In recent years, with the reduction in size and height for electronic devices such as cellular phones and portable music players, multilayer printed wiring boards mounted on the electronic devices have been progressively reduced in size. Accordingly, multilayer ceramic capacitors mounted on the multilayer printed wiring boards have been also progressively reduced in size and height.

Some of the multilayer ceramic capacitors are built into multilayer printed wiring boards, such as the multilayer ceramic capacitor described in, for example, Japanese Patent Application Laid-Open No. 2002-203735. Because the multilayer ceramic capacitor in Japanese Patent Application Laid-Open No. 2002-203735 is built into a multilayer printed wiring board, there is a need for tight adhesion between the multilayer ceramic capacitor and the multilayer printed wiring board.

Such capacitors as in Japanese Patent Application Laid-Open No. 2002-203735 cause the problem of peeling between the capacitors and interlayer resin insulating layers or adhesives in the multilayer printed wiring boards in contact with the capacitors, when the capacitors are built into multilayer printed wiring boards. Therefore, peeling between the multilayer ceramic capacitors and the resin in the multilayer printed wiring boards has the possibility of causing problems such as decreased component reliability due to ingress of moisture from the peeled sites, and fractured portions connected to via (small-diameter hole for the passage of signals) electrodes formed in the multilayer printed wiring boards.

›SUMMARY OF THE INVENTION

Therefore, preferred embodiments of the present invention provide a multilayer ceramic capacitor that achieves tight adhesion between the multilayer ceramic capacitor and a resin of a multilayer printed wiring board.

A multilayer ceramic capacitor according to a preferred embodiment of the present invention is a multilayer ceramic capacitor including a ceramic body with a plurality of ceramic layers and internal electrodes stacked, which has principal surfaces opposed to each other, side surfaces opposed to each other, and end surfaces opposed to each other; and an external electrode including a base layer including a sintered metal containing a metal and glass and a plated layer provided on the surface of the base layer, which is provided on the end surface of the ceramic body to be connected to the internal electrodes, the external electrode includes a principal surface portion disposed on the principal surface of the ceramic body, the outermost layer of the plated layer of the external electrode includes a Cu plated layer, and the ratio of arithmetic mean roughness (Ra) at the surface of the ceramic body/arithmetic mean roughness (Ra) at the surface of the external electrode meets about 0.06≦the arithmetic mean roughness (Ra) at the surface of the ceramic body/the arithmetic mean roughness (Ra) at the surface of the external electrode≦about 0.97. In this regard, as a metal for the base layer, an appropriate metal is used such as Ni, Cu, Ag, Pd, Au, an Ag—Pd alloy.

Furthermore, the multilayer ceramic capacitor is preferably about 0.9 mm or more and about 1.1 mm or less in dimension in a direction of connecting the pair of end surfaces to each other, about 0.4 mm or more and about 0.6 mm or less in dimension in a direction of connecting the pair of side surfaces to each other, and about 0.085 mm or more and about 0.15 mm or less in dimension in a direction of connecting the pair of principal surfaces to each other.

In a multilayer ceramic capacitor according to a preferred embodiment of the present invention, the arithmetic mean roughness (Ra) at the surface of the external electrode is larger than the arithmetic mean roughness (Ra) at the surface of the ceramic body, and the close contact with resin in an embedding recess for the capacitor, which is provided in a multilayer printed wiring board, is thus stronger at the external electrode, as compared with at the ceramic body. Therefore, even when a comparable external force is applied to the external electrode and the ceramic body, gaps are unlikely to be generated between the external electrode and the multilayer printed wiring board, ingress of moisture between the external electrode and the resin in the multilayer printed wiring board is thus suppressed or prevented, and as a result, reliability of resistance to moisture is ensured for the multilayer ceramic capacitor.

According to various preferred embodiments of the present invention, a multilayer ceramic capacitor which causes no peeling between an external electrode of the multilayer ceramic capacitor and a resin insulating layer of a multilayer printed wiring board is provided.

The above and other elements, features, steps, characteristics and advantages of the present invention will become more apparent from the following detailed description of the preferred embodiments with reference to the attached drawings.

›BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view illustrating an example of a multilayer ceramic capacitor according to a preferred embodiment of the present invention.

FIG. 2 is a side view of the multilayer ceramic capacitor shown in FIG. 1 .

FIG. 3 is a cross-sectional view along line III-III of FIG. 1 .

FIG. 4 is a drawing illustrating a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, specifically, a schematic cross-sectional view illustrating a metal of a Cu plated layer of an external electrode, which penetrates into a base layer.

FIG. 5 is a drawing illustrating a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, specifically, an explanatory drawing for schematically explaining a maximum thickness D max and an average thickness D ave of a principal surface portion.

FIG. 6 is a schematic drawing for explaining the shape of an external electrode of a multilayer ceramic capacitor according to a preferred embodiment of the present invention, which is able to achieve a greater effect.

FIG. 7 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

FIG. 8 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

FIG. 9 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

FIG. 10 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

FIG. 11 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

FIG. 12 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

FIGS. 13A and 13B are plan views of multilayer ceramic capacitors, which illustrate the shapes of edge ends of external electrodes on principal surfaces of ceramic bodies.

FIG. 14 is a flowchart showing an example of a method for manufacturing the multilayer ceramic capacitor shown in FIG. 1 .

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 1 of 11

FIG. 1 is an external perspective view illustrating a multilayer ceramic capacitor 10 . FIG. 2 is a side view of the multilayer ceramic capacitor 10 shown in FIG. 1 . FIG. 3 is a cross-sectional view along line III-III of FIG. 1 .

The multilayer ceramic capacitor 10 shown in FIG. 1 includes a ceramic body 12 , for example, in the form of a cuboid. This multilayer ceramic capacitor 10 is mostly a multilayer ceramic capacitor built in a multilayer printed wiring board. The ceramic body 12 includes a plurality of ceramic layers 14 stacked. The ceramic body 12 includes a pair of principal surfaces 12 a , 12 b opposed to each other, a pair of side surfaces 12 c , 12 d opposed to each other, and a pair of end surfaces 12 e , 12 f opposed to each other.

The principal surfaces 12 a , 12 b are each arranged in a length direction L and a width direction W.

The side surfaces 12 c , 12 d are each arranged in the length direction L and a height direction T.

The end surfaces 12 e , 12 f are each arranged in the width direction W and the height direction T.

Therefore, the length direction L refers to a direction of connecting the pair of end surfaces 12 e , 12 f to each other, the width direction W refers to a direction of connecting the pair of side surfaces 12 c , 12 d to each other, and the height direction T refers to a direction of connecting the pair of principal surfaces 12 a , 12 b to each other.

It is to be noted that while the multilayer ceramic capacitor 10 according to this preferred embodiment preferably is cuboid shaped, the shape of the ceramic body 12 is not particularly limited.

In addition, the ceramic body 12 preferably has corners and ridges rounded.

The ceramic layers 14 of the ceramic body 12 can be formed from a dielectric ceramic material. As the dielectric ceramic material for the ceramic layers 14 , a dielectric ceramic can be used which contains a main constituent such as, for example, BaTiO 3 , CaTiO 3 , SrTiO 3 , and CaZrO 3 . Furthermore, depending on desired characteristics of the multilayer ceramic capacitor 10 , the main constituents may be used to which accessory constituents are added such as Mn compounds, Mg compounds, Si compounds, Fe compounds, Cr compounds, Co compounds, Ni compounds, rare-earth compounds.

Furthermore, the ceramic layers 14 are preferably about 0.5 μm or more and about 10 μm or less in height.

In this preferred embodiment, for each effective portion of the ceramic body 12 , opposed portions 18 a , 18 b of internal electrodes 16 a , 16 b to be described are opposed with the ceramic layers 14 of the dielectric ceramic interposed therebetween to form electrostatic capacitance. Thus, this preferred embodiment defines and functions as a capacitor.

Within the ceramic body 12 , a plurality of substantially rectangular first internal electrodes 16 a and second internal electrodes 16 b are alternately arranged at regular intervals in the height direction T of the ceramic body 12 .

The first internal electrodes 16 a include the opposed portions 18 a and extended portions 20 a . The opposed portions 18 a are opposed to the second internal electrodes 16 b . The extended portions 20 a are exposed by extending from the opposed portions 18 a to the end surface 12 e of the ceramic body 12 , but not exposed at the end surface 12 f or the side surfaces 12 c , 12 d.

The second internal electrodes 16 b include the opposed portions 18 b and extended portions 20 b as in the case of the first internal electrodes 16 a . The opposed portions 18 b are opposed to the first internal electrodes 16 a . The extended portions 20 b are exposed by extending from the opposed portions 18 b to the end surface 12 f of the ceramic body 12 , but not exposed at the end surface 12 e or the side surfaces 12 c , 12 d.

Furthermore, the first internal electrodes 16 a and the second internal electrodes 16 b are each parallel or substantially parallel to the principal surface 12 a and principal surface 12 b of the ceramic body 12 . In addition, the first internal electrodes 16 a and the second internal electrodes 16 b are opposed to each other with the ceramic layers 14 interposed therebetween in the height direction T of the ceramic body 12 .

