Semiconductor light emitting device and method for manufacturing same

This is a continuation application of International Application PCT/JP2012/001803, filed on Mar. 14, 2012; the entire contents of which are incorporated herein by reference. This application also claims priority to Japanese Application No. 2011-203855, filed on Sep. 16, 2011. The entire contents of each are incorporated herein by reference.

Embodiments of the invention relates to a semiconductor light emitting device, and a method for manufacturing same.

The reduction of chromaticity variation in the development of a white light emitting diode (LED) is one of major problems. In particular, in a wafer-level packaging technique which carries out formation of a interconnect layer, protection resin, and a luminescent layer collectively for a plurality of chips within a wafer without performing a chip selection process, emission wavelength variation among the chips within the wafer affects the chromaticity variation considerably.

FIG. 1 is a schematic cross-sectional view of a semiconductor light emitting device 10 of a first embodiment;

FIG. 2A is a schematic plan view of the semiconductor light emitting device of a first embodiment, and FIG. 2B is a schematic plan view of one chip;

FIGS. 3A-3C show layouts of a plurality of chips in a semiconductor light emitting device of first embodiment;

FIG. 4 is a circuit diagram showing a connection relationship between a plurality of chips in a semiconductor light emitting device of a first embodiment;

FIGS. 5A-7D show cross sections showing a manufacturing method of the semiconductor light emitting device of a first embodiment;

FIGS. 8A-8E show cross sections showing a manufacturing method of the semiconductor light emitting device of a second embodiment;

FIGS. 9A-9D show cross sections showing a manufacturing method of the semiconductor light emitting device of a third embodiment;

FIGS. 10A-11D show cross sections showing a manufacturing method of the semiconductor light emitting device of a fourth embodiment;

FIGS. 12A-12C show cross sections showing a manufacturing method of the semiconductor light emitting device of a fifth embodiment;

FIGS. 13A-13C show cross sections showing a manufacturing method of the semiconductor light emitting device of a sixth embodiment;

FIGS. 14A and 14B show cross sections showing a manufacturing method of the semiconductor light emitting device of a seventh embodiment;

FIG. 15 is a CIExy chromaticity diagram showing adjustable range of chromaticity of a semiconductor light emitting device of a first embodiment; and

FIG. 16A is a CIExy chromaticity diagram showing adjustable range of chromaticity of semiconductor light emitting devices of a fourth and sixth embodiments, and FIG. 16B is a CIExy chromaticity diagram showing adjustable range of chromaticity of a semiconductor light emitting device of a fifth embodiment.

According to one embodiment, a semiconductor light emitting device includes: not less than three chips, each of the chips including a semiconductor layer having a first face, a second face formed on a side opposite to the first face, and a light emitting layer, a p-side electrode provided on the second face in a region having the light emitting layer, and an n-side electrode provided on the second face in a region without having the light emitting layer; and fluorescent body layers of a same kind provided on the first faces of the chips. The chips include: a central chip centrally positioned in a plan view, and at least two peripheral chips arranged symmetrically to each other sandwiching the central chip in the plan view. A thickness of the fluorescent body layer on the first face is same among the peripheral chips, and the fluorescent body layer on the first face of the central chip and the fluorescent body layers on the first faces of the peripheral chips have thicknesses different from each other.

Embodiments of the invention will now be described with reference to the drawings. In each of the drawings, like components are marked with like reference numerals.

First Embodiment

FIG. 1 is a schematic cross-sectional view of a semiconductor light emitting device 10 of a first embodiment.

FIG. 2A is a schematic plan view of the semiconductor light emitting device 10 , and FIG. 2B is a schematic plan view of one chip.

The semiconductor light emitting device 10 is a multi-tip device including a plurality of chips 3 a and 3 b in a package structure body which is formed at a wafer level to be described below. The plurality of chips 3 a and 3 b are separated from one another. Each of the chips 3 a and 3 b has a semiconductor layer 15 , a p-side electrode 16 , and an n-side electrode 17 .

The plurality of chips are denoted by different numerals 3 a and 3 b depending on a positional difference in the plan view shown in FIG. 2A . However, the chip 3 a and the chip 3 b have the same structure, and are sometimes denoted simply by a numeral 3 representatively without discrimination between the chips 3 a and 3 b.

The semiconductor layer 15 has a first face (upper face in FIG. 1 ) 15 a and a second face formed on the side opposite thereto. The electrodes and interconnects are provided on the second face side. Light is emitted to the outside mainly from the first face 15 a on the side opposite to the second face.

Furthermore, the semiconductor layer 15 has a first semiconductor layer 11 and a second semiconductor layer 12 . The first semiconductor layer 11 and the second semiconductor layer 12 are made of material containing, for example, gallium nitride. The first semiconductor layer 11 includes, for example, a foundation buffer layer, an n-type layer, and the like, and the n-type layer functions as a lateral current pathway. The second semiconductor layer 12 includes a p-type layer and a light emitting layer (active layer) 12 a.

The second face side of the semiconductor layer 15 is processed into a convex-concave shape. The convex part formed on the second face side includes the light emitting layer 12 a . On the surface of the second semiconductor layer 12 being the surface of the convex part thereof, a p-side electrode 16 is provided. That is, the p-side electrode 16 is provided on a region having the light emitting layer 12 a.

On the periphery of the convex part on the second face side of the semiconductor layer 15 , a region which does not have the second semiconductor layer 12 including the light emitting layer 12 a is provided, and, on the face of the first semiconductor layer 11 in the region, an n-side electrode 17 is provided. That is, the n-side electrode 17 is provided on the region without including the light emitting layer 12 a.

In the plan view of the second face shown in FIG. 2B , the n-side electrode 17 surrounds the periphery of the p-side electrode 16 continuously. The plan view layout of the p-side electrode 16 and the n-side electrode 17 is not limited to the layout shown in FIG. 2B and another layout can be used.

On the second face side, the area of the second semiconductor layer including the light emitting layer 12 a is larger than the area of the first semiconductor layer 11 which does not include the light emitting layer 12 a . Furthermore, the area of the p-side electrode 16 is larger than the area of the n-side electrode 17 . Accordingly, it is possible to obtain a large light emitting region.

On a side face of the second semiconductor layer 12 including the light emitting layer 12 a , an insulating film 14 is provided. Moreover, the insulating film 14 is also provided on the second face on which the p-side electrode 16 and the n-side electrode 17 are not provided. The insulating film 14 is an inorganic insulating film such as, for example, a silicon oxide film and a silicon nitride film.

The second face side, on which the insulating film 14 , the p-side electrode 16 , and the n-side electrode 17 are provided, is covered by a first insulating layer (hereinafter, simply referred to as insulating layer) 18 . The first face 15 a is not covered by the insulating layer 18 .

Furthermore, the insulating layer 18 fills a space between the chips 3 a and 3 b separated from each other, and covers sides of the chips 3 a and 3 b . A side of the semiconductor layer 15 continuing from the first face 15 a is covered by the insulating layer 18 . The insulating layer 18 covering each side face of the chips 3 a and 3 b constitutes a side face of the semiconductor light emitting device 10 together with a resin layer 25 covering a side of a interconnect part which will be described below.

