Isosorbide derivatives and liquid crystal displays comprising the same
Granted 16 Oct 2012 · no office action yet
Assignee: Industrial Technology Research Institute
Law firm: Law firm · Log in to unlock
Attorney: Attorney · Log in to unlock
Inventors: Chien-Hsien Cheng, Kung-Lung Cheng, Chih-Lung Chin, Kevin Lin +3 · Examiner: Shean C Wu · AU 1722 · TC 1700
Life of the application
6 dated eventsAbstract
An isosorbide derivative of Formula (I) is provided. [structure] In Formula (I), Z is —CH 2 —CH 2 —, —CH╠CH—, —C≡C—, —CH 2 —O—, —CH 2 —S—, —CH╠N—O—, —CO—O—, —CO—S—, single bond, -ph-, —CO—O-ph- or —CO—O-ph-CO—O—, and ph represents benzene, R 1 and R 2 are, independently, C1-25 alkyl, —CN, —NCS, —CX 3 or —OCX 3 , and X represents halogen, and m and n are, independently, 0, 1 or 2. The invention also provides a liquid crystal display including the isosorbide derivative.
Description
13 parts›CROSS REFERENCE TO RELATED APPLICATIONS
This Application claims priority of Taiwan Patent Application No. 99133984, filed on Oct. 6, 2010, the entirety of which is incorporated by reference herein.
›BACKGROUND OF THE INVENTION
1. Field of the Invention
The invention relates to an isosorbide derivative, and more particularly to an isosorbide derivative doped into liquid crystal materials.
2. Description of the Related Art
Recently, along with the development of the liquid crystal industry, the applications of liquid crystal materials, for various requirements, have also grown. Cholesteric liquid crystals with bistability and stable frame performance under no applied voltage are popularly applied in new-generation flat panel display technology.
Cholesteric liquid crystal materials possess a helical structure and liquid crystal characteristics. The helical structure is normally formed by doping chiral dopants into achiral cholesteric liquid crystal molecules. Thus, the helical twist of the cholesteric liquid crystals is mainly determined by helical twisting power (HTP) of the chiral dopant. Generally, various chiral structures possess various HTP values.
A chiral dopant is an optically active substance. When a chiral dopant is added to liquid crystals with a nematic phase, the liquid crystals are twisted to form a cholesteric liquid crystal phase. The helical twisting power (HTP) of the chiral dopant is mainly determined by the characteristics thereof, which are simultaneously, affected by, for example, a nematic liquid crystal host and surrounding/process temperature.
›BRIEF SUMMARY OF THE INVENTION
One embodiment of the invention provides an isosorbide derivative represented by Formula (I):
In Formula (I), Z is —CH 2 —CH 2 —, —CH═CH—, —C≡C—, —CH 2 —O—, —CH 2 —S—, —CH═N—O—, —CO—O—, —CO—S—, single bond, -ph-, —CO—O-ph- or —CO—O-ph-CO—O—, and ph represents benzene, R 1 and R 2 are, independently, C1-25 alkyl, —CN, —NCS, —CX 3 or —OCX 3 , and X represents halogen, and m and n are, independently, 0, 1 or 2.
One embodiment of the invention provides a liquid crystal display comprising an upper substrate, a lower substrate opposed to the upper substrate, and a liquid crystal layer disposed between the upper substrate and the lower substrate, comprising an isosorbide derivative represented by Formula (I):
In Formula (I), Z is —CH 2 —CH 2 —, —CH═CH—, —C≡C—, —CH 2 —O—, —CH 2 —S—, —CH═N—O—, —CO—O—, —CO—S—, single bond, -ph-, —CO—O-ph- or —CO—O-ph-CO—O—, and ph represents benzene, R 1 and R 2 are, independently, C1-25 alkyl, —CN, —NCS, —CX 3 or —OCX 3 , and X represents halogen, and m and n are, independently, 0, 1 or 2.
The invention provides a novel chiral dopant of isosorbide derivatives with a core structure of an isosorbide and a side chain containing piperazine. The disclosed isosorbide derivative effectively improves, for example, the temperature stability of cholesterol liquid crystals (for example achieving temperature dependence less than or equal to 0.2 nm/° C.). Additionally, the disclosed isosorbide derivative also possesses a large helical twisting power (HTP), for example exceeding 45 μm −1 , which considerably improves the helical twist of cholesterol liquid crystals.