The internal electrodes 16 a , 16 b are each, for example, about 0.2 μm or more and about 2 μm or less in height. The internal electrodes 16 a , 16 b can be composed of an appropriate conductive material. The internal electrodes 16 a , 16 b can be composed of, for example, a metal such as Ni, Cu, Ag, Pd, and Au, or an alloy containing one of the metals, such as, for example, an Ag—Pd alloy.

In this regard, the respective metals of the first internal electrodes 16 a and second internal electrodes 16 b are preferably diffused in a first external electrode 22 a and a second external electrode 22 b as described later. The metal of the first internal electrode 16 a diffuses into the first external electrode 22 a to expand the volume of the metal in the first external electrode 22 a and fill minute gaps in the first external electrode 22 a , thus making it possible improve the sealing property against ingress of moisture. Likewise, the metal of the second internal electrode 16 b diffuses into the second external electrode 22 b to expand the volume of the metal in the second external electrode 22 b and fill minute gaps in the second external electrode 22 b , thus making it possible improve the sealing property against ingress of moisture. It is to be noted that the diffusion distances of the metals of the internal electrodes 16 a , 16 b into the external electrodes 22 a , 22 b are preferably about 4 μm or more.

In addition, glass layers may be formed on exposed portions where the extended portions 20 a , 20 b of the internal electrodes 16 a , 16 b are exposed at the end surfaces 12 e , 12 f of the ceramic body 12 . The formation of the glass layers on the exposed portions of the internal electrodes 16 a , 16 b ensures moisture resistance and plating resistance, and suppresses or prevents ingress of moisture from the outside, even when the external electrodes 22 a , 22 b to be described are poorly dense. As a result, the moisture resistance and plating resistance of the multilayer ceramic capacitor 10 is significantly improved.

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 2 of 11

The first external electrode 22 a and the second external electrode 22 b are respectively provided on the end surfaces 12 e , 12 f of the ceramic body 12 . The first external electrode 22 a is electrically connected through the extended portions 20 a to the first internal electrodes 16 a at the end surface 12 e . In addition, the first external electrode 22 a is provided on the principal surfaces so as to partially cover the principal surfaces 12 a , 12 b and the side surfaces 12 c , 12 d from the surface of the end surface 12 e . The second external electrode 22 b is electrically connected through the extended portions 20 b to the second internal electrodes 16 b at the end surface 12 f . In addition, the second external electrode 22 b is provided on the principal surfaces so as to partially cover the principal surfaces 12 a , 12 b and the side surfaces 12 c , 12 d from the surface of the end surface 12 f.

The first external electrode 22 a includes a base layer 24 a and a plated layer 26 a provided on the surface of the base layer 24 a . Furthermore, the second external electrode 22 b includes a base layer 24 b and a plated layer 26 b provided on the surface of the base layer 24 b.

The base layers 24 a , 24 b include a sintered metal containing Cu and glass. The base layers 24 a , 24 b may be co-fired by co-firing with the internal electrodes 16 a , 16 b , or post-fired by baking a conductive paste applied. The base layers 24 a , 24 b are preferably about 1 μm or more and about 20 μm or less in thickness.

The plated layers 26 a , 26 b may include a plurality of layers. The material constituting the outermost plated layers 26 a , 26 b includes a Cu plated film. The plated layers 26 a , 26 b are preferably about 1 μm or more and about 10 μm or less in thickness. When the outermost layers include a Cu plated film, it becomes possible to use the multilayer ceramic capacitor 10 as an electronic component built in a multilayer printed wiring board.

More specifically, in the case of embedding the multilayer ceramic capacitor 10 into a multilayer printed wiring board, there is a need to provide via holes for electronic component connection in the multilayer printed wiring board, in order to provide electrical connection to the external electrode 22 a , 22 b . The via holes for electronic component connection are formed with the use of a laser such as a CO 2 laser, for example. In the case of forming the via holes with the use of a laser, the first external electrodes 22 a , 22 b of the multilayer ceramic capacitor 10 are directly irradiated with the laser. In this regard, when the outermost layers of the plated layers 26 a , 26 b of the external electrodes 22 a , 22 b include a Cu plated film, the laser can be reflected at a high reflectance, and the capacitor can be thus used in a preferred manner as the multilayer ceramic capacitor 10 for being embedded in the multilayer printed wiring board. This is because when the laser reflectance is low with respect to the external electrodes 22 a , 22 b of the multilayer ceramic capacitor 10 , the laser may reach even the inside of the multilayer ceramic capacitor 10 , and damage the multilayer ceramic capacitor 10 .

In this regard, when the plated layers 26 a , 26 b are entirely composed of Cu, the Cu metal of the plated layers 26 a , 26 b may penetrate in the base layers 24 a , 24 b to a position of about ⅓ or more the thicknesses of the base layers 24 a , 24 b respectively from the surface layers of the base layers 24 a , 24 b , as shown in FIG. 4 . The adoption of this structure achieves a more pronounced effect. Further, in regard to penetration of the metal of the plated layers 26 a , 26 b into the base layers 24 a , 24 b , the Cu metal of the plated layers 26 a , 26 b is preferably present at about 30% or more with respect to the total proportion of the Cu metal of the base layers 24 a , 24 b and plated layers 26 a , 26 b on lines, when the lines are drawn along the portion of about ⅓ in thickness from the surface layers of the base layers 24 a , 24 b in any observation field of view of about 30 μm in x-axis and about 30 μm in y-axis, including the base layers 24 a , 24 b formed on the principal surfaces of the ceramic body at a polished surface obtained by polishing the side surface (surface LT) of the multilayer ceramic capacitor 10 along the length direction L until reaching about ½ the dimension in the width direction W.

More specifically, the Cu plated layers 26 a , 26 b are formed with the use of a pyrophosphoric acid Cu plating solution or a cyanide Cu plating solution, for example. These plating solutions with high glass erosion capability, efficiently dissolve the glass contained in the base layer 24 a , 24 b , and easily cause the Cu metal of the Cu plated layers 26 a , 26 b to penetrate into the base layer 24 a , 24 b , thus making it possible to improve the content rate of Cu in the base layers 24 a , 24 b.

In addition, when the multilayer ceramic capacitor 10 is formed so that the Cu metal of the Cu plated layers 26 a , 26 b penetrates in the base layers 24 a , 24 b to a position of about ⅓ or more the thicknesses of the base layers 24 a , 24 b from the surface layers of the base layers 24 a , 24 b , the Cu content rate is high in the base layers 24 a , 24 b . Accordingly, in combination with the base layers 24 a , 24 b and Cu plated layers 26 a , 26 b in total, the content rate of Cu per unit thickness is increased to improve the thermal conductivity (heat release performance) of the base layers 24 a , 24 b , and increase the laser resistance of the external electrodes 22 a , 22 b.

In addition, when the multilayer ceramic capacitor 10 is formed so that the Cu metal of the Cu plated layers 26 a , 26 b penetrates in the base layers 24 a , 24 b to a position of about ⅓ or more the thicknesses of the base layers 24 a , 24 b from the surface layers of the base layers 24 a , 24 b , the difference in level between the surface of the multilayer printed wiring board and the surfaces of the external electrodes 22 a , 22 b are reduced because the external electrode 22 a ( 22 b ) including the base layer 24 a ( 24 b ) and the Cu plated layer 26 a ( 26 b ) is reduced in total thickness. As a result, the gap between the surface of the multilayer printed wiring board and the mounting surface 12 a (or 12 b ) of the ceramic body 12 is narrowed to make peeling less likely to be caused between the multilayer printed wiring board and the external electrodes 22 a , 22 b , and also improve the mechanical strength of the component.

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 3 of 11

In this regard, the glass in the base layers 24 a , 24 b is preferably composed of glass containing BaO in an amount of about 10 weight % or more and about 50 weight % or less, SrO in an amount of about 10 weight % or more and about 50 weight % or less, B 2 O 3 in an amount of about 3 weight % or more and about 30 weight % or less, and SiO 2 in an amount of about 3 weight % or more and about 30 weight % or less. Thus, in the formation of the Cu plated layers 26 a , 26 b with the use of a pyrophosphoric acid Cu plating solution or a cyanide Cu plating solution, for example, the glass contained in the base layers 24 a , 24 b is dissolved reliably.

It is to be noted that whether the Cu metal of the Cu plated layers 26 a , 26 b penetrates into the base layers 24 a , 24 b or not can be confirmed by polishing the side surface (surface LT) of the multilayer ceramic capacitor 10 along the length direction L until reaching about ½ the dimension in the width direction W, and observing the polished surface with an optical microscope.

Furthermore, the metal thicknesses of the external electrodes 22 a , 22 b are preferably about 8.7 μm or more and about 13.9 μm or less. The metal thickness refers to a value obtained by measuring the thickness of the metal with a fluorescent X-ray film thickness meter (SFT-9400 from Seiko Instruments Inc.), and converting the measured X-ray Cu amount into a film thickness.

Furthermore, the plated layers 26 a , 26 b as outermost layers may have surfaces oxidized. In regard to the area of the oxidation, at least ridges of the external electrodes 22 a , 22 b are preferably oxidized.