The insulating layer 18 is a resin such as polyimide or the like having a good patterning properties for a fine opening, for example. Alternatively, an inorganic material such as silicon oxide or silicon nitride may be used for the insulating layer 18 .

In the insulating layer 18 , a first via 18 a reaching the p-side electrode 16 and a second via 18 b reaching the n-side electrode 17 are formed. Moreover, the insulating layer 18 has a interconnect face 18 c on the side opposite to the first face 15 a.

On the interconnect face 18 c , a p-side interconnect layer 21 and an n-side interconnect layer 22 are provided apart from each other. For each one of the chips 3 a and 3 b , one p-side interconnect layer 21 and one n-side interconnect layer 22 are provided.

The p-side interconnect layer 21 is also provided within the first via 18 a . The p-side interconnect layer 21 is electrically connected to the p-side electrode 16 through the plurality of first vias 18 a.

The n-side interconnect layer 22 is also provided within the second via 18 b . The n-side interconnect layer 22 is electrically connected to the n-side electrode 17 through one, for example, second via 18 b.

On the face of the p-side interconnect layer 21 on the side opposite to the chips 3 a and 3 b , a p-side metal pillar 23 is provided. The p-side metal pillar 23 has a thickness larger than the thickness of the p-side interconnect layer 21 . The p-side interconnect layer 21 and the p-side metal pillar 23 constitute a p-side interconnect part in the embodiment.

On the face of the n-side interconnect layer 22 on the side opposite to the chips 3 a and 3 b , an n-side metal pillar 24 is provided. The n-side metal pillar 24 has a thickness larger than the thickness of the n-side interconnect layer 22 . The n-side interconnect layer 22 and the n-side metal pillar 24 constitute an n-side interconnect part in the embodiment.

Furthermore, on the interconnect face 18 c of the insulating layer 18 , a resin layer 25 is provided as a second insulating layer. The resin layer 25 covers the periphery of the p-side interconnect part and the periphery of the n-side interconnect part.

The face of the p-side interconnect layer 21 except a connection face with the p-side metal pillar 23 and the face of the n-side interconnect layer 22 except a connection face with the n-side metal pillar 24 are covered by the resin layer 25 . Furthermore, the resin layer 25 is provided between the p-side metal pillar 23 and the n-side metal pillar 24 , and covers a side face of the p-side metal pillar 23 and a side face of the n-side metal pillar 24 . The resin layer 25 fills a space between the p-side metal pillar 23 and the n-side metal pillar 24 .

The face of the p-side metal pillar 23 on the side opposite to the p-side interconnect layer 21 is exposed without being covered by the resin layer 25 , and functions as a p-side external terminal 23 a which is to be bonded to a mounting substrate. The face of the n-side metal pillar 24 on the side opposite to the n-side interconnect layer 22 is exposed without being covered by the resin layer 25 , and functions as an n-side external terminal 24 a which is to be bonded to the mounting substrate.

The respective thicknesses of the p-side interconnect part, the n-side interconnect part, and the resin layer 25 are larger than each of the thickness of the chips 3 a and 3 b . The aspect ratio (ration of a thickness to a planar size) of the p-side metal pillar 23 and the n-side metal pillar 24 is not limited to a value not smaller than one and the ratio may be smaller than one.

The p-side metal pillar 23 , the n-side metal pillar 24 , and the resin layer 25 which reinforces the metal pillars function as a support body for the chips 3 a and 3 b . Accordingly, even when a substrate used for forming the semiconductor layer 15 is removed as will be described below, the support body including the p-side metal pillar 23 , the n-side metal pillar 24 , and the resin layer 25 supports the chips 3 a and 3 b stably, and can increase the mechanical strength of the semiconductor light emitting device 10 .

Furthermore, in a state in which the semiconductor light emitting device 10 is mounted on the mounting substrate, it is possible to reduce a stress applied to the semiconductor layer 15 , by causing the p-side metal pillar 23 and the n-side metal pillar 24 to absorb the stress.

As the material for the p-side interconnect layer 21 , the n-side interconnect layer 22 , the p-side metal pillar 23 , and the n-side metal pillar 24 , copper, gold, nickel, silver, or the like can be used. When copper is used among these materials, it is possible to obtain a good thermal conductivity, a high migration resistance and a distinguished adhesion to insulating material.

As the resin layer 25 , it is preferable to use a resin having a coefficient of thermal expansion the same as or close to the coefficient of the mounting substrate. An example of such resin can include, for example, epoxy resin, silicone resin, fluorine resin, or the like.

Furthermore, the resin layer 25 may be caused to contain carbon black to be provided with light-shielding properties for the light emitted from the light emitting layer 12 a . In addition, the resin layer 25 may be caused to contain powder having a reflectivity for the light emitted from the light emitting layer 12 a.

The first semiconductor layer 11 is electrically connected to the n-side metal pillar 24 including the n-side external terminal 24 a via the n-side electrode 17 and the n-side interconnect layer 22 . The second semiconductor layer 12 including the light emitting layer 12 a is electrically connected to the p-side metal pillar 23 including the p-side external terminal 23 a via the p-side electrode 16 and the p-side interconnect layer 21 .

A part of the n-side interconnect layer 22 overlaps the insulating layer 18 on a light emitting region including the light emitting layer 12 a . The area of the n-side interconnect layer 22 is larger than the n-side electrode 17 . Furthermore, the area of the n-side interconnect layer 22 expanded on the insulating layer 18 is larger than the area connecting the n-side interconnect layer to the n-side electrode 17 through the second via 18 b.

It is possible to obtain a high light output by the light emitting layer 12 a formed over a region larger than the n-side electrode 17 . And also, it is possible to realize a structure in which the n-side electrode 17 provided in a region, which is smaller than the light emitting region and does not include the light emitting layer 12 a , is rearranged on the mounting face side as the n-side interconnect layer 22 having an area larger than the area of this region.

The area connecting the p-side interconnect layer 21 to the p-side electrode 16 through the plurality of first vias 18 a is larger than the area connecting the n-side interconnect layer 22 to the n-side electrode 17 through the second via 18 b . Accordingly, it is possible to improve current distribution to the light emitting layer 12 a and also to improve radiation properties of heat generated in the light emitting layer 12 a.

On the first face 15 a of the semiconductor layer 15 , a fluorescent body layer 31 is provided. The fluorescent body layer 31 contains phosphor particles capable of absorbing the emitted light (excited light) from the light emitting layer 12 a and capable of emitting wavelength-converted light. The phosphor particles are dispersed in transparent resin which is transparent to the light from the light emitting layer 12 a and the wavelength-converted light of the phosphor particles. The semiconductor light emitting device 10 can emit mixed light of the light from the light emitting layer 12 a and the wavelength-converted light of the phosphor particles.

For example, when the phosphor particles are set to yellow phosphor particles emitting yellow light, it is possible to obtain white color or light bulb color as a mixed color between blue light from the light emitting layer 12 a which is made of GaN-based fluorescent material and yellow light which is the wavelength-converted light in the fluorescent body layer 31 .

For example, as shown in FIGS. 2A and 2B , the outer shape of the semiconductor light emitting device 10 in the plan view is formed in a rectangular shape, and three chips including one central chip 3 a and two peripheral chips 3 b are aligned in the longitudinal direction of the rectangle (one-dimensional direction).