A detailed description is given in the following embodiments.
›DETAILED DESCRIPTION OF THE INVENTION
The following description is of the best-contemplated mode of carrying out the invention. This description is made for the purpose of illustrating the general principles of the invention and should not be taken in a limiting sense. The scope of the invention is best determined by reference to the appended claims.
One embodiment of the invention provides an isosorbide derivative represented by Formula (I):
In Formula (I), Z may be —CH 2 —CH 2 —, —CH═CH—, —C≡C—, —CH 2 —O—, —CH 2 —S—, —CH═N—O—, —CO—O—, —CO—S—, single bond, -ph-, —CO—O-ph- or —CO—O-ph-CO—O—. The “ph” represents benzene.
R 1 and R 2 may be, independently, C1-25 alkyl, —CN, —NCS, —CX 3 or —OCX 3 . The “X” represents halogen.
Additionally, m and n may be, independently, 0, 1 or 2.
Some exemplary isosorbide derivatives of the invention are disclosed as follows:
One embodiment of the invention provides a liquid crystal display comprising an upper substrate, a lower substrate opposed to the upper substrate, and a liquid crystal layer disposed between the upper substrate and the lower substrate, comprising an isosorbide derivative represented by Formula (I):
In Formula (I), Z may be —CH 2 —CH 2 —, —CH═CH—, —C≡C—, —CH 2 —O—, —CH 2 —S—, —CH═N—O—, —CO—O—, —CO—S—, single bond, -ph-, —CO—O-ph- or —CO—O-ph-CO—O—. The “ph” represents benzene.
R 1 and R 2 may be, independently, C1-25 alkyl, —CN, —NCS, —CX 3 or —OCX 3 . The “X” represents halogen.
Additionally, m and n may be, independently, 0, 1 or 2.
The disclosed isosorbide derivative may be doped into, for example, a cholesterol liquid crystal display.
The invention provides a novel chiral dopant of isosorbide derivatives with a core structure of an isosorbide and a side chain containing piperazine. The disclosed isosorbide derivative effectively improves, for example, the temperature stability of cholesterol liquid crystals (for example achieving the temperature dependence less than or equal to 0.2 nm/° C.). Additionally, the disclosed isosorbide derivative also possesses a large helical twisting power (HTP), for example exceeding 45 μm −1 , which considerably improves helical twist of cholesterol liquid crystals.
›Examples9
›EXAMPLE 1
Synthesis of an Isosorbide Derivative of the Invention I
First, 2.2 g of 4-[4-Methyl-piperazin-1-yl]-benzoic acid (10 mmol) and 2.43 g of 1,1″-Carbonyldiimidazole (CDI) (15 mmol) were placed in a 100 mL two-neck round-bottom flask. Next, 30 mL of anhydrous tetrahydrofuran (THF) was conducted into the flask under nitrogen. After reflux for 4 hours and cooling the flask to room temperature, “A” solution was prepared.
Next, 0.45 g of isosorbide (3 mmol) was placed in another round-bottom flask and then dissolved by adding THF under an ice bath. After adding NaH to the flask, “B” solution was prepared. After two hours, “A” solution was poured into “B” solution with stirring for about two hours to warm the flask to room temperature. After complete extraction, a yellow solid was obtained. The solid was then recrystallized with MeOH to form 1.15 g of a white solid of compound A-2C1 with a yield of 70%.
›EXAMPLE 2
Synthesis of an Isosorbide Derivative of the Invention II
First, 2.76 g of 4-[4-Pentyl-piperazin-1-yl]-benzoic acid (10 mmol) and 2.43 g of 1,1″-Carbonyldiimidazole (CDI) (15 mmol) were placed in a 100 mL two-neck round-bottom flask. Next, 30 mL of anhydrous tetrahydrofuran (THF) was conducted into the flask under nitrogen. After reflux for 4 hours and cooling the flask to room temperature, “A” solution was prepared.