This is because with the oxidized plated layers 26 a , 26 b as outermost layers, when the multilayer ceramic capacitor 10 is embedded into a multilayer printed wiring board, the oxidized film surfaces and a resin of the multilayer printed wiring board are attached through oxygen binding due to the plated layers 26 a , 26 b oxidized between the plated layers 26 a , 26 b of the multilayer ceramic capacitor 10 and the resin of the multilayer printed wiring board, and the adhesion is thus improved between the multilayer ceramic capacitor 10 and the multilayer printed wiring board. It is to be noted that the effect mentioned above is greater when the entire surfaces of the external electrodes 22 a , 22 b are oxidized.

In this regard, the arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b is larger than the arithmetic mean roughness (Ra) at the surface of the ceramic body 12 . More specifically, the ratio of the arithmetic mean roughness (Ra) at the surface of the ceramic body 12 /the arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b falls within the range of about 0.06 or more and about 0.97 or less.

In order to calculate the arithmetic mean roughness (Ra) at the surface of the ceramic body 12 , as a measurement condition, a laser microscope (Product Name: VK-9510) from Keyence Corporation is preferably used at a 100-fold lens magnification in a color ultradeep mode set. The measurement area with the laser microscope corresponds to a region of about 90 μm square including a central portion of the principal surface 12 a of the ceramic body 12 . Then, the arithmetic mean roughness (Ra) at the surface of the ceramic body 12 is a value calculated on the basis of the surface roughness measured under the measurement condition.

On the other hand, in order to calculate the arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b , as a measurement condition, a laser microscope (Product Name: VK-9510) from Keyence Corporation is preferably used at a 100-fold lens magnification in a color ultradeep mode set. The measurement area with the laser microscope corresponds to a region of about 90 μm square including central portions of portions of the external electrode 22 a or external electrode 22 b provided on the principal surface 12 a or the principal surface 12 b (principal surface portions 23 a to 23 d ). Then, the arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b is a value calculated on the basis of the surface roughness measured under the measurement condition.

Furthermore, in regard to the principal surface portions 23 a , 23 b of the first external electrode 22 a disposed on the principal surfaces 12 a , 12 b of the ceramic body 12 , as shown in FIG. 5 , when the maximum thickness and average thickness of the principal surface portions 23 a , 23 b are denoted respectively by D max and D ave , the D max and D ave are preferably set so as to satisfy the condition expression of D ave ×250%≧D max ≧D ave ×120%. Likewise, in regard to the principal surface portions 23 c , 23 d of the second external electrode 22 b disposed on the principal surfaces 12 a , 12 b of the ceramic body 12 , when the maximum thickness and average thickness of the principal surface portions 23 c , 23 d are denoted respectively by D max and D ave , the D max and D ave are preferably set so as to satisfy the condition expression of D ave ×250%≧D max ≧D ave ×120%. The adoption of this structure achieves a more pronounced effect.

When the multilayer ceramic capacitor 10 is formed so that the maximum thicknesses D max and average thicknesses D ave of the principal surface portions 23 a to 23 d of the external electrodes 22 a , 22 b on the principal surfaces 12 a , 12 b satisfy the condition expression of D ave ×250%≧D max ≧D ave ×120%, the principal surface portions 23 a to 23 d are increased in thickness, and principal surface portions 23 a to 23 d function as cushioning materials, and disperse the mounting load (stress) applied in suctioning the multilayer ceramic capacitor 10 with a suction nozzle of a mounting machine (mounter) or pushing the capacitor into a multilayer printed wiring board.

As a result, the generation of breakages and cracks is significantly reduced or prevented without concentrating the mounting load (stress) on portions of the multilayer ceramic capacitor 10 with mechanical strength decreased.

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 4 of 11

The maximum thickness D max and the average thickness D ave are measured by polishing the side surface of the multilayer ceramic capacitor 10 along the length direction L until reaching about ½ the dimension in the width direction W, and observing the polished surface with an optical microscope.

In addition, when the impurity is potassium, which is present on the surfaces of the outermost Cu plated layers of the plated layers 26 a , 26 b of the external electrodes 22 a , 22 b and the surface of the ceramic body 12 , the multilayer ceramic capacitor 10 is preferably treated so that the concentration of impurity potassium is about 0.30 ppm or less. Alternatively, when the impurity is sulfur, which is present on the surfaces of the outermost Cu plated layers of the plated layers 26 a , 26 b of the external electrodes 22 a , 22 b and the surface of the ceramic body 12 , the multilayer ceramic capacitor 10 is preferably treated so that the concentration of impurity sulfur is about 0.40 ppm or less.

Furthermore, FIG. 6 is a schematic drawing for explaining the shape of the external electrode 22 a , 22 b of the multilayer ceramic capacitor 10 according to a preferred embodiment of the present invention, which is able to achieve a greater effect, and an enlarged view around the external electrode 22 a in FIG. 3 . It is to be noted that because the external electrode 22 b has the same shape as the external electrode 22 a , the explanation will be thus left out herein.

The external electrode 22 a of the multilayer ceramic capacitor 10 according to this preferred embodiment is preferably formed so that when the distance from the position of the maximum thickness on the principal surface 12 a of the ceramic body 12 to the position of the maximum thickness on the end surface 12 e of the ceramic body 12 is referred to as a dimension E, whereas the distance from the position of the maximum thickness on the end surface 12 e of the ceramic body 12 to an edge end of the external electrode 22 a on the principal surface 12 a of the ceramic body 12 is referred to as a dimension e, the ratio E/e is about 0.243 or more and about 0.757 or less. The adoption of this structure achieves a more pronounced effect.

More specifically, in the case of the multilayer ceramic capacitor 10 , the external electrodes 22 a , 22 b are preferably formed so that when the distance from the position of the maximum thickness on the principal surface 12 a of the ceramic body 12 to the position of the maximum thickness on the end surface 12 e of the ceramic body 12 is referred to as a dimension E, whereas the distance from the position of the maximum thickness on the end surface 12 e of the ceramic body 12 to an edge end of the external electrode 22 a on the principal surface 12 a of the ceramic body 12 is referred to as a dimension e, the ratio E/e is about 0.243 or more and about 0.757 or less. Thus, the stress concentration which is generated at corners of the multilayer ceramic capacitor 10 is significantly reduced or prevented. As a result, it becomes possible to suppress or prevent peeling that is generated between the corners of the multilayer ceramic capacitor 10 and the resin in the embedding recess for the capacitor, which is provided in the multilayer printed wiring board.

The dimension E and the dimension e are measured by polishing, for a cross section, the side surface of the multilayer ceramic capacitor 10 along the length direction L until reaching about ½ the dimension in the width direction W, and observing the polished surface with an optical microscope.

Furthermore, FIG. 7 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

The height of an effective portion that is a portion of the ceramic body 12 where the first internal electrodes 16 a and the second internal electrode 16 b are provided is referred to as A in the height direction T. The height of the ceramic layer 14 defining outer layer that is a portion of the ceramic body 12 located closer to the principal surface 12 a than the effective portion is referred to as B in the height direction T. The height of the ceramic layer 14 defining outer layer that is a portion of the ceramic body 12 located closer to the principal surface 12 d than the effective portion is referred to as C in the height direction T. In this case, the ratios A/B and A/C each preferably falls within the range of about 0.5 to about 16.

Furthermore, in regard to the multilayer ceramic capacitor 10 , when the dimension in the height direction T is about 50 μm to about 150 μm, the ratios of A/B and A/C each preferably fall within the range of about 0.6 to about 6.

In addition, in regard to the multilayer ceramic capacitor 10 , when the dimension in the height direction T is about 150 μm to about 250 μm, the ratios of A/B and A/C each preferably fall within the range of about 2 to about 16.

As just described, in regard to the multilayer ceramic capacitor 10 , when the ratios of A/B and A/C each fall within the range of about 0.5 to about 16, the crack generation in the ceramic body 12 which starts from the contact point between the principal surface 12 a of the ceramic body 12 and the end of the external electrode 22 a is effectively suppressed or prevented. As the reason therefor, the following reason is considered.

In the multilayer ceramic capacitor 10 , the ratios A/B and A/C each falls within the range of about 0.5 to about 16, thus leading to the small height ratio of the ceramic layers 14 defining outer layers closer to the principal surface 12 a and the principal surface 12 b to the effective portion EP. More specifically, the ceramic layers 14 defining outer layers closer to the principal surface 12 a and the principal surface 12 b are relatively small in height. For this reason, when the ceramic body 12 is subjected to firing, compressive stress applied to the ceramic layers 14 defining outer layers closer to the principal surface 12 a and the principal surface 12 b is likely to be increased, due to contraction of electrode paste layers defining the internal electrodes 16 a , 16 b . For this reason, for example, in the case of baking the external electrodes 22 a , 22 b after firing the ceramic body 12 , the compressive stress of the ceramic layers 14 defining outer layers closer to the principal surface 12 a and the principal surface 12 b is increased before baking the external electrodes 22 a , 22 b . For this reason, tensile stress is less likely to be applied to the ceramic body 12 , even when the electrode paste layers defining the external electrodes 22 a , 22 b are contracted in baking the external electrodes 22 a , 22 b . Therefore, the ceramic body 12 is believed to be less likely to be cracked. Even in the case of simultaneously carrying out firing for the ceramic body 12 and firing defining the external electrodes 22 a , 22 b , tensile stress is less likely to be applied to the ceramic body 12 for the same reason, and thus less likely to be applied to the ceramic body 12 .