The central chip 3 a is positioned at the center of the three chips in the one-dimensional alignment direction. The two peripheral chips 3 b are arranged symmetrically to each other sandwiching the central chip 3 a in the one-dimensional alignment direction.

On the central chip 3 a and the peripheral chips 3 b , the same kind of fluorescent body layers 31 are provided. For example, the fluorescent body layers 31 containing the same kind of yellow phosphor particles are provided on the central chip 3 a and the peripheral chips 3 b.

The thicknesses of the fluorescent body layers 31 provided on the first faces 15 a of the respective two peripheral chips 3 b are the same.

The thickness of the fluorescent body layer 31 on the first face 15 a in the central chip 3 a is different from the thickness of the fluorescent body layers 31 on the first faces 15 a in the peripheral chips 3 b . In an example shown in FIG. 1 , the fluorescent body layer 31 on the central chip 3 a has a thickness smaller than the thickness of the fluorescent body layers 31 on the peripheral chips 3 b.

As will be described below, the process of forming the fluorescent body layer 31 has a process of collectively supplying a liquid transparent resin in which phosphor particles are dispersed, on a plurality of chips in a wafer state and a process of performing thermal curing. Accordingly, the concentration (density) of the phosphor particles is approximately uniform within the wafer face.

Accordingly, a relatively thin fluorescent body layer 31 contains a smaller amount of the phosphor particles and a relatively thick fluorescent body layer 31 contains a larger amount of the phosphor particles. By adjusting the thickness of the fluorescent body layer 31 , it is possible to adjust the chromaticity of the mixed light of the light emitted from the chips 3 a and 3 b and the wavelength-converted light in the fluorescent body layer 31 .

FIG. 15 shows a CIExy chromaticity diagram. The coordinates A show the chromaticity of the blue light emitted from a GaN-based chip, and the coordinates B show the chromaticity of the light emitted from a yellow fluorescent body layer alone.

By adjusting the thickness of the fluorescent body layer 31 , it is possible to adjust chromaticity along a straight line shown by the broken line between the coordinates A and the coordinate B. The chromaticity can be adjusted toward the coordinates A side when the fluorescent body layer 31 is relatively thin, and the chromaticity can be adjusted toward the coordinates B side when the fluorescent body layer 31 is relatively thick.

Furthermore, FIG. 4 is a circuit diagram showing a connection relationship between the central chip 3 a and the peripheral chip 3 b.

The central chip 3 a and the peripheral chips 3 b are connected in parallel to a power supply 100 . The two peripheral chips 3 b are connected in series.

By adjusting power supplied from the power supply 100 to each of the central chip 3 a and the peripheral chips 3 b which are connected in parallel, it is possible to adjust a ratio of light emission intensity between the central chip 3 a and the peripheral chips 3 b.

For example, by changing an input current amount relatively between the central chip 3 a and the peripheral chips 3 b , it is possible to adjust the ratio of the light emission intensity between the central chip 3 a and the peripheral chips 3 b . Alternatively, by adjusting a duty ratio of the input power between the central chip 3 a and the peripheral chips 3 b , it is possible to adjust the ratio of the light emission intensity between the central chip 3 a and the peripheral chips 3 b.

When the input power (current) is increased for the central chip 3 a in which the fluorescent body layer 31 is relatively thin, the semiconductor light emitting device 10 emits mixed light having a larger amount of a blue component. When the input power (current) for the peripheral chips 3 b in which the fluorescent body layers 31 are relatively thick, the semiconductor light emitting device 10 emits mixed light having a larger amount of a yellow component.

That is, by changing the thickness of the fluorescent body layer 31 provided on the first face 15 a between the central chip 3 a and the peripheral chips 3 b and also by adjusting the input power between the central chip 3 a and the peripheral chips 3 b which are connected in parallel, it is possible to adjust the chromaticity of the mixed light emitted from the semiconductor light emitting device 10 .

Moreover, according to the embodiment, while the thickness of the fluorescent body layer 31 is changed between the center and the periphery in the plan view from the light emitting face side, the fluorescent body layers 31 which have the same thickness and arranged symmetrically to each other with respect to the center are provided on the periphery. Accordingly, when the semiconductor light emitting device 10 is viewed from the fluorescent body layer 31 side in FIG. 1 , a uniform color mixing effect and light distribution can be obtained.

FIGS. 3A to 3C show other specific examples for the plan view layout of the central chip 3 a and the peripheral chip 3 b.

The plurality of chips including the central chip 3 a and the peripheral chip 3 b may be aligned in two-dimensional directions in a plane as shown in FIGS. 3A to 3C , not limited to the one dimensional direction. The number of the central chips 3 a is not limited to one and may be not less than two. At least not less than two chips 3 b are arranged symmetrically to each other sandwiching the central chip 3 a , on the periphery of the central chip 3 a.

FIG. 3A shows a layout in which four peripheral chips 3 b are aligned in a cross shape on the periphery of one central chip 3 a.

FIG. 3B show a layout in which eight peripheral chips 3 b are aligned in a grid pattern on the periphery of one central chip 3 a.

FIG. 3C shows a layout in which 12 peripheral chips 3 b are aligned in a grid pattern on the periphery of four central chips 3 a.

In any of the specific examples of FIGS. 3A to 3C , the thickness of the fluorescent body layer 31 provided on the first face 15 a is changed between the central chip 3 a and the peripheral chip 3 b , and also the fluorescent body layers 31 having the same thickness are provided on the plurality of peripheral chips 3 b . Accordingly, when the semiconductor light emitting device is viewed from the light emitting face side, a uniform color mixing effect and light distribution can be obtained.

Next, with reference to FIG. 5A to FIG. 7D , a manufacturing method of the semiconductor light emitting device 10 of the embodiment will be explained.

FIG. 5A shows a cross section of a wafer on which the semiconductor layer 15 including the first semiconductor layer 11 and the second semiconductor layer 12 is formed on a major face of the substrate 5 . The first semiconductor layer 11 is formed on the major face of the substrate 5 , and the second semiconductor layer 12 is formed on this first semiconductor layer 11 .

For example, the first semiconductor layer 11 and the second semiconductor layer 12 which are made of gallium nitride-based material can be grown epitaxially on a sapphire substrate by an MOCVD (metal organic vapor deposition) method.

The first semiconductor layer 11 includes the foundation buffer layer and the n-type GaN layer. The second semiconductor layer 12 includes the light emitting layer 12 a (shown in FIG. 1 ) and the p-type GaN layer. For the light emitting layer 12 a , it is possible to use material emitting light of blue, violet, blue violet, near ultraviolet, ultraviolet, or the like. The face contacting the substrate 5 in the first semiconductor layer 11 is the first face 15 a of the semiconductor layer 15 .

After the semiconductor layer 15 has been formed on the substrate 5 , the second semiconductor layer 12 is selectively removed as shown in FIG. 5B by RIE (Reactive Ion Etching) using a resist which is not shown in the drawing, and the first semiconductor layer 11 is exposed selectively. The region where the first semiconductor layer 11 is exposed does not include the light emitting layer 12 a.

