Woven filter fabric for a band filter

This application is the US-national stage of PCT application PCT/EP2010/002891 filed 12 May 2010, published 18 Nov. 2010 as WO2010/130412, and claiming the priority of German patent application 102009021398.8 itself filed 14 May 2009, German patent application 102009060252.6 itself filed 23 Dec. 2009, and German patent application 102010007553.1 filed 11 Feb. 2010.

The present invention relates to a filter cloth for a belt filter, in particular for use in hydrothermal acid regeneration.

In hydrothermal acid regeneration, ferric oxides, in particular Fe 2 O 3 , precipitate from a 75% aqueous FeCl 3 solution at a temperature of approximately 170° C. and are filtered out.

The hydrothermal acid regeneration in metal processing, in particular after pickling of metal strips, is concerned with the regeneration of hydrochloric acid contaminated with FeCl 2 . To do this, the following method steps are carried out.

(1) The hydrochloric acid containing FeCl 2 is concentrated. (2) FeCl 2 is oxidized with O 2 at 150° C. and 7 bar to form FeCl 3 :

2FeCl2+2HCl+½O 2 →2FeCl 3 +H 2 O

(3) Fe 2 O 3 precipitates during hydrolysis at 170° C. and atmospheric pressure. Reusable 18%-30% hydrochloric acid is obtained:

2FeCl 3 +3H 2 O→FeO 3 ↓+6HCl↑

In industrial production, Fe 2 O 3 is separated from the solution by a belt filter. A belt filter is very useful in industrial production for separating solid substances from liquids. The liquid to be filtered is conveyed onto the filter fleece web. The solid particles are retained on the filter fleece. The cleaned liquid flows into the storage tank and can be discharged from there for reuse or disposal. The residue remaining on the fleece forms a filter cake. If the density of the filter cake obstructs an optimal outflow of the liquid, the filter cake together with the fleece is transported automatically into a waste tank. The entire process is carried out continuously and fully automatically without interrupting the flow of liquid.

It has been found that the known filter cloths are not suitable to be used in a vacuum belt filter.

It is the object of the present invention to provide a belt filter that meets the requirements in terms of durability and capability of a belt filter for separating ferric oxides from acidic hot solutions under vacuum.

The object of the present invention is attained by a filter cloth for a belt filter where the filter cloth has an air permeability of 100 l/(min*dm 2 ) to 350 l/(min*dm 2 ) and the fibers of the filter cloth have a fiber thickness of 25 μm to 35 μm and 50% by weight to 100% by weight of perfluoroalkoxylalkane (PFA).

Within the meaning of the invention, air permeability means air volume in liters per time in minutes and per area in dm 2 , l/min/dm 2 , expressed as l/(min*dm 2 ).

Due to the durability and capability, the filter cloth according to the invention is suitable for a belt filter for separating ferric oxides from acidic hot solutions under vacuum.

Perfluoroalkoxylalkane (PFA) is a completely fluorinated polymer, a copolymer of polytetrafluoroethylene (PTFE) and poly-(perfluorovinylmethylether). PFA can be processed thermoplastically, for example by injection molding or polymer welding. PFA has low strength and low hardness.

A preferred embodiment of the invention is a filter cloth for a belt filter where the fibers have a fiber thickness of 28 μm to 32 μm. In this range for the fiber thickness, very good results are achieved. Particularly good results for a vacuum belt filter are achieved with a monofilament from PFA with a thickness of approximately at least 30 μm.

A preferred embodiment of the invention is a filter cloth for a belt filter where the fibers of the filter cloth contain from 90% by weight to 100% by weight of PFA. The best results are achieved with fibers that contain PFA in the range of 90% by weight to 100% by weight.

A preferred embodiment of the invention is a filter cloth for a belt filter where the filter cloth has an air permeability of 100 l/(min*dm 2 ) to 200 l/(min*dm 2 ). In this range, very good filtration results are achieved.

A preferred embodiment of the invention is a filter cloth for a belt filter where the filter cloth has 25 to 35 warp threads and 15 to 25 weft threads per 1 cm. In these ranges for warp and weft threads, very good results are achieved for the filter cloth.

A preferred embodiment of the invention is a filter cloth for a belt filter where the filter cloth is longer than 7000 mm, preferably 7000 mm to 8000 mm long, and has a width from 700 mm to 800 mm. A belt filter with these dimensions is particularly well suited and usable.