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 5 of 11

When the dimension of the multilayer ceramic capacitor 10 in the height direction T is about 150 μm to about 250 μm, the ratios of A/B and A/C each preferably fall within the range of about 2 to about 16.

It is to be noted that A, B, and C can be measured in the following manner. More specifically, a cross section is exposed by polishing the side surface 12 c of the multilayer ceramic capacitor 10 until the dimension in the width direction W is reduced down to about ½. A, B, and C can be measured at the center of the cross section in the length direction with the use of an optical microscope. The thickness A can be measured at a portion located in the center of the cross section in the length direction and in the center thereof in the height direction T.

Furthermore, FIG. 8 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

More specifically, in the multilayer ceramic capacitor 10 , when the dimension in the length direction L of the multilayer ceramic capacitor 10 is referred to as L 0 , whereas the distance in the length direction L is referred to as L 1 between an end in the length direction L of a portion of the first external electrode 22 a located on the principal surface 12 a and an end of the second internal electrode 16 b closer to the end surface 12 e , the ratio of L 1 /L 0 is preferably about 0.05 to about 0.35. Accordingly, the ceramic body 12 is unlikely to be cracked in the multilayer ceramic capacitor 10 . The ratio of L 1 /L 0 is more preferably about 0.13 or more.

Further, in regard to L 0 , a cross section is exposed by polishing the side surface 12 c , 12 d of the multilayer ceramic capacitor 10 until the dimension in the width direction W is reduced down to about ½. The cross section can be observed with the use of an optical microscope to make a dimension measurement.

In regard to L 1 , a cross section is exposed by polishing the side surface 12 c , 12 d of the multilayer ceramic capacitor 10 until the dimension in the width direction W is reduced down to about ½. The cross section is observed with the use of an optical microscope to first specify the second internal electrode 16 b closest to the end surface 12 e . Then, the dimension can be obtained by measuring the distance in the length direction L between the second internal electrode 16 b and the end surface 12 e.

In addition, in this regard, the length of the first external electrode 22 a in the length direction L is referred to as LE 1 as viewed from the principal surface 12 b . The length of the first external electrode 22 a in the length direction L is referred to as LE 2 as viewed from the principal surface 12 a . The length of the second external electrode 22 b in the length direction L is referred to as LE 3 as viewed from the principal surface 12 b . The length of the second external electrode 22 b in the length direction L is referred to as LE 4 as viewed from the principal surface 12 a . The distance in the length direction L is referred to as LE 5 between the thickest portion of the first external electrode 22 a located on the principal surface 12 b and the outermost end of the first external electrode 22 a in the length direction L. The distance in the length direction L is referred to as LE 6 between the thickest portion of the first external electrode 22 a located on the principal surface 12 a and the outermost end of the first external electrode 22 a in the length direction L. The distance in the length direction L is referred to as LE 7 between the thickest portion of the second external electrode 22 b located on the principal surface 12 b and the outermost end of the second external electrode 22 b in the length direction L. The distance in the length direction L is referred to as LE 8 between the thickest portion of the second external electrode 22 b located on the principal surface 12 a and the outermost end of the second external electrode 22 b in the length direction L. The ratio of the absolute value of the difference between LE 5 and LE 6 to the longer one of LE 1 and LE 2 ((absolute value of difference between LE 5 and LE 6 )/(longer one of LE 1 and LE 2 )) is referred to as A 1 . The ratio of the absolute value of the difference between LE 7 and LE 8 to the longer one of LE 3 and LE 4 ((absolute value of difference between LE 7 and LE 8 )/(longer one of LE 3 and LE 4 )) is referred to as A 2 .

In this case, in the multilayer ceramic capacitor 10 , A 1 and A 2 are each preferably about 0.2 or more. Thus, the ceramic body 10 is more unlikely to be cracked in mounting the multilayer ceramic capacitor 10 onto a mounting substrate with the use of a mounter.

Further, in regard to LE 1 and LE 3 , a cross section is exposed by polishing the side surface 12 c , 12 d of the multilayer ceramic capacitor 10 until the dimension in the width direction W is reduced down to about ½. The dimensions can be obtained by observing the cross section of the multilayer ceramic capacitor from the principal surface 12 b with the use of an optical microscope, and measuring the length of the external electrode in the center in the width direction W.

In addition, in regard to LE 2 and LE 4 , a cross section is exposed by polishing the side surface 12 c , 12 d of the multilayer ceramic capacitor 10 until the dimension in the width direction W is reduced down to about ½. The dimensions can be obtained by observing the cross section of the multilayer ceramic capacitor 10 from the principal surface 12 a with the use of an optical microscope, and measuring the length of the external electrode in the center in the width direction W.

In addition, in regard to LE 5 to LE 8 , a cross section is first exposed by polishing the side surface 12 c , 12 d of the multilayer ceramic capacitor 10 until the dimension in the width direction W is reduced down to about ½. This cross section is observed with the use of an optical microscope to specify the thickest portion of the external electrode located on the principal surface. Next, the dimensions can be obtained by measuring the distance between the thickest portion and the outermost end of the external electrode.

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 6 of 11

In this regard, in the multilayer ceramic capacitor 10 , the dimensions a, b, c, d, e, and f shown in FIG. 9 are defined as follows: “a” is a distance in the height direction between the principal surface 12 a and an effective portion EP that refers to a region where the first internal electrodes 16 a and the second internal electrodes 16 b are opposed in the height direction T; “b” is a distance in the length direction between the end surface 12 e and the effective portion EP in the length direction L; “c” is a thickness of the thickest portion of the base layer 24 a provided over the principal surface 12 a ; “d” is a distance in the length direction L between a point of the base layer 24 a over the end surface 12 e which is farthest from the end surface 12 e and an end of the base layer 24 a over the principal surface 12 a which is closest to the end surface 12 f ; “e” is a thickness of the thickest portion of the base layer 24 a provided over the end surface 12 e ; and “f” is a height of the ceramic body 12 .

In the multilayer ceramic capacitor 10 , the ratio (c·d+e·f/2)/(a·b) is preferably about 6 or less. For this reason, with a large (a·b), the ridges of the ceramic body 12 are increased in strength. In addition, the tensile stress applied to the ridges of the ceramic body 12 is low because the base layer 24 a is thin with a small (c·d+e·f/2). Therefore, the multilayer ceramic capacitor 10 is unlikely to be cracked from the ridges of the ceramic body 12 .

Furthermore, the ratio (c·d+e·f/2)/(a·b) is preferably about 2 or more. Thus, the base layer 24 a can be made not to be excessively thin. Accordingly, the multilayer ceramic capacitor 10 has excellent resistance to moisture.

Further, the thicknesses of the base layers 24 a , 24 b can be measured through the observation of, with a microscope, a cross section exposed by polishing the side surface 12 c or side surface 12 d of the multilayer ceramic capacitor 10 until the height of the multilayer ceramic capacitor 10 is reduced to about ½.

The distance a in the height direction between the effective portion EP where the first internal electrodes 16 a and the second internal electrodes 16 b are opposed in the height direction T, and the principal surface 12 a can be measured through the observation of, with a microscope, a cross section exposed by polishing the side surface 12 c or side surface 12 d of the multilayer ceramic capacitor 10 until the height of the multilayer ceramic capacitor 10 is reduced to about ½.

In the length direction L, the distance b in the length direction between the end surface 12 e and the effective portion EP is regarded as the distance between the second internal electrode 16 b extending closest to the end surface 12 e among the second internal electrodes 16 b and the end surface 12 e in a cross section exposed by polishing the side surface 12 c or side surface 12 d of the multilayer ceramic capacitor 10 until the height of the multilayer ceramic capacitor 10 is reduced to about ½.

The height f of the ceramic body 12 can be obtained by measuring the height of the center in the width direction W in a cross section exposed by polishing the end surface 12 e or end surface 12 f of the ceramic body 12 until the height of the ceramic body 12 in the length direction L is reduced to about ½.

Furthermore, FIG. 10 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 . The multilayer ceramic capacitor 10 according to the present invention is achieved by meeting any of the conditions (1) to (5) listed below.

Condition 1

The internal electrode located closest to the principal surface 12 a is configured so that the multilayer ceramic capacitor 10 is about 0.9 mm or more and about 1.1 mm or less in dimension in the length direction L, the multilayer ceramic capacitor 10 is about 0.4 mm or more and about 0.6 mm or less in dimension in the width direction W, the multilayer ceramic capacitor 10 is about 0.085 mm or more and about 0.11 mm or less in dimension in the height direction T, and the ratio (T MAX −T MIN )/T of about 1.0% to about 5.0% is met. The target dimensions of the multilayer ceramic capacitor 10 preferably are about 1.0 mm in dimension in the length direction L, about 0.5 mm in dimension in the width direction W, and about 0.10 mm in dimension in the height direction T.