Next, as shown FIG. 5C , the p-side electrode 16 is formed on the face of the second semiconductor layer 12 and the n-side electrode 17 is formed on the face of the first semiconductor layer 11 . The p-side electrode 16 and the n-side electrode 17 are formed by a sputter method, an evaporation method, or the like, for example. For the p-side electrode 16 and the n-side electrode 17 , either one may be formed first and both ones may be formed with the same material at the same time.

Here, while illustration will be omitted from the process cross-sectional views after FIG. 5C , the insulating film 14 shown in FIG. 1 is formed on the second face side.

Next, a groove 6 reaching the substrate 5 is formed in the semiconductor layer 15 as shown in FIG. 5C by RIE, for example, using a resist mask which is not shown in the drawing. The grooves 6 are formed, for example, in a planar layout of a grid pattern, on the substrate 5 in a wafer state. The semiconductor layer 15 is divided into the plurality of chips 3 by the grooves 6 .

The process dividing the semiconductor layer 15 into the plurality of chips 3 may be performed in the step shown in FIG. 5B before the electrodes 16 and 17 are formed.

Next, the whole exposed part on the substrate 5 is covered by the insulating layer 18 shown in FIG. 6A . After that, the first via 18 a and the second via 18 b are formed in the insulating layer 18 by etching using a resist mask which is not shown in the drawing. The first via 18 a reaches the p-side electrode 16 and the second via 18 b reaches the n-side electrode 17 .

Next, a metal film, which is not shown in the drawing, functioning as a seed metal for plating is formed on the interconnect face 18 c which is the upper face of the insulating layer 18 , the inner wall of the first via 18 a , and the inner wall of the second via 18 b . Then, resist which is not shown in the drawing is formed selectively on the metal film, and Cu electrolytic plating using the metal film as a current path is performed.

By this plating, on the interconnect face 18 c , as shown in FIG. 6B , the p-side interconnect layer 21 and the n-side interconnect layer 22 are formed selectively. The p-side interconnect layer 21 and the n-side interconnect layer 22 are made of copper materials, for example, which are formed by plating at the same time.

The p-side interconnect layer 21 is also formed within the first via 18 a and electrically connected to the p-side electrode 16 via the metal film of the seed metal. The n-side interconnect layer 22 is also formed within the second via 18 b and electrically connected to the n-side electrode 17 via the metal film of the seed metal.

Next, Cu electrolytic plating is performed using resist which is not shown in the drawing as a mask and using the still remaining metal film as a current path. By this plating, as shown in FIG. 6C , the p-side metal pillar 23 and the n-side metal pillar 24 are formed. The p-side metal pillar 23 is formed on the p-side interconnect layer 21 , and the n-side metal pillar 24 is formed on the n-side interconnect layer 22 .

After the p-side metal pillar 23 and the n-side metal pillar 24 have been formed, the exposed part of the metal film which has been used as the seed metal is removed. Accordingly, the metal film connecting the p-side interconnect layer 21 and the n-side interconnect layer 22 is cut out.

Next, the resin layer 25 shown in FIG. 1 is formed. Then, in a state in which the chip 3 is supported by the support body including the p-side metal pillar 23 , the n-side metal pillar 24 , and the resin layer 25 , the substrate 5 is removed by a laser lift-off method, for example.

A laser beam is directed toward the first semiconductor layer 11 from the rear face side of the substrate 5 . The laser beam has a permeability to the substrate 5 and has a wavelength in the absorption region of the first semiconductor layer 11 .

When the laser beam reaches the boundary face between the substrate 5 and the first semiconductor layer 11 , the first semiconductor layer 11 near the boundary face absorbs the laser beam energy and is decomposed. For example, the first semiconductor layer 11 of the GaN-based material is decomposed into gallium (Ga) and nitrogen gas. By this decomposition reaction, a minute gap is formed between the substrate 5 and the first semiconductor layer 11 , and the substrate 5 and the first semiconductor layer 11 are separated from each other. The laser irradiation is performed plural times for respective predetermined regions over the whole wafer and the substrate 5 is removed.

Since the semiconductor layer 15 is supported by the support body thicker than the semiconductor layer 15 and a wafer state can be kept even when the substrate 5 is removed. Furthermore, the resin constituting the resin layer 25 and the metal constituting the p-side metal pillar 23 and the n-side metal pillar 24 are soft material in comparison with the semiconductor layer 15 of the GaN-based material. Accordingly, even when a large internal stress generated in the epitaxial growth forming the semiconductor layer 15 on the substrate 5 is released in a single burst at the peeling of the substrate 5 , it is possible to avoid the breakage of the chip 3 .

After the removal of the substrate 5 , the first face 15 a is cleaned and is subjected to frost processing forming unevenness as needed. By forming the minute unevenness on the first face 15 a , it is possible to improve a light extraction efficiency. After that, as shown in FIG. 7A , on the first face 15 a , the fluorescent body layer 31 is formed.

The process of forming the fluorescent body layer 31 includes a process of supplying liquid-state transparent resin in which the phosphor particles are dispersed onto the first face 15 a by a method of printing, potting, molding, compression molding, or the like and a process of performing thermal curing of the transparent resin.

After the formation of the fluorescent body layer 31 , the fluorescent body layer 31 is cut to be thinned selectively by mechanical cutting work, for example. Therefore, as shown in FIG. 7B , the variation in thickness of the fluorescent body layer 31 is given within the wafer.

The cut amount of the fluorescent body layer 31 , that is, the thickness of the fluorescent body layer 31 is set based on the measurement result of the wavelength of the light obtained on the upper face side of the fluorescent body layer 31 when each of the chips 3 a and 3 b are caused to emit light in a wafer state.

After that, the wafer is cut at the position of the groove 6 and divided into pieces of the plurality of the semiconductor light emitting devices 10 . As shown in FIG. 7C , the semiconductor light emitting device 10 is divided from the wafer as a unit including one central chip 3 a and two peripheral chips 3 b arranged symmetrically to each other sandwiching the central chip 3 a.

As described above, the thicknesses of the fluorescent body layers 31 provided on the two peripheral chips 3 b are the same as each other and the fluorescent body layers 31 provided on the peripheral chips 3 b is thicker than the fluorescent body layer 31 provided on the central chip 3 a.

Alternatively, as shown in FIG. 7D , the fluorescent body layers 31 provided on the peripheral chips 3 b may be thinner than the fluorescent body layer 31 provided on the central chip 3 a . Also in this structure of FIG. 7D , a uniform color mixing effect and light distribution can be obtained when the semiconductor light emitting device is viewed from the light emitting face side.

In dicing, since the hard sapphire substrate 5 is already removed, it is not necessary to cut the substrate 5 and it becomes easy to perform the dicing.

Furthermore, in the groove 6 , the semiconductor layer 15 is not formed but the insulating layer 18 of resin is provided. Moreover, in the lower part of the groove 6 in FIG. 7B , the resin layer 25 is provided. Accordingly, in the dicing region, the semiconductor layer 15 is not provided but the resin which is softer than the semiconductor layer 15 is provided. Therefore, it is possible to avoid a damage the semiconductor layer 15 receives during the dicing. In addition, in the dicing region, also the interconnect layer or the metal pillar is not provided.