A further aspect of the invention is a method of producing a filter cloth for a belt filter with an air permeability of 100 l/(min*dm 2 ) to 350 l/(min*dm 2 ) where fibers with a thickness of 25 μm to 35 μm and with 50% by weight to 100% by weight of PFA are woven to form a filter cloth with 25 to 35 warp threads and 15 to 25 weft threads per 1 cm.

A further aspect of the invention is the use of the filter cloth according to the invention for a belt filter for separating solid ferric oxides, in particular Fe 2 O 3 , from an acidic hot aqueous FeCl 3 solution, in particular during a hydrothermal acid regeneration.

The invention is explained in more detail by means of a drawing and an example. Therein:

FIG. 1 is a perspective top view of a filter cloth according to the invention,

FIG. 2 is a perspective exploded view of a Nutsche filter with cover, and

FIG. 3 is a perspective view of a laboratory apparatus for testing a filter cloth.

The filter cloth 1 shown in FIG. 1 is illustrated with a PFA monofilament standard thread with a thickness of approximately 27 μm, with an air permeability of 100 l/(min*dm 2 ), 200 l/(min*dm 2 ) and 350 l/(min*dm 2 ). Here, weft threads 2 and warp threads 3 are woven with 31 warp threads and 20 weft threads per 1 cm to form a filter cloth 1 with a length of 8000 mm and a width of 800 mm. After weaving, the filter cloth 1 is calendered three times for adjusting the air permeability. Heat and pressure are introduced into the fabric by heating and cooling rolls. This way, the fabric shrinks by approximately 10% to 31 threads per 0.7 cm and a length of 7000 mm and a width of 700 mm.

The Nutsche filter 4 and cover 5 shown in FIG. 2 represent the important parts of a laboratory apparatus for testing the filter cloth 1 . The filter cloth 1 is placed onto the Nutsche filter 4 , and the Nutsche filter is screwed together with the cover 5 . In the lower region, the Nutsche filter 4 has a suction nozzle 6 . A vacuum hose 9 is connected to the suction nozzle 6 .

FIG. 3 shows the complete laboratory apparatus for testing a filter cloth. The vacuum hose 9 runs from the suction nozzle 6 of the Nutsche filter 4 to a pressure-equalizing container 7 . A second vacuum hose 8 that runs directly to the vacuum pump 10 is connected to the pressure-equalizing container 7 .

To be able to evaluate the effectiveness of the filter cloth 1 according to the invention, three filters with the same is structure were prepared with different materials. Beside perfluoroalkoxylalkane (PFA), polyphenylene sulfide (PPS) and polyetheretherketone (PEEK) were tested.

The properties of the three filter cloths are shown in table 1

The filtration test was carried out as follows. 450 g FeCl 3 were admixed with 60 g Fe 2 O 3 . The solids mixture was admixed with 150 ml water. The suspension was heated in a beaker to a temperature of 170° C. while stirring continuously. This way, FeCl 3 went into solution and a 75% FeCl 3 solution was formed. The content of the beaker was poured suddenly onto the filter cloth 1 . No residue remained in the beaker. The cover/beaker cap 5 was first put onto the Nutsche filter 4 , and on the lower side of the filter cloth 1 , a vacuum of 600 mbar was applied at the suction nozzle 6 . The filter cake was formed within 10 s to 15 s. The filter cloth 1 did not show any changes. The results and the comparison between the PFA according to the invention and PPS and PEEK are shown in table 2.

The PVA filter material 1 according to the invention was not damaged. Even after repeating the filter test, no changes were noted in the PFA filter cloth. The comparative filters PPS and PEEK failed during filtration and showed damage.

Analysis of the filter cake of the filter 1 according to the invention has shown that the grain sizes of Fe 2 O 3 were from 10 μm to 50 μm.

The tests were carried out with the PFA filter cloth 1 according to the invention with 200 l/(min*dm 2 ) and 100 l/(min*dm 2 ). The results of the tests made clear that by reducing air permeability, the retention of the finest particles increased, but no significantly longer filtration time was needed. The filter forms when the filter cake builds up and influences the degree of filtration through the particle size.

The results obtained were surprising and unexpected for those skilled in the art.