Condition 2

The internal electrode located closest to the principal surface 12 a is configured so that the multilayer ceramic capacitor 10 is about 0.9 mm or more and about 1.1 mm or less in dimension in the length direction L, the multilayer ceramic capacitor 10 is about 0.4 mm or more and about 0.6 mm or less in dimension in the width direction W, the multilayer ceramic capacitor 10 is about 0.12 mm or more and about 0.15 mm or less in dimension in the height direction T, and the ratio (T MAX −T MIN )/T of about 1.3% to about 5.3% is met. The target dimensions of the multilayer ceramic capacitor 10 preferably are about 1.0 mm in dimension in the length direction L, about 0.5 mm in dimension in the width direction W, and about 0.15 mm in dimension in the height direction T.

Condition 3

The internal electrode located closest to the principal surface 12 a is configured so that the multilayer ceramic capacitor 10 is about 0.9 mm or more and about 1.1 mm or less in dimension in the length direction L, the multilayer ceramic capacitor 10 is about 0.4 mm or more and about 0.6 mm or less in dimension in the width direction W, the multilayer ceramic capacitor 10 is about 0.18 mm or more and about 0.20 mm or less in dimension in the height direction T, and the ratio (T MAX −T MIN )/T of about 1.5% to about 5.0% is met. The target dimensions of the multilayer ceramic capacitor 10 are about 1.0 mm in dimension in the length direction L, about 0.5 mm in dimension in the width direction W, and about 0.20 mm in dimension in the height direction T.

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 7 of 11

Condition 4

The internal electrode located closest to the principal surface 12 a is configured so that the multilayer ceramic capacitor 10 is about 0.9 mm or more and about 1.1 mm or less in dimension in the length direction L, the multilayer ceramic capacitor 10 is about 0.4 mm or more and about 0.6 mm or less in dimension in the width direction W, the multilayer ceramic capacitor 10 is about 0.21 mm or more and about 0.23 mm or less in dimension in the height direction T, and the ratio (T MAX −T MIN )/T of about 1.8% to about 5.9% is met. The target dimensions of the multilayer ceramic capacitor 10 preferably are about 1.0 mm in dimension in the length direction L, about 0.5 mm in dimension in the width direction W, and about 0.22 mm in dimension in the height direction T.

Condition 5

The internal electrode located closest to the principal surface 12 a is configured so that the multilayer ceramic capacitor 10 is about 0.9 mm or more and about 1.1 mm or less in dimension in the length direction L, the multilayer ceramic capacitor 10 is about 0.4 mm or more and about 0.6 mm or less in dimension in the width direction W, the multilayer ceramic capacitor 10 is about 0.24 mm or more and about 0.30 mm or less in dimension in the height direction T, and the ratio (T MAX −T MIN )/T of about 1.2% to about 6.0% is met. The target dimensions of the multilayer ceramic capacitor 10 preferably are about 1.0 mm in dimension in the length direction L, about 0.5 mm in dimension in the width direction W, and about 0.25 mm in dimension in the height direction T.

This multilayer ceramic capacitor 10 preferably meets any of the conditions (1) to (5). Thus, the ceramic body 12 is reinforced in a preferred manner with the first internal electrodes 16 a and the second internal electrodes 16 b , and the stress applied to the ceramic body 12 when the multilayer ceramic capacitor 10 is mounted with the use of a mounter is dispersed. Accordingly, the ceramic body 12 is more unlikely to be cracked in mounting the multilayer ceramic capacitor 10 . Because cracks are unlikely to be generated, the generation of short circuit defects in the multilayer ceramic capacitor 10 is also effectively suppressed or prevented.

It is to be noted that T, T MAX , and T MIN can be each measured by observing, with the use of a microscope, a cross section exposed by polishing the end surface 12 e or end surface 12 f of the multilayer ceramic capacitor 10 until the dimension in the length direction L is reduced down to about ½.

Furthermore, FIG. 11 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

Multilayer ceramic capacitors preferably have external electrodes that are unlikely to be peeled from ceramic bodies. In the multilayer ceramic capacitor 10 , reactive layers 28 containing about 5 atomic % to about 15 atomic % of Ti, about 5 atomic % to about 15 atomic % of Si, and about 2 atomic % to about 10 atomic % of V are preferably provided between the ceramic body 12 and the base layers 24 a , 24 b . Thus, in the multilayer ceramic capacitor 10 , the external electrodes 22 a , 22 b are unlikely to be peeled from the ceramic body 12 .

It is to be noted that as a cause of the fact that the external electrodes are unlikely to be peeled, for example, it is conceivable that when the ceramic body with the base layers formed is immersed in a plating bath in order to form plated layers, glass in the base layers is eluted to decrease the adhesion strength between the base layers and the ceramic body. The reactive layers 28 containing about 5 atomic % to about 15 atomic % of Ti, about 5 atomic % to about 15 atomic % of Si, and about 2 atomic % to about 10 atomic % of V are preferably formed between the ceramic body 12 and the base layers 24 a , 24 b . The reactive layer 28 which has this composition is formed in such a way that the ceramic body 12 is reacted with a base paste in firing the ceramic body 12 . The reactive layers 28 have low solubility in plating baths such as a sulfuric acid Cu bath, a pyrophosphoric acid Cu bath, and a cyanide Cu bath. For this reason, the adhesion strength between the base layers 24 a , 24 a and the ceramic body 12 is unlikely to be decreased in the case of forming the plated layers 26 a , 26 b by Cu plating. Accordingly, the external electrodes 22 a , 22 b are unlikely to be peeled on the ceramic body 12 .

In addition, from the perspective of effective suppression or prevention of peeling of the external electrodes 22 a , 22 b , the maximum thickness of the reactive layer 28 is preferably about 0.5 μm to about 5 μm. The external electrodes are peeled from the ceramic body when the maximum thickness of the reactive layer 28 is smaller than about 0.5 μm, whereas the deflective strength is decreased because of a decrease in the strength itself of the ceramic body 12 when the maximum thickness of the reactive layer 28 is larger than about 5 μm.

Furthermore, FIG. 12 shows a cross-sectional view of a preferred embodiment of a multilayer ceramic capacitor according to the present invention, which is able to achieve a greater effect, along the line III-III of FIG. 1 .

In this case, in the multilayer ceramic capacitor 10 , the thickness of the thickest portion of the first external electrode 22 a located on the end surface 12 e is referred to as t 1 in a cross section passing through the center in the width direction W and extending in the length direction L and the height direction T.

In addition, in the multilayer ceramic capacitor 10 , the thickness of the thickest portion of the first external electrode 22 a located on the principal surface 12 a is referred to as t 2 in a cross section passing through the center in the width direction W and extending in the length direction L and the height direction T.

Furthermore, in the multilayer ceramic capacitor 10 , the thickness of the first external electrode 22 a on a line passing through the point of intersection between a tangent line on a corner of the ceramic body 12 and the corner and the point of intersection between a line along the principal surface 12 a and a line along the end surface 12 e is referred to as t 3 in a cross section passing through the center in the width direction W and extending in the length direction L and the height direction T.

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 8 of 11

The multilayer ceramic capacitor 10 preferably is embedded into a multilayer printed wiring board, and used. In such a case, the multilayer ceramic capacitor 10 preferably has excellent resistance to moisture, and excellent adhesion to the resin constituting the multilayer printed wiring board.

As a result of earnest study, it has been found that the shape of the external electrode is related to the moisture resistance of the multilayer ceramic capacitor 10 and the adhesion thereof to the resin. Specifically, the relationships among t 1 to t 3 can control the moisture resistance and the adhesion to the resin.

More specifically, in the multilayer ceramic capacitor 10 , the ratio t 2 /t 1 is preferably about 0.7 to about 1.0, and the ratio t 3 /t 1 is preferably about 0.4 to about 1.2. Thus, the multilayer ceramic capacitor 10 has excellent resistance to moisture, and excellent adhesion to the resin of the multilayer printed wiring board.

An excessively small ratio t 2 /t 1 may result in failure to sufficiently ensure the thicknesses of the external electrodes around corners of the ceramic body, and ingress of plating solutions, etc., into the multilayer ceramic capacitor 10 , thus decreasing reliability of resistance to moisture. On the other hand, an excessively large ratio t 2 /t 1 may eliminate the roundness of the external electrodes around corners of the ceramic body, and make stress more likely to be concentrated on the corners, thus decreasing the adhesion between the multilayer ceramic capacitor 10 and the resin of the multilayer printed wiring board.

An excessively small ratio t 3 /t 1 may result in failure to sufficiently ensure the thicknesses of the external electrodes, and ingress of plating solutions, etc., into the multilayer ceramic capacitor 10 , thus decreasing the moisture resistance. On the other hand, an excessively large ratio t 3 /t 1 may eliminate the roundness of the external electrodes around corners of the ceramic body, and make stress more likely to be concentrated on the corners, thus decreasing the adhesion between the multilayer ceramic capacitor 10 and the resin of the multilayer printed wiring board.

