%, 18% or 20%, relative to the total weight of the liquid crystal composition of the present invention; and the upper limit of the weight percentage of the compound of general formula A-1 is 50%, 45%, 40%, 38%, 35%, 30%, 28%, 27%, 26% or 25%, relative to the total weight of the liquid crystal composition of the present invention.

In some embodiments of the present invention, the compound of general formula A-1 provides 0-50 wt. % of the total weight of the liquid crystal composition.

It is preferred that the lower limit and the upper limit of the content of the compound of general Formula A-1 are slightly lower when it is desired to maintain the liquid crystal composition of the present invention with a lower viscosity and a shorter response time. Further, it is preferred that the lower limit and the upper limit of the content of the compound of general Formula A-1 are slightly lower when it is desired to maintain the liquid crystal composition of the present invention with a higher clearing point and a good temperature stability. In addition, it is preferred that the lower limit and the upper limit of the content of the compound of general Formula A-1 are slightly higher in order to maintain the driving voltage lower and make the absolute value of the dielectric anisotropy larger.

In some embodiments of the present invention, the compound of general formula A-2 is selected from a group consisting of the following compounds:

in which,

R A2 represents C 1-8 linear or branched alkyl, wherein one or more nonadjacent —CH 2 — in the C 1-8 linear or branched alkyl can each be independently replaced by —CH═CH—, —C≡C—, —O—, —CO—, —CO—O— or —O—CO—, and one or more —H in these groups can each be independently substituted by —F or —Cl;

L A21 , L A22 , L A23 , L A24 and L A25 each independently represents —H or —F; and

X A2 represents —F, —CF 3 , —OCF 3 or —CH 2 CH 2 CH═CF 2 .

The lower limit of the weight percentage of the compound of general formula A-2 is 0%, 0.5%, 1%, 2%, 4%, 6%, 8%, 10%, 12%, 14%, 15%, 16%, 17%, 18% or 20%, relative to the total weight of the liquid crystal composition of the present invention; and the upper limit of the weight percentage of the compound of general formula A-2 is 60%, 55%, 50%, 45%, 40%, 35%, 30%, 28%, 27%, 26% or 25%, relative to the total weight of the liquid crystal composition of the present invention.

In some embodiments of the present invention, the compound of general formula A-2 provides 0-60 wt. % of the total weight of the liquid crystal composition.

It is preferred that the lower limit and the upper limit of the content of the compound of general Formula A-2 are slightly lower when it is desired to maintain the liquid crystal composition of the present invention with a lower viscosity and a shorter response time. Further, it is preferred that the lower limit and the upper limit of the content of the compound of general Formula A-2 are slightly lower when it is desired to maintain the liquid crystal composition of the present invention with a higher clearing point and a good temperature stability. In addition, it is preferred that the lower limit and the upper limit of the content of the compound of general Formula A-2 are slightly higher in order to maintain the driving voltage lower and make the absolute value of the dielectric anisotropy larger.

In addition to the above compounds, the liquid crystal composition of the present invention may also contain normal nematic liquid crystal compound, smectic liquid crystal compound, cholesteric liquid crystal compound, antioxidant, ultraviolet absorber, infrared absorber, polymerizable monomer or light stabilizer, etc.

Dopants which can be preferably added to the liquid crystal composition according to the present invention are shown below.

In some embodiments of the present invention, the dopants provide 0-5 wt. % of the total weight of the liquid crystal composition; preferably, the dopants provide 0.01-1 wt. % of the total weight of the liquid crystal composition.

Further, additives used in the liquid crystal composition of the present invention, such as antioxidant, light stabilizer and the like, are preferably selected from the following substances:

in which, n represents a positive integer of 1-12.

Preferably, the light stabilizer is selected from a group consisting of the light stabilizers as shown below.

In some embodiments of the present invention, the light stabilizers provide 0-5 wt. % of the total weight of the liquid crystal composition; preferably, the light stabilizers provide 0.01-1 wt. % of the total weight of the liquid crystal composition; and further preferably, the light stabilizers provide 0.01-0.1 wt. % of the total weight of the liquid crystal composition.

In still another aspect, the present invention provides a liquid crystal display device comprising the above liquid crystal composition.

In some embodiments of the present invention, the liquid crystal display device is particularly suitable in VA, IPS or FFS display modes.

Beneficial Effects

Compared with the prior art, the liquid crystal composition of the present has a smaller voltage change rate at high and low temperatures and a shorter low temperature response time, while maintaining an appropriate optical anisotropy, an appropriate clearing point, an appropriate absolute value of dielectric anisotropy, such that the liquid crystal display device comprising the liquid crystal composition has a better display and a faster response speed.

The present invention will be illustrated by combining the detailed embodiments below. It should be noted that, the following examples are exemplary embodiments of the present invention, which are only used to illustrate the present invention, not to limit it. Other combinations and various modifications within the conception of the present invention are possible without departing from the subject matter and scope of the present invention.

For the convenience of the expression, the group structures of the liquid crystal compositions in the following Examples are represented by the codes listed in Table 1:

Take the compound with following structural formula as an example:

represented by the codes listed in Table 1, this structural formula can be expressed as nCCGF, in which, n in the code represents the number of the carbon atoms of the alkyl on the left, for example, n is “3”, meaning that the alkyl is —C 3 H 7 ; C in the code represents 1,4-cyclohexylidene, G represents 2-fluoro-1,4-phenylene, and F represents fluoro substituent.

The abbreviated codes of the test items in the following Examples are as follows:

Cp (° C.) clearing point (nematic-isotropy phases transition temperature) Δn optical anisotropy (589 nm, 25° C.) Δε dielectric anisotropy (1 KHz, 25° C.) DV/DT voltage change rate at high and low temperatures (%) τ (−20° C.) low temperature response time (ms) in which, Cp: tested and obtained through melting point apparatus; Δn: tested and obtained by using Abbe refractometer under sodium lamp (589 nm) light source at 25° C.; Δε: Δε=ε // −ε ⊥ , in which, ε // is the dielectric constant parallel to the molecular axis, ε ⊥ is the dielectric constant perpendicular to the molecular axis, with the test conditions: 25° C., 1 KHz, VA type test cell with a cell gap of 6 μm; DV/DT: tested by using DMS505 tester; with the test conditions: test frequency: 60 Hz, test waveform: square, high temperature 60° C., room temperature 20° C.; τ (−20° C.) :tested and obtained by using DMS505 tester at −20° C.; with the test conditions: IPS type test cell with a cell gap of 3.5 driving voltage 5.5 V.

The ingredients used in the following Examples can be synthesized by well-known methods or obtained by commercial means. These synthetic techniques are routine, and the test results show that the liquid crystal compounds thus prepared meet the criteria for the electronic compounds.

The liquid crystal compositions are prepared according to the formulations of the liquid crystal compositions specified in the following Examples. The preparation of the liquid crystal compositions is proceeded according to the conventional methods in the art, such as heating, ultrasonic wave, or suspension.

The liquid crystal composition specified in the following Examples are prepared and studied. The formulas of the liquid crystal compositions and their test results for the performance are shown below.

Comparative Example 1

The liquid crystal composition of Comparative Example 1 is prepared according to each compound and weight percentage listed in Table 2 and is tested by filling the same between two substrates of a liquid crystal display device.