Each of the processes before the dicing is collectively performed in a wafer state. Accordingly, after the dicing, it is not necessary to form the support body and protect chips by the insulating material, for each of the semiconductor light emitting devices 10 , and thus it become possible to reduce production cost significantly. In a state of being divided into pieces, the side faces of the chips 3 a and 3 b is already covered and protected by the insulating layer 18 .

Second Embodiment

FIG. 8D is a schematic cross-sectional view of a semiconductor light emitting device of a second embodiment.

This semiconductor light emitting device, as the first embodiment, also includes, for example, one central chip 3 a and two peripheral chips 3 b arranged symmetrically to each other sandwiching the central chip 3 a . The configurations of the chip and a support body supporting the chip are the same as the configurations in the first embodiment.

Furthermore, the central chip 3 a and the peripheral chips 3 b are connected in parallel to a power supply, and by adjusting power supplied from the power supply to each of the central chip 3 a and the peripheral chips 3 b , it is possible to adjust a ratio of light emission intensity between the central chip 3 a and the peripheral chips 3 b.

The thicknesses of the fluorescent body layers 31 provided on the two peripheral chips 3 b are the same as each other. Moreover, the thickness of the fluorescent body layer 31 on the central chip 3 a and the thickness of the fluorescent body layers 31 on the peripheral chips 3 b are different from each other. In the second embodiment, the fluorescent body layer 31 is not provided on the central chip 3 a and the thickness of the fluorescent body layer 31 on the central chip 3 a is zero. That is, the expression in which the thickness of the fluorescent body layer 31 is different between the central chip 3 a and the peripheral chips 3 b includes the presence or absence of the fluorescent body layer 31 .

Also in the second embodiment, by varying the thickness of the fluorescent body layer 31 between the central chip 3 a and the peripheral chips 3 b and also by adjusting input power between the central chip 3 a and the peripheral chips 3 b which are connected in parallel, it is possible to adjust the chromaticity of mixed light emitted from the semiconductor light emitting device.

Moreover, the fluorescent body layers 31 which are arranged symmetrically to each other with respect to the center and which have the same thickness are provided on the peripheral. Accordingly, it is possible to obtain a uniform color mixing effect and light distribution when the semiconductor light emitting device is viewed from the fluorescent body layer 31 side. 0

Furthermore, when the thickness of the fluorescent body layer 31 is varied between the central chip 3 a and the peripheral chips 3 b , the thickness of the fluorescent body layer 31 on the central chip 3 a is set to zero, that is, the fluorescent body layer 31 is not provided on the central chip 3 a . Accordingly, the usage of the fluorescent body layer 31 can be reduced and cost reduction is realized.

Here, from the central chip 3 a , light is emitted also in a direction oblique to the first face 15 a and the light can travel in the fluorescent body layers 31 on the peripheral chips 3 b . Accordingly, the fluorescent body layer 31 on the peripheral chip 3 b can perform wavelength conversion also by excitation of the light emitted from the central chip 3 a.

Next, with reference to FIGS. 8A to 8D , a manufacturing method of the semiconductor light emitting device of the second embodiment will be explained.

The process up to the removal of the substrate 5 is carried out as in the first embodiment.

After a substrate 5 has been removed, as shown in 8 A, a sacrifice layer 41 is formed on the chip 3 a selected from among the chips within the wafer.

When the sacrifice layer 41 is a resin having photosensitivity, after the sacrifice layer 41 has been formed over the whole face of the wafer, the sacrifice layer 41 is exposed selectively through the use of a photo-mask. After the exposure, the sacrifice layer 41 is removed selectively by development.

Alternatively, after an inorganic sacrifice layer 41 has been formed over the whole face of the wafer, resist is formed on the sacrifice layer 41 . Then, by exposure and development of the resist, the resist is patterned. Then, through the use of the patterned resist as a mask, the sacrifice layer 41 is etched selectively.

For example, the sacrifice layer 41 is formed on the plurality of chips within the wafer every other chip in the one-dimensional alignment direction.

After the formation of the sacrifice layer 41 , the fluorescent body layer 31 is formed on the wafer. As shown in 8 B, the fluorescent body layer 31 fills a space between the sacrifice layer 41 and the sacrifice layer 41 and is formed on the chip 3 b on which the sacrifice layer 41 is not formed.

By forming the sacrifice layer 41 so as to cause the cross section thereof to have a trapezoidal shape, the upper end opening of a space between the sacrifice layer 41 and the sacrifice layer 41 becomes wider than the bottom part and embedding properties of the fluorescent body layer 31 are improved.

After that, the fluorescent body layer 31 on the sacrifice layer 41 is removed by cutting work, for example, and the upper face of the sacrifice layer 41 is exposed. Then, as shown in FIG. 8C , the sacrifice layer 41 is removed selectively. The fluorescent body layer 31 is left on the chip 3 b.

Then, as in the first embodiment, the wafer is cut at the position of a groove 6 and divided into pieces of the semiconductor light emitting devices. As shown in FIG. 8D , the semiconductor light emitting device is divided from the wafer in a unit including one central chip 3 a and two peripheral chips 3 b arranged symmetrically to each other sandwiching the central chip 3 a.

As described above, the thicknesses of the fluorescent body layers 31 provided on the two peripheral chips 3 b are the same as each other and the fluorescent body layer 31 is not provided on the central chip 3 a.

Alternatively, as shown in FIG. 8E , the semiconductor light emitting device may have a structure in which the fluorescent body layer 31 is provided on the central chip 3 a and the fluorescent body layers 31 are not provided on the peripheral chips 3 b . Also in this structure of FIG. 8E , since the thickness of the fluorescent body layer 31 on the periphery is varied (zero thickness) symmetrically with respect to the center, a uniform color mixing effect and light distribution can be obtained when the semiconductor light emitting device is viewed from the light emitting face side.

By the process using the sacrifice layer 41 , it is possible easily to form the fluorescent body layer 31 selectively in a wafer level.

Third Embodiment

FIG. 9C is a schematic cross-sectional view of a semiconductor light emitting device of a third embodiment.

This semiconductor light emitting device, as the first embodiment, also includes one central chip 3 a and two peripheral chips 3 b arranged symmetrically to each other sandwiching the central chip 3 a , for example. The configurations of the chip and a support body supporting the chip are the same as the configurations in the first embodiment.

Furthermore, the central chip 3 a and the peripheral chips 3 b are connected in parallel to a power supply, and, by adjusting power supplied from the power supply to each of the central chip 3 a and the peripheral chips 3 b , it is possible to adjust a ratio of light emission intensity between the central chip 3 a and the peripheral chips 3 b.

The thicknesses of the fluorescent body layers 31 provided on the two peripheral chips are the same as each other. Furthermore, the thickness of the fluorescent body layer 31 on the central chip 3 a and the thickness of the fluorescent body layer 31 on the peripheral chips 3 b are different from each other. In the third embodiment, the fluorescent body layer 31 is not provided on the central chip 3 a and the thickness of the fluorescent body layer 31 on the central chip 3 a is zero. Then, on the central chip 3 a , a transparent resin layer 42 which is transparent to light emitted from the light emission layer is provided. By the transparent resin layer 42 , the first face 15 a of the central chip 3 a can be protected.