Next, 0.45 g of isosorbide (3 mmol) was placed in another round-bottom flask and then dissolved by adding THF under an ice bath. After adding NaH to the flask, “B” solution was prepared. After two hours, “A” solution was poured into “B” solution with stirring for about two hours to warm the flask to room temperature. After complete extraction, a yellow solid was obtained. The solid was then recrystallized with MeOH to form 1.25 g of a white solid of compound A-2C5 with a yield of 63%.
›EXAMPLE 3
Synthesis of an Isosorbide Derivative of the Invention III
First, 2.76 g of 4-[4-(1-Methyl-butyl)-piperazin-1-yl]-benzoic acid (10 mmol) and 2.43 g of 1,1″-Carbonyldiimidazole (CDI) (15 mmol) were placed in a 100 mL two-neck round-bottom flask. Next, 30 mL of anhydrous tetrahydrofuran (THF) was conducted into the flask under nitrogen. After reflux for 4 hours and cooling the flask to room temperature, “A” solution was prepared.
Next, 0.45 g of isosorbide (3 mmol) was placed in another round-bottom flask and then dissolved by adding THF under an ice bath. After adding NaH to the flask, “B” solution was prepared. After two hours, “A” solution was poured into “B” solution with stirring for about two hours to warm the flask to room temperature. After complete extraction, a yellow solid was obtained. The solid was then recrystallized with MeOH to form 1.29 g of a white solid of compound A-2IC5 with a yield of 65%.
›EXAMPLE 4
Synthesis of an Isosorbide Derivative of the Invention IV
First, 3.52 g of 4-[4-(4-Pentyl-phenyl)-piperazin-1-yl]-benzoic acid (10 mmol) and 2.43 g of 1,1″-Carbonyldiimidazole (CDI) (15 mmol) were placed in a 100 mL two-neck round-bottom flask. Next, 30 mL of anhydrous tetrahydrofuran (THF) was conducted into the flask under nitrogen. After reflux for 4 hours and cooling the flask to room temperature, “A” solution was prepared.
Next, 0.45 g of isosorbide (3 mmol) was placed in another round-bottom flask and then dissolved by adding THF under an ice bath. After adding NaH to the flask, “B” solution was prepared. After two hours, “A” solution was poured into “B” solution with stirring for about two hours to warm the flask to room temperature. After complete extraction, a yellow solid was obtained. The solid was then recrystallized with MeOH to form 1.61 g of a white solid of compound A-2BC5 with a yield of 66%.
›EXAMPLE 5
Synthesis of an Isosorbide Derivative of the Invention V
First, 2.2 g of 4-[4-Methyl-piperazin-1-yl]-benzoic acid (10 mmol) and 2.43 g of 1,1″-Carbonyldiimidazole (CDI) (15 mmol) were placed in a 100 mL two-neck round-bottom flask. Next, 30 mL of anhydrous tetrahydrofuran (THF) was conducted into the flask under nitrogen. After reflux for 4 hours and cooling the flask to room temperature, “A” solution was prepared.
Next, 1.9 g of isosorbide (13 mmol) was placed in another round-bottom flask and then dissolved by adding THF under an ice bath. After adding NaH to the flask, “B” solution was prepared. After two hours, “A” solution was poured into “B” solution with stirring for about two hours to warm the flask to room temperature. After complete extraction, a yellow solid was obtained. After column chromatography (eluent: ethyl acetate:hexane=1:1), 2.1 g of an intermediate (6 mmol) was formed with a yield of 66%.
Next, 2.21 g of 4-[4-Pentyl-piperazin-1-yl]-benzoic acid (8 mmol) and 2.43 g of 1,1″-Carbonyldiimidazole (CDI) (15 mmol) were placed in a 100 mL two-neck round-bottom flask. Next, 30 mL of anhydrous tetrahydrofuran (THF) was conducted into the flask under nitrogen. After reflux for 4 hours and cooling the flask to room temperature, “C” solution was prepared.
Next, the intermediate was placed in another round-bottom flask and then dissolved by adding THF under an ice bath. After adding NaH to the flask, “D” solution was prepared. After two hours, “C” solution was poured into “D” solution with stirring for about two hours to warm the flask to room temperature. After complete extraction, a yellow solid was obtained. The solid was then recrystallized with MeOH to form 1.83 g of a white solid of compound A-C1C5 with a yield of 50%.