It is to be noted that t 1 to t 3 can be measured in the following manner.

Method of t 1 Measurement

Method of t 2 Measurement

Method of t 3 Measurement

A cross section is exposed by polishing the side surface 12 c or side surface 12 d of the multilayer ceramic capacitor 10 until the height of the multilayer ceramic capacitor 10 in the width direction W is reduced down to about ½. The thickness t 3 of the first external electrode 22 a on the line passing through the point of intersection between the tangent line on the corner of the ceramic body 12 and the corner and the point of intersection between the line along the principal surface 12 a and the line along the end surface 12 e can be measured by observing the cross section with the use of a microscope.

It is to be noted that, although not shown, the first external electrode 22 a and the second external electrode 22 b , or respective portions of the first external electrode 22 a and second external electrode 22 b (more specifically, respective portions of the base layer 24 a and base layer 24 b ) may be embedded in the ceramic body 12 . In this case, when the thicknesses of central portions of the principal surface portions 23 a , 23 b of the external electrode 22 a on the principal surfaces 12 a , 12 b are referred to as t 0 , whereas the maximum thickness of the portion of the external electrode 22 a embedded in the ceramic body 12 is referred to as t 1 , the condition of ( 1/10)t 0 ≦t 1 ≦(⅖)t 0 is preferably met. Likewise, when the thicknesses of central portions of the principal surface portions 23 c , 23 d of the external electrode 22 b on the principal surfaces 12 a , 12 b are referred to as t 0 , whereas the maximum thickness of the portion of the external electrode 22 b embedded in the ceramic body 12 is referred to as t 1 , the condition of ( 1/10)t 0 ≦t 1 ≦(⅖)t 0 is preferably met.

When t 1 is less than ( 1/10)t 0 , the adhesion between the external electrodes 22 a , 22 b and the ceramic body 12 may be excessively decreased to make the external electrodes 22 a , 22 b more likely to be peeled, thus decreasing the reliability of the multilayer ceramic capacitor 10 . In addition, when t 1 is less than ( 1/10)t 0 , the portions of the external electrodes 22 a , 22 b , which are not embedded, may be excessively increased in height to sufficiently reduce the multilayer ceramic capacitor 10 in height.

On the other hand, when t 1 is greater than (⅖)t 0 , the reliability of the multilayer ceramic capacitor 10 may be decreased. More specifically, there is a possibility that high stress will be applied to the internal electrode 16 a or the internal electrode 16 b to damage the internal electrode 16 a or the internal electrode 16 b , when the external electrodes 22 a , 22 b are embedded in the principal surfaces 12 a , 12 b of the ceramic body 12 . As a result, desired capacitance is unable to be obtained, or short circuit may be caused.

As a method for measuring the embedded amounts (t 0 and t 1 ), the side surface 12 c , 12 d of the multilayer ceramic capacitor 10 can be polished for a cross section along the length direction L down to about ½ the dimension in the width direction W, and the thicknesses of the central portions of the external electrodes 22 a , 22 b at the points in the cross section can be measured with an optical microscope or the like.

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 9 of 11

In addition, edge ends of the external electrodes 22 a , 22 b formed on the principal surfaces 12 a , 12 b of the ceramic body 12 preferably have linear shapes in planar view (that is, preferably not crescent shapes). As shown in FIGS. 13A and 13B , the linear shape refers to, when the line connecting both ends at end edges of the external electrodes 22 a , 22 b formed on the principal surfaces 12 a , 12 b is regarded as a reference line P in planar view, a shape where the width h with respect to the reference line P is not more than about ±30 μm away from the positions of the centers in the width direction W (the positions at about ½ dimensions in the width direction W) of the end edges of the external electrodes 22 a , 22 b . Thus, the external electrodes 22 a , 22 b can be uniformly formed even on both ends of the ceramic body 12 in the width direction W. As a result, even when the laser for irradiation is somewhat shifted in embedding the multilayer ceramic capacitor 10 into a multilayer printed wiring board, it is possible to irradiate the surfaces of the external electrodes 22 a , 22 b with the laser, and the probability of joint is increased between the via hole and the multilayer ceramic capacitor 10 .

The dimensions of the multilayer ceramic capacitor 10 are preferably about 0.9 mm or more and about 1.1 mm or less in the length direction L, about 0.4 mm or more and about 0.6 mm or less in the width direction W, and about 0.085 mm or more and about 0.15 mm or less in the height direction T.

In the case of the multilayer ceramic capacitor 10 , the arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b is larger than the arithmetic mean roughness (Ra) at the surface of the ceramic body 12 . More specifically, the ratio of the arithmetic mean roughness (Ra) at the surface of the ceramic body 12 /the arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b falls within the range of about 0.06 or more and about 0.97 or less. Thus, in close contact between the resin of the multilayer printed wiring board and the multilayer ceramic capacitor 10 , the close contact between the external electrodes 22 a , 22 b and the resin in the embedding recess for the capacitor, which is provided in the multilayer printed wiring board, is stronger than the close contact between the ceramic body 12 and the resin in the embedding recess for the capacitor, which is provided in the multilayer printed wiring board. Therefore, gaps are more unlikely to be produced between the external electrodes 22 a , 22 b and the resin in the embedding recess for the capacitor, which is provided in the multilayer printed wiring board, and ingress of moisture into the gaps is also suppressed or prevented. As a result, reliability of resistance to moisture is ensured for the multilayer ceramic capacitor 10 .

Next, a non-limiting example of a method for producing the previously described multilayer ceramic capacitor 10 will be described. FIG. 14 is a flowchart showing a method for manufacturing the multilayer ceramic capacitor 10 .

In a step S 1 , slurry for sheet forming is prepared in such a way that an organic binder, a dispersant, and a plasticizer, etc. are added to a ceramic powder containing a barium titanate material, a strontium titanate material, or the like. Next, the slurry for sheet forming is formed into ceramic green sheets for inner layers or outer layers by a doctor blade method.

Next, in a step S 2 , an internal electrode paste containing Ag is applied onto the ceramic green sheets for inner layers by a screen printing method, thus forming electrode paste films to define and function as the first internal electrodes 16 a and the second internal electrodes 16 b.

Next, in a step S 3 , the plurality of ceramic green sheets for inner layers, which have the electrode paste films formed, are stacked so as to alternate the electrode paste films for the first internal electrodes 16 a and the electrode paste films for the second internal electrodes 16 b . Furthermore, the plurality of ceramic green sheets defining outer layers without any electrode paste films formed for internal electrodes are stacked so as to sandwich the stacked ceramic green sheets for inner layers, and pressed by pressure bonding to prepare a mother laminated body.

In this regard, as for the mold for use in the press, the mold is provided with appropriate surface roughness to obtain the ceramic body 12 with desired arithmetic mean roughness (Ra). It is to be noted that the surface of the ceramic body 12 may be subjected to a physical impact (for example, polishing) or chemical treatment (for example, acid etching), as a method for providing the surface of the ceramic body 12 with desired arithmetic mean roughness (Ra).

Then, this mother laminated body is cut along a virtual cut line on the mother laminated body with a dicing machine or a pushing machine into a size for individual ceramic bodies 12 to provide a plurality of unfired ceramic bodies 12 (raw ceramic laminated bodies).

The unfired ceramic bodies 12 have ridges and corners shaped in R by barrel polishing.

Next, in a step S 4 , the unfired ceramic bodies 12 are subjected to binder removal treatment, and then firing to provide sintered ceramic bodies 12 . The firing temperature can be set appropriately depending on the types of the ceramic material and conductive paste used. The firing temperature can be, for example, about 900° C. or higher and about 1300° C. or lower. The ceramic green sheets for inner layers and outer layers and the electrode paste films are subjected to co-firing to turn the ceramic green sheets for inner layers into the ceramic layers 14 for inner layers, turn the ceramic green sheets defining outer layers into the ceramic layers 14 defining outer layers, and turn the electrode paste films into the first internal electrodes 16 a or the second internal electrodes 16 b.

Next, in a step S 5 , a base paste (a paste containing Cu and glass) for the external electrodes 22 a , 22 b is applied by a method such as dipping to both ends of the sintered ceramic body 12 . The base paste applied to the ceramic body 12 is subjected to hot-air drying for about 10 minutes in the range of about 60° C. or higher and about 180° C. or lower, for example.

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 10 of 11

Next, in a step S 6 , the base paste applied to the ceramic body 12 is baked.

Thus, the base layers 24 a , 24 b of the external electrodes 22 a , 22 b are formed. The baking temperature is preferably adjusted to, for example, about 780° C. or higher and about 900° C. or lower.

Next, in a step S 7 , plated layers are formed on the surfaces of the base layers 24 a , 24 b to form the external electrodes 22 a , 22 b . Thereafter, through immersion in a roughening liquid, the external electrodes 22 a , 22 b are obtained which have desired arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b . It is to be noted that the surfaces of the external electrodes 22 a , 22 b may be subjected to a physical impact (for example, polishing), as a method for providing the surfaces of the external electrodes 22 a , 22 b with desired arithmetic mean roughness (Ra). Then, the formation can be achieved so that the ratio of the arithmetic mean roughness (Ra) at the surface of the ceramic body/the arithmetic mean roughness at the surface of the external electrode falls within the range of about 0.06 or more and about 0.97 or less.