Also in the third embodiment, by varying the thickness of the fluorescent body layer 31 between the central chip 3 a and the peripheral chips 3 b and also by adjusting input power for each of the central chip 3 a and the peripheral chips 3 b which are connected in parallel, it is possible to adjust the chromaticity of mixed light emitted from the semiconductor light emitting device.

Moreover, the fluorescent body layers 31 which are arranged symmetrically to each other with respect to the center and have the same thickness are provided on the peripheral. Accordingly, it is possible to obtain a uniform color mixing effect and light distribution when the semiconductor light emitting device is viewed from the fluorescent body layer 31 side.

Furthermore, when the thickness of the fluorescent body layer 31 is varied between the central chip 3 a and the peripheral chip 3 b , the thickness of the fluorescent body layer 31 on the central chip 3 a is set to zero, that is, the fluorescent body layer 31 is not provided on the central chip 3 a . Accordingly, the usage of the fluorescent body layer 31 can be reduced and cost reduction is realized.

Next, with reference to FIGS. 9A to 9C , a manufacturing method of the semiconductor light emitting device of the third embodiment will be explained.

The process up to the removal of the substrate 5 is carried out as in the first embodiment.

After the substrate 5 has been removed, as shown in 9 A, the transparent resin layer 42 is formed on the chip 3 a selected among the chips within the wafer.

When the transparent resin layer 42 is a resin having photosensitivity, after the transparent resin layer 42 has been formed over the whole face of the wafer, the transparent resin layer 42 is subjected to selective exposure by the use of a photo-mask. After the exposure, the transparent resin layer 42 is removed selectively by development.

Alternatively, after the transparent resin layer 42 has been formed over the whole face of the wafer, resist is formed on the transparent resin layer 42 . Then, by exposure and development of the resist, the resist is patterned. After that, by the use of the patterned resist as a mask, the transparent resin layer 42 is etched selectively.

For example, the transparent resin layer 42 is formed on the plurality of chips within the wafer every other chip in the one-dimensional alignment direction.

After the formation of the transparent resin layer 42 , the fluorescent body layer 31 is formed on the wafer. As shown in 9 B, the fluorescent body layer 31 fills a space between the transparent resin layer 42 and the transparent resin layer 42 and is formed on the chip 3 b on which the transparent resin layer 42 is not formed.

After that, as in the first embodiment, the wafer is cut at the position of a groove 6 and divided into pieces of the semiconductor light emitting devices. As shown in FIG. 9C , the semiconductor light emitting device is divided from the wafer in a unit including one central chip 3 a and two peripheral chips 3 b arranged symmetrically to each other sandwiching the central chip 3 a.

As described above, the thicknesses of the fluorescent body layers 31 provided on the two peripheral chips 3 b are the same as each other and on the central chip 3 a , the fluorescent body layer 31 is not provided but the transparent resin layer 42 is provided.

Alternatively, as shown in FIG. 9D , the semiconductor light emitting device may have a structure in which the fluorescent body layer 31 is provided on the central chip 3 a and the transparent resin layers 42 are provided on the peripheral chips 3 b instead of the fluorescent body layers 31 . Also in this structure of FIG. 9D , since the thickness of the fluorescent body layer 31 on the periphery is varied (zero thickness) symmetrically with respect to the center, a uniform color mixing effect and light distribution can be obtained when the semiconductor light emitting device is viewed from the light emitting face side.

Fourth Embodiment

FIG. 11D is a schematic cross-sectional view of a semiconductor light emitting device of a fourth embodiment.

This semiconductor light emitting device also includes one central chip 3 a and two peripheral chips 3 b and 3 c arranged symmetrically to each other sandwiching the central chip 3 a , for example. The configurations of the chip and a support body supporting the chip are the same as the configurations in the first embodiment.

Of the two peripheral chips 3 b and 3 c , a first fluorescent body layer 32 is provided on one peripheral chip 3 b and a second fluorescent body layer 33 is provided on the other chip 3 c.

The kinds of the first fluorescent body layer 32 and the second fluorescent body layer 33 are different from each other. The first fluorescent body layer 32 has a structure in which green phosphor particles, emitting green light when receiving excitation light from the chip, are dispersed in transparent resin. The second fluorescent body layer 33 has a structure in which red phosphor particles, emitting red light when receiving excitation light form the chip, are dispersed in transparent resin.

The thickness of the first fluorescent body layer 32 provided on the peripheral chip 3 b and the thickness of the second fluorescent body layer 33 provided on the peripheral chip 3 c are the same as each other. A fluorescent body layer is not provided on the central chip 3 a and the thickness of the fluorescent body layer on the central chip 3 a is zero.

The central chip 3 a , the peripheral chip 3 b , and the peripheral chip 3 c have the same configuration and emit blue light. Consequently, according to the semiconductor light emitting device of the fourth embodiment, the blue light from each of the chips, the green light from the first fluorescent body layer 32 , and the red light from the second fluorescent body layer 33 are mixed, and white color or light bulb color are obtained.

Furthermore, the central chip 3 a , the peripheral chip 3 b , and the peripheral chip 3 c are connected in parallel to a power supply, and, by adjusting power supplied from the power supply to each of the chips, it is possible to adjust ratios of emission intensity among the chips, and it is possible to adjust the chromaticity of the mixed light emitted from the semiconductor light emitting device.

Here, from the central chip 3 a , light is emitted also in a direction oblique to the first face 15 a and the light can travel in the first fluorescent body layer 32 on the peripheral chip 3 b and in the second fluorescent body layer 33 on the peripheral chip 3 c . Accordingly, the first fluorescent body layer 32 and the second fluorescent body layer 33 can perform wavelength conversion also by excitation of the light emitted from the central chip 3 a.

FIG. 16A shows a CIExy chromaticity diagram. The coordinates C show the chromaticity of the blue light emitted from the central chip 3 a on which a fluorescent body layer is not provided. The coordinates D show the chromaticity of mixed light of the emission light of the peripheral chip 3 b and the emission light of the first fluorescent body layer 32 thereon. The coordinates E show the chromaticity of mixed light of the emission light of the peripheral chip 3 c and the emission light of the second fluorescent body layer 33 thereon.

By adjusting input power for each of the central chip 3 a , the peripheral chip 3 b , and the peripheral chip 3 c , it is possible to realize a chromaticity within a triangular range having the coordinates C, D, and E as apexes.

Next, with reference to FIGS. 10A to 11D , a manufacturing method of the semiconductor light emitting device of the fourth embodiment will be explained.

The process up to the removal of the substrate 5 is carried out as in the first embodiment.

After a substrate 5 has been removed, as shown in 10 A, a first sacrifice layer 43 is formed on the chip selected among the chips within the wafer. In a partial cross section of the wafer shown in FIG. 10A , the first sacrifice layer 43 is formed on the two chips 3 a and 3 c neighboring each other.

When the first sacrifice layer 43 is a resin having photosensitivity, after the first sacrifice layer 43 has been formed over the whole face of the wafer, the first sacrifice layer 43 is subjected to selective exposure through the use of a photo-mask. After the exposure, the first sacrifice layer 43 is removed selectively by development.

Alternatively, after an inorganic first sacrifice layer 43 has been formed over the whole face of the wafer, resist is formed on the first sacrifice layer 43 . Then, by exposure and development of the resist, the resist is patterned. After that, through the use of the patterned resist as a mask, the first sacrifice layer 43 is etched selectively.

After the formation of the first sacrifice layer 43 , as shown in FIG. 10B , the first fluorescent body layer 32 is formed on the wafer. The first fluorescent body layer 32 is formed on the chip 3 b on which the first sacrifice layer 43 is not formed.

After that, the first fluorescent body layer 32 on the first sacrifice layer 43 is removed by cutting work, for example, and, as shown in FIG. 10C , the upper face of the first sacrifice layer 43 is exposed. Then, as shown in FIG. 10D , the first sacrifice layer 43 is removed selectively. The first fluorescent body layer 32 is left on the chip 3 b.

Next, on one chip 3 a of two neighboring chips 3 a and 3 c on which the first sacrifice layers 43 are removed, as shown in FIG. 10E , a second sacrifice layer 44 is formed. The second sacrifice layer 44 can be formed by the same method as the first sacrifice layer 43 .

After the formation of the second sacrifice layer 44 , as shown in FIG. 11A , the second fluorescent body layer 33 is formed on the wafer. The second fluorescent body layer 33 is formed on the chip 3 c on which the first fluorescent body layer 32 is not formed or the second sacrifice layer 44 is not formed.

After that, the second fluorescent body layers 33 on the first fluorescent body layer 32 and the second sacrifice layer 44 are removed by cutting work, for example, and as shown in FIG. 11B , the upper face of the first fluorescent body layer 32 and the upper face of the second sacrifice layer 44 are exposed.

Then, as shown in FIG. 11C , the second sacrifice layer 44 is removed selectively. The first fluorescent body layer 32 is left on the chip 3 b , and the second fluorescent body layer 33 is left on the chip 3 c.

After that, as in the first embodiment, the wafer is cut at the position of a groove 6 and divided into pieces of the semiconductor light emitting devices. As shown in FIG. 11D , the semiconductor light emitting device is divided from the wafer in a unit including one central chip 3 a and two peripheral chips 3 b and 3 c aligned symmetrically to each other sandwiching the central chip 3 a.

By the process using the first sacrifice layer 43 and the second sacrifice layer 44 , it is possible easily to form the structure including, in one package, the central chip 3 a on which a fluorescent body layer is not provided, the peripheral chip 3 b on which the first fluorescent body layer 32 is provided, and the peripheral chip 3 c on which the second fluorescent body layer 33 of a kind different from the first fluorescent body layer 32 is provided, in a wafer level.

Fifth Embodiment

FIG. 12C is a schematic cross-sectional view of a semiconductor light emitting device of a fifth embodiment.

This semiconductor light emitting device also includes one central chip 3 a and two peripheral chips 3 b and 3 c arranged symmetrically to each other sandwiching the central chip 3 a , for example. The configurations of the chip and a support body supporting the chip are the same as the configurations in the first embodiment.

Of the two peripheral chips 3 b and 3 c , the first fluorescent body layer 32 is provided on one peripheral chip 3 b and the second fluorescent body layer 33 is provided on the other chip 3 c . On the central chip 3 a , a third fluorescent body layer 34 is provided.

The kinds of the first fluorescent body layer 32 , the second fluorescent body layer 33 , and the third fluorescent body layer 34 are different from one another. The first fluorescent body layer 32 has a structure in which green phosphor particles emitting green light when receiving excitation light from the chip, are dispersed in transparent resin. The second fluorescent body layer 33 has a structure in which red phosphor particles emitting red light when receiving excitation light form the chip, are dispersed in transparent resin. The third fluorescent body layer 34 has a structure in which blue phosphor particles emitting blue light when receiving excitation light from the chip, are dispersed in transparent resin.

The central chip 3 a , the peripheral chip 3 b , and the peripheral chip 3 c have the same configuration and emit ultraviolet light or near-ultraviolet light. The ultraviolet light or near-ultraviolet light emitted from the chips 3 a and 3 b is not a component directly constituting white light.

That is, according to the semiconductor light emitting device of the fifth embodiment, the green light from the first fluorescent body layer 32 , the red light from the second fluorescent body layer 33 and the blue light from the third fluorescent body layer 34 are mixed, and white color or light bulb color is obtained.

Furthermore, the central chip 3 a , the peripheral chip 3 b , and the peripheral chip 3 c are connected in parallel to a power supply, and, by adjusting power supplied from the power supply to each of the chips, it is possible to adjust ratios of light emission intensity among the chips, and it is possible to adjust the chromaticity of the mixed light emitted from the semiconductor light emitting device.

FIG. 16B shows a CIExy chromaticity diagram. The coordinates H show the chromaticity of the emission light (blue light) of the third single fluorescent body layer 34 . The coordinates I show the chromaticity of the emission light (green light) of the first single fluorescent body layer 32 . The coordinates J show the chromaticity of the emission light (red light) of the second single fluorescent body layer 33 .

By adjusting input power for the central chip 3 a , the peripheral chip 3 b , and the peripheral chip 3 c , it is possible to realize a chromaticity within a triangular range having the coordinates H, I, and J as apexes.

Next, with reference to FIGS. 12A to 12C , a manufacturing method of the semiconductor light emitting device of the fifth embodiment will be explained.

The process up to the removal of the second sacrifice layer 44 shown in FIG. 11C is carried out as in the fourth embodiment.

After the second sacrifice layer 44 has been removed, as shown in FIG. 12A , the third fluorescent body layer 34 is formed on the wafer. The third fluorescent body layer 34 is formed on the chip 3 a on which the second sacrifice layer 44 is removed.

After that, the third fluorescent body layers 34 on the first fluorescent body layer 32 and the second fluorescent body layer 33 are removed by cutting work, for example, and as shown in FIG. 12B , the upper face of the first fluorescent body layer 32 and the upper face of the second fluorescent body layer 33 are exposed.

Then, the wafer is cut at the position of a groove 6 and divided into pieces of the semiconductor light emitting devices. As shown in FIG. 12C , the semiconductor light emitting device is divided from the wafer in a unit including one central chip 3 a and two peripheral chips 3 b and 3 c arranged symmetrically to each other sandwiching the central chip 3 a.

According to the fifth embodiment, by the process using the first sacrifice layer 43 and the second sacrifice layer 44 , it is possible easily to form the structure including, in one package, the peripheral chip 3 b on which the first fluorescent body layer 32 is provided, the peripheral chip 3 c on which the second fluorescent body layer 33 of a kind different from the first fluorescent body layer 32 is provided, and the central chip 3 a on which the third fluorescent body layer 34 of a kind different from the first fluorescent body layer 32 and the second fluorescent body layer 33 is provided, in a wafer level.

Sixth Embodiment

FIG. 13C is a schematic cross-sectional view of a semiconductor light emitting device of a sixth embodiment.

This semiconductor light emitting device is different from the semiconductor light emitting device of the fourth embodiment which is shown in FIG. 11D in the point that optical filter films 51 are formed on the upper face of the first fluorescent body layer 32 and the upper face of the second fluorescent body layers 33 .

The optical filter film 51 is a dielectric multilayer film, for example, and has a reflectivity for the blue light emitted from the chips 3 a and 3 b . The optical filter film 51 has a permeability to the green light emitted from the first fluorescent body layer 32 and the red light emitted from the second fluorescent body layer 33 a.