Next, if necessary, in a step S 8 , a cleaning process is applied to the multilayer ceramic capacitor 10 in order to obtain the multilayer ceramic capacitor 10 with small impurity amounts (contamination amounts) of K (potassium) and S (sulfur). Pure water or an extremely low concentration of sulfuric acid or hydrochloric acid is used for the cleaning liquid. For cleaning the multilayer ceramic capacitor 10 , various methods are selected depending on the size, shape, amount of throughput, etc, for products. For example, the capacitor is stirred in a cleaning tank, or cleaned by a batch process. Alternatively, the capacitor is subjected to shower cleaning with a cleaning liquid while being transferred, or subjected to ultrasonic cleaning. In this way, the multilayer ceramic capacitor 10 is obtained which has small impurity amounts (contamination amounts) of K (potassium) and S (sulfur).

It is to be noted that in the step S 5 , in the case of applying the base paste by dipping, the position of the maximum thickness of the base paste formed on the principal surfaces 12 a , 12 b of the ceramic body 12 can be varied by adjusting the rheology of the base paste, carrying out surface treatment of the ceramic body, and applying the base paste twice, if necessary. In this way, the external electrodes 22 a , 22 b can be formed so that the ratio E/e between the dimensions E and e for the external electrodes 22 a , 22 b falls within the range of about 0.243≦E/e≦about 0.757.

In addition, the multilayer ceramic capacitor 10 which is able to achieve a greater effect, as shown in FIG. 7 , can be obtained by, in the step S 3 , for control, changing the stacked number of ceramic green sheets for inner layers or ceramic green sheets defining outer layers, and appropriately changing the height A of the effective portion, the height B of the ceramic layer for an outer layer closer to the principal surface 12 a , and the height C of the ceramic layer for an outer layer closer to the principal surface 12 b.

In addition, the multilayer ceramic capacitor 10 which is able to achieve a greater effect, as shown in FIG. 8 , can be obtained by, in the step S 5 , appropriately controlling the lengths in the length direction L of the portions of the external electrodes located on the principal surfaces in accordance with the following method. More specifically, the lengths in the length direction of the portions of the external electrodes located on the principal surfaces can be controlled by, for example, varying the wettability of the ceramic body to the conductive paste. The wettability of the ceramic body to the base paste can be varied by, for example, applying a surfactant, or carrying out plasma treatment or the like.

Furthermore, the multilayer ceramic capacitor 10 which is able to achieve a greater effect, as shown in FIG. 9 , can be obtained in such a way that the distance a in the height direction T between the effective portion EP where the first internal electrodes 16 a and the second internal electrodes 16 b are opposed in the height direction T and the principal surface 12 a is varied appropriately by increasing or decreasing the stacked number of ceramic green sheets defining outer layers in the step S 3 .

In addition, in the step S 2 , the distance b in the length direction between the end surface 12 e and the effective portion EP can be controlled in the length direction L by appropriately changing the size of the electrode figure of a printing plate used to form the internal electrodes on the ceramic green sheets for inner layers.

Furthermore, the height f of the ceramic body 12 can be arbitrarily varied depending on the combination of the height of the ceramic green sheets for inner layers with the internal electrodes formed or the ceramic green sheets defining outer layers, that is, the effective layers, with the ceramic layers 14 defining outer layers in the step S 3 .

Further, for the multilayer ceramic capacitor 10 which is able to achieve a greater effect, as shown in FIG. 9 , the thickness c of the portion of the base layer 24 a provided over the principal surface 12 a is able to be adjusted depending on the combination of the viscosity of the base paste in which the ceramic body 12 is immersed for dipping, the paste thickness in the paste bath, the pull-up rate after the immersion of the ceramic body 12 in the step S 5 .

In addition, in the step S 5 , the distance d in the length direction L between the thickest portion of the base layer 24 a provided over the end surface 12 e and a portion of the base layer 24 a located closest to the end surface 12 f , which is located over the principal surface 12 a is able to be controlled with the viscosity of the base paste in which the ceramic body 12 is immersed for dipping, the paste thickness in the paste bath, and the period of time for which the ceramic body 12 is immersed in the paste.

›DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS · 11 of 11

Furthermore, in the step S 5 , the thickness e of the portion of the base layer 24 a provided over the end surface 12 e is able to be adjusted depending on the combination of the viscosity of the base paste in which the ceramic body 12 is immersed for dipping, the paste thickness in the paste bath, the pull-up rate after the immersion of the ceramic body 12 . In addition, depending on the condition for the pull-up, it is possible to change the magnitude relationship with the thickness of the portion of the base layer 24 a provided over the principal surface 12 a.

In addition, the multilayer ceramic capacitor 10 which is able to achieve a greater effect, as shown in FIG. 10 , can be obtained in such a way that a ceramic green sheet for an outer layer, ceramic green sheets for inner layers with electrode paste films formed in shapes corresponding to the first internal electrodes 16 a or the second internal electrodes 16 b , and a plurality of ceramic green sheets defining outer layers are stacked in this order, and pressed in the stacking direction to prepare a mother laminated body in the step S 3 .

Specifically, the mother laminated body is pressed with the use of a first pressing tool that has a plate-shaped pressing surface and a second pressing tool that has a pressing surface with a plurality of recesses and protrusions. Thereafter, the mother laminated body is further pressed with the use of a pair of pressing tools that have plate-shaped pressing surfaces. In this way, the mother laminated body can be prepared which has electrode paste films including a plurality of recesses and protrusions.

In addition, the multilayer ceramic capacitor 10 which is able to achieve a greater effect, as shown in FIG. 11 , can be obtained by appropriately controlling the type of the glass and the amount of the glass in the base paste which forms the base layers, with regard to the composition of the reactive layers. In addition, the reactive layers can be controlled, as for the thicknesses thereof, by appropriately changing the baking temperature for the base layers in the step S 6 .

Specifically, the base paste for use in the formation of the base layers includes a metal powder and SiO 2 —B 2 O 3 -based glass frit, and the glass frit preferably contains SiO 2 : about 10 weight % to about 50 weight %, B 2 O 2 : about 10 weight % to about 30 weight %, and V 2 O 5 : about 1 weight % to about 10 weight % in terms of oxide. The glass frit is preferably contained in an amount of about 0.5 weight % to about 10 weight % with respect to 100 weight % of the metal powder.

In addition, the baking temperature for the base layers is preferably about 730° C. to about 850° C.

In addition, the multilayer ceramic capacitor 10 which is able to achieve a greater effect, as shown in FIG. 12 , can be obtained in such a way that t 1 to t 3 are varied by appropriately controlling, for example, the viscosity of the base paste for forming the base layers 24 a , 24 b , the rate of immersing the ceramic body 12 in the base paste, the rate of pulling up the body, the condition for drying the base paste, etc., in the step S 5 .

In this way, the desired multilayer ceramic capacitor 10 is obtained.

›EXPERIMENTAL EXAMPLES · 1 of 2

In experimental examples, respective samples of multilayer ceramic capacitors were prepared according to the following examples and comparative examples.

1. Preparation of Sample for Evaluation

In the experimental examples, samples for the evaluation of the multilayer ceramic capacitor 10 were prepared by controlling the arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b , without control for impurity reduction in the step S 8 of the manufacturing method mentioned in the previously described preferred embodiment, and control for changing the position of the maximum thickness of the base paste formed on the principal surfaces 12 a , 12 b of the ceramic body 12 in the step S 5 thereof. The target dimensions of the multilayer ceramic capacitor 10 are about 1.0 mm in dimension in the length direction L, about 0.5 mm in dimension in the width direction W, and about 0.15 mm in dimension in the height direction T.

Respective samples according to Examples 1 to 12 and Comparative Examples 1 to 7 were each prepared by varying the arithmetic mean roughness (Ra) at the surface of the ceramic body 12 and the arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b.

2. Calculation of Arithmetic Mean Roughness (Ra) at Surface of Ceramic Body

In order to calculate the arithmetic mean roughness (Ra) at the surface of the ceramic body 12 , as a measurement condition, a laser microscope (from Keyence Corporation; Product Name: VK-9510) preferably was used at a 100-fold lens magnification in a color ultradeep mode set. The measurement area with the laser microscope was regarded as a region of about 90 μm square including a central portion of the principal surface 12 a of the ceramic body 12 . The numerical values of the data were calculated as average values for 72 samples.

3. Calculation of Arithmetic Mean Roughness (Ra) at Surface of External Electrode

In order to calculate the arithmetic mean roughness (Ra) at the surfaces of the external electrodes 22 a , 22 b , as a measurement condition, a laser microscope (from Keyence Corporation; Product Name: VK-9510) preferably was used at a 100-fold lens magnification in a color ultradeep mode set. The measurement area with the laser microscope was regarded as a region of 90 μm square including central portions of the principal surface portions 23 a to 23 d (portions of the external electrodes 22 a , 22 b provided on the pair of principal surfaces of the ceramic body 12 ) of the external electrodes 22 a , 22 b . The numerical values of the data were calculated as average values for 72 samples.

Table 1 shows the values of: the arithmetic mean roughness (Ra) at the surface of the ceramic body; the arithmetic mean roughness (Ra) at the surfaces of the external electrodes; and the ratio of the arithmetic mean roughness (Ra) at the surface of ceramic body/the arithmetic mean roughness (Ra) at the surfaces of the external electrodes, for each of the samples according to Examples 1 to 12 and Comparative Examples 1 to 7.

Then, for each of the samples, after embedding the multilayer ceramic capacitor 10 in a substrate, the multilayer ceramic capacitor 10 was evaluated by a moisture resistance load test and a laser resistance test in the following manner.

4. Moisture Resistance Load Test Method

The samples of the multilayer ceramic capacitors according to the examples and the comparative examples were each embedded in a substrate (approximate dimensions 15 mm×5 mm×1 mm) including an interlayer insulating layer of resin and including a via electrode capable of being electrically connected to the multilayer ceramic capacitor from the exterior. Thereafter, the substrates with the respective samples of the multilayer ceramic capacitors embedded therein were subjected to a thermal shock cycle test. As a condition for the thermal shock cycle test, the substrates for use in the test were maintained for about 30 minutes under an environment at a low temperature of about −55° C., and thereafter maintained for about 30 minutes under an environment at a temperature of about 125° C. This cycle was regarded as one cycle, and 20 cycles were conducted alternately at the low temperature and the high temperature. Furthermore, thereafter, a moisture resistance acceleration test was carried out under a condition at about 2 V for about 72 hours in a high-temperature and high humidity bath at 125° C. and relative humidity of 95% RH, and when the insulation resistance value (IR value) was decreased by two or more orders of magnitude, the moisture resistance was determined to be degraded. For this moisture resistance load test, 72 pieces were prepared for each of the samples according to the examples and the comparative examples.

5. Laser Resistance Test Method

For each of the samples of multilayer ceramic capacitors according to the examples and the comparative examples, central portions of the principal surface portions 23 a to 23 d of the external electrodes 22 a , 22 b were irradiated with a laser to confirm whether the Cu plating was left or not with a metallograph after irradiation. Portions without no Cu plating left were determined to be defective. The following condition was made as the laser irradiation condition.

Laser Irradiation Condition

Output: 12 A Mask Diameter: 1.4 mm in diameter Pulse Width: 16 μs Energy: 3.5 mJ The Number of Shots: 5 shots Pulse Mode: burst Frequency: 4000 Hz

For this laser resistance test, 20 pieces were prepared for each of the samples according to the examples and the comparative examples.

The results of the tests mentioned above are shown in Table 1.

From the results in Table 1, in Comparative Examples 1 and 2, the ratio of the arithmetic mean roughness (Ra) at the ceramic body surface/the arithmetic mean roughness (Ra) at the external electrode surfaces falls within the range of less than about 0.06, and the arithmetic mean roughness (Ra) at the external electrode surfaces is relatively large in magnitude. Thus, laser resistance has failed to be ensured at the surfaces of the external electrodes, thus producing multilayer ceramic capacitors with no Cu plating left. This is believed to be because the roughened surfaces of the external electrodes 22 a , 22 b increases the laser absorption efficiency, thus resulting in burns.

›EXPERIMENTAL EXAMPLES · 2 of 2

In addition, in Comparative Examples 3 to 7, the ratio of the arithmetic mean roughness (Ra) at the ceramic body surface/the arithmetic mean roughness (Ra) at the external electrode surfaces falls within the range of about 1.00 or more, and from the results of the moisture resistance reliability test, the multilayer ceramic capacitors have moisture resistance degraded, with insulation resistance values (IR values) decreased by two or more orders of magnitude. This is believed to be because, due to the fact that the arithmetic mean roughness (Ra) at the ceramic body surface is equal to or more than the arithmetic mean roughness (Ra) at the external electrode surfaces, the generation of gaps between the surfaces of the external electrodes 22 a , 22 b and the resin in the embedding recesses for the capacitors, formed in the substrates, caused ingress of moisture into the multilayer ceramic capacitors, thus degrading the insulation resistance values (IR values).

On the other hand, in Examples 1 to 12, the ratio of the arithmetic mean roughness (Ra) at the ceramic body surface/the arithmetic mean roughness (Ra) at the external electrode surfaces falls within the range of about 0.06 or more and about 0.97 or less, thus leading to stronger close contact between the external electrode surfaces and the resin in the embedding recesses for the capacitors, formed in the substrate, and it has been thus confirmed that the moisture resistance reliability test also shows favorable results. In addition, it has been confirmed that the laser resistance is ensured with the laser absorption efficiency decreased, because the laser is reflected at the surfaces of the external electrodes 22 a , 22 b.

Therefore, in the case of the multilayer ceramic capacitors according to Examples 1 to 12, the ratio of the arithmetic mean roughness (Ra) at the ceramic body surface/the arithmetic mean roughness (Ra) at the external electrode surfaces falls within the range of about 0.06 or more and about 0.97 or less, thus leading to stronger close contact between the external electrode surfaces and the resin in the embedding recesses for the capacitors, provided in the substrate, and gaps are unlikely to be generated between the external electrodes and the resin in the substrates, even when external forces act after embedding the substrates. As a result, ingress of moisture into the multilayer ceramic capacitors is suppressed or prevented, and reliability of resistance to moisture is thus ensured for the multilayer ceramic capacitors.

In the preferred embodiments and experimental examples mentioned above, the side surfaces of the ceramic bodies also preferably include external electrodes provided thereon, but there is no need to provide the external electrodes on the side surfaces of the ceramic bodies.

Multilayer ceramic capacitors according to the present invention may be used in a preferred manner, in particular, as a multilayer ceramic capacitor built in a multilayer printed board.

While preferred embodiments of the present invention have been described above, it is to be understood that variations and modifications will be apparent to those skilled in the art without departing from the scope and spirit of the present invention. The scope of the present invention, therefore, is to be determined solely by the following claims.

›Tables in the description — 1

TABLE 1

	Arithmetic	Arithmetic Mean	Arithmetic Mean Surface	The Number of
	Mean Surface	Surface	Roughness (Ra) at Surface	Defective in	The number of
	Roughness (Ra)	Roughness (Ra)	of Ceramic Main Body/	Moisture	Defectives in
	at Surface of	at External	Arithmetic Mean Surface	Resistance	Laser
	Ceramic Main	Electrode	Roughness (Ra) at External	Reliability	Resistance
	Body	Surface	Electrode Surface	Test	Test
Comparative Example 1	0.05	1.23	0.04	0/72	7/20
Comparative Example 2	0.05	1.00	0.05	0/72	5/20
Example 1	0.05	0.80	0.06	0/72	0/20
Example 2	0.05	0.45	0.11	0/72	0/20
Example 3	0.05	0.23	0.22	0/72	0/20
Example 4	0.08	0.23	0.35	0/72	0/20
Example 5	0.13	0.34	0.38	0/72	0/20
Example 6	0.53	0.80	0.66	0/72	0/20
Example 7	0.63	0.90	0.70	0/72	0/20
Example 8	0.32	0.45	0.71	0/72	0/20
Example 9	0.62	0.80	0.78	0/72	0/20
Example 10	0.53	0.63	0.84	0/72	0/20
Example 11	0.45	0.52	0.87	0/72	0/20
Example 12	0.32	0.33	0.97	0/72	0/20
Comparative Example 3	0.45	0.45	1.00	1/72	0/20
Comparative Example 4	0.53	0.45	1.18	2/72	0/20
Comparative Example 5	0.13	0.10	1.30	4/72	0/20
Comparative Example 6	0.45	0.32	1.41	6/72	0/20
Comparative Example 7	0.32	0.22	1.45	7/72	0/20

Claims as granted

19 claims

Classifications

6 codes

IPC · International Patent Classification

Section H — Electricity

H01G4/232
H01G4/012
H01G4/30
H01G4/12
H05K1/11
H05K1/18

Claim changes

Soon

Coming soonHow the claims changed between publication and grant

See which claims were amended, added or cancelled during examination, with every added and removed word marked.

AmendedAddedCancelledUnchanged

The published claims of this application are not paired with the granted ones in what we hold.

File wrapper

⤢ drag to zoom

USPTOApplicanthover for detail · click to open

Pendency

2.3 y

855 days filing → grant

Office actions

non-final + final

Responses

no RCE

Examiner

Timothy Thompson

art unit 2847 · TC 2800

Law firm

Law firm · Log in to unlock

Citations: 11 back · 1 forward

See the full prosecution history — every USPTO and applicant action on this file, in order.

Documents

Log in to open the documents of this file: the application as filed, every office action and response, the notice of allowance.

Chain of title

⤢ drag to zoom

Titlehover for detail · click to open

See the full assignment history — every owner this patent has passed through, with recordation dates and reel/frame numbers.