FIG. 16A shows a CIExy chromaticity diagram. The coordinates C show the chromaticity of the blue light emitted from the central chip 3 a on which a fluorescent body layer is not provided. The coordinates F show the chromaticity of the emission light (green light) from the first fluorescent body layer (green fluorescent body layer) 32 on the upper face of which the optical filter film 51 is provided. The coordinates G show the chromaticity of the emission light (red light) from the second fluorescent body layer (red fluorescent body layer) 33 on the upper face of which the optical filter film 51 is provided.

According to the sixth embodiment, by adjusting input power for the central chip 3 a , the peripheral chip 3 b , and the peripheral chip 3 c , it is possible to realize a chromaticity within a triangular range having the coordinates C, F, and G as apexes.

In the sixth embodiment, on the upper face of the green fluorescent body layer and the upper face of the red fluorescent body layer, the optical filter film 51 is provided reflecting the blue light from the chip. Accordingly, it is possible to expand the chromaticity adjustable range in the sixth embodiment more than in the fourth embodiment which can realize a chromaticity within the rectangular range having the coordinates C, D, and E as apexes.

Next, with reference to FIGS. 13A to 13C , a manufacturing method of the semiconductor light emitting device of the sixth embodiment will be explained.

The process up to the formation of the second fluorescent body layer 33 shown in FIG. 11B is carried out as in the fourth embodiment.

Then, after the second fluorescent body layer 33 has been formed, as shown in FIG. 13A , the optical filter film 51 is formed on the upper face of the first fluorescent body layer 32 , the upper face of the second sacrifice layer 44 , and the upper face of the second fluorescent body layer 33 over the whole face of the wafer.

Next, as shown in FIG. 13B , the second sacrifice layer 44 is removed selectively. The optical filter film 51 on the upper face of the second sacrifice layer 44 is removed by lift-off together with the second sacrifice layer 44 .

After that, the wafer is cut at the position of a groove 6 and divided into pieces of the semiconductor light emitting devices. As shown in FIG. 13C , the semiconductor light emitting device is divided from the wafer in a unit including one central chip 3 a and two peripheral chips 3 b and 3 c arranged symmetrically to each other sandwiching the central chip 3 a.

By the process using the first sacrifice layer 43 and the second sacrifice layer 44 , it is possible easily to form the structure including, in one package, the central chip 3 a on which a fluorescent body layer is not provided, the peripheral chip 3 b on which the optical filter film 51 and the first fluorescent body layer 32 are provided, and the peripheral chip 3 c on which the optical filter film 51 and the second fluorescent body layer 33 are provided, in a wafer level.

Seventh Embodiment

FIG. 14B is a schematic cross-sectional view of a semiconductor light emitting device of a seventh embodiment.

This semiconductor light emitting device is different from the semiconductor light emitting device of the fourth embodiment which is shown in FIG. 11D in that a transparent resin layer 52 is provided on the central chip 3 a . The transparent resin layer 52 is transparent to the light emitted from the chips 3 a and 3 b . By the transparent resin layer 52 , the first face 15 a of the central chip 3 a can be protected.

Next, with reference to FIGS. 14A to 14B , a manufacturing method of the semiconductor light emitting device of the seventh embodiment will be explained.

The process up to the removal of second sacrifice layer 44 shown in FIG. 11C is carried out as in the fourth embodiment.

Then, on the chip 3 a on which the second sacrifice layer 44 is removed, as shown in FIG. 14A , the transparent resin layer 52 is formed.

Then, the wafer is cut at the position of a groove 6 and divided into pieces of the semiconductor light emitting devices. As shown in FIG. 14B , the semiconductor light emitting device is divided from the wafer in a unit including one central chip 3 a and two peripheral chips 3 b and 3 c arranged symmetrically to each other sandwiching the central chip 3 a.

According to the seventh embodiment, by the process using the first sacrifice layer 43 and the second sacrifice layer 44 , it is possible to easily form the structure at a wafer level, including, in one package, the peripheral chip 3 b on which the first fluorescent body layer 32 is provided, the peripheral chip 3 c on which the second fluorescent body layer 33 of a kind different from the first fluorescent body layer 32 , and the central chip 3 a on which the transparent resin layer 52 is provided.

In each of the above described embodiments, after removing the substrate to expose the first face 15 and before forming the fluorescent body layer, by forming an inorganic film such as a silicon nitride film over the whole face, the protection of the first face 15 and the improvement of the light extraction efficiency can be realized.

As the above described fluorescent body layer, a red fluorescent body layer, yellow fluorescent body layer, a green fluorescent body layer, or a blue fluorescent body layer to be illustrated below, can be used.

The red fluorescent body layer can contain, for example, a nitride-based fluorescent body CaAlSiN 3 :Eu or a SiAlON-based fluorescent body.

When the SiAlON-based fluorescent body is used, in particular

(M 1-x ,R x ) a1 AlSi b1 O c1 N d1   composition formula (1)

(Here, M is at least one kind of metal element excluding Si and Al, and in particular, at least either one of Ca and Sr is desirable. R is a light emission center element and in particular, Eu is desirable. x, a1, b1, c1, and d1 satisfy the following relationship. x is larger than 0 and 1 or less, a1 is larger than 0.6 and less than 0.95, b1 is larger than 2 and less than 3.9, c1 is larger than 0.25 and less than 0.45, and d1 is larger than 4 and less than 5.7) can be used.

By using the SiAlON-based fluorescent body expressed by composition formula (1), it is possible to improve the temperature characteristics of the wavelength conversion efficiency and further improve the efficiency in a large current density region.

The yellow fluorescent body layer can contain, for example, a silicate-based fluorescent body (Sr, Ca, Ba) 2 SiO 4 :Eu.

The green fluorescent body layer can contain, for example, a halophosphoric acid-based fluorescent body (Ba, Ca, Mg) 10 (PO 4 ) 6 Cl 2 :Eu or a SiAlON-based fluorescent body.

When the SiAlON-based fluorescent body is used, in particular,

(M 1-x ,R x ) a2 AlSi b2 O c2 N d2   composition formula (2)

(Here, M is at least one kind of metal element excluding Si and Al, and in particular, at least either one of Ca and Sr is desirable. R is a light emission center element and in particular, Eu is desirable. x, a2, b2, c2, and d2 satisfy the following relationship. x is larger than 0 and 1 or less, a2 is larger than 0.93 and less than 1.3, b2 is larger than 4.0 and less than 5.8, c2 is larger than 0.6 and less than 1, and d2 is larger than 6 and less than 11) can be used.

By using the SiAlON-based fluorescent body represented by composition formula (2), it is possible to improve the temperature characteristics of the wavelength conversion efficiency and further improve the efficiency in a large current density region.

The blue fluorescent body layer can contain, for example, an oxide-based fluorescent body BaMgAl 10 O 17 :Eu.

While certain embodiments have been described, these embodiments have been presented by way of example only, and are not intended to limit the scope of the inventions. Indeed, the novel embodiments described herein may be embodied in a variety of other forms; furthermore, various omissions, substitutions and changes in the form of the embodiments described herein may be made without departing from the spirit of the inventions. The accompanying claims and their equivalents are intended to cover such forms or modifications as would fall within the scope and spirit of the invention.