›EXAMPLE 6
Synthesis of an Isosorbide Derivative of the Invention VI
First, 3.40 g of 4-(4-Carboxy-phenyl)-piperazin-1-carboxylic acid-p-tolyl ester (10 mmol) and 2.43 g of 1,1″-Carbonyldiimidazole (CDI) (15 mmol) were placed in a 100 mL two-neck round-bottom flask. Next, 30 mL of anhydrous tetrahydrofuran (THF) was conducted into the flask under nitrogen. After reflux for 4 hours and cooling the flask to room temperature, “A” solution was prepared.
Next, 0.45 g of isosorbide (3 mmol) was placed in another round-bottom flask and then dissolved by adding THF under an ice bath. After adding NaH to the flask, “B” solution was prepared. After two hours, “A” solution was poured into “B” solution with stirring for about two hours to warm the flask to room temperature. After complete extraction, a yellow solid was obtained. The solid was then recrystallized with MeOH to form 1.54 g of a white solid of compound A-2aBC1 with a yield of 65%.
›EXAMPLE 7
Synthesis of an Isosorbide Derivative of the Invention VII
First, 2.31 g of 4-(4-cyano-piperazin-1-yl)-benzoic acid (10 mmol) and 2.43 g of 1,1″-Carbonyldiimidazole (CDI) (15 mmol) were placed in a 100 mL two-neck round-bottom flask. Next, 30 mL of anhydrous tetrahydrofuran (THF) was conducted into the flask under nitrogen. After reflux for 4 hours and cooling the flask to room temperature, “A” solution was prepared.
Next, 0.45 g of isosorbide (3 mmol) was placed in another round-bottom flask and then dissolved by adding THF under an ice bath. After adding NaH to the flask, “B” solution was prepared. After two hours, “A” solution was poured into “B” solution with stirring for about two hours to warm the flask to room temperature. After complete extraction, a yellow solid was obtained. The solid was then recrystallized with MeOH to form 0.9 g of a white solid of compound A-2CN with a yield of 68%.
›EXAMPLE 8
Synthesis of an Isosorbide Derivative of the Invention VIII
First, 2.74 g of 4-(4-Trifluoromethyl-piperazin-1-yl)-benzoic acid (10 mmol) and 2.43 g of 1,1″-Carbonyldiimidazole (CDI) (15 mmol) were placed in a 100 mL two-neck round-bottom flask. Next, 30 mL of anhydrous tetrahydrofuran (THF) was conducted into the flask under nitrogen. After reflux for 4 hours and cooling the flask to room temperature, “A” solution was prepared.
Next, 0.45 g of isosorbide (3 mmol) was placed in another round-bottom flask and then dissolved by adding THF under an ice bath. After adding NaH to the flask, “B” solution was prepared. After two hours, “A” solution was poured into “B” solution with stirring for about two hours to warm the flask to room temperature. After complete extraction, a yellow solid was obtained. The solid was then recrystallized with MeOH to form 1.18 g of a white solid of compound A-2CF3 with a yield of 60%.
›EXAMPLE 9
Helical Twisting Power (HTP) and Temperature Dependence of the Isosorbide Derivatives of the Invention
The related physical-chemical properties, for example helical twisting power (HTP) and temperature dependence (dλ/dT) of the isosorbide derivatives (compounds A-2C1, A-2C5, A-2I C5, A-2BC5, A-C1C5, A-2aBC1, A-2CN and A-2CF3) of the invention are shown in Table 1. The test temperature was 20-50° C.
The results indicate that the disclosed isosorbide derivatives (compounds A-2C1, A-2C5, A-2IC5, A-2BC5, A-C1C5, A-2aBC1, A-2CN and A-2CF3) possess large helical twisting power (HTP), for example exceeding 45 μm −1 , and low temperature dependence, for example less than or equal to 0.2 nm/° C. Thus, the disclosed isosorbide derivative is considerably suitable for application in, for example, a cholesterol liquid crystal display.
While the invention has been described by way of example and in terms of preferred embodiment, it is to be understood that the invention is not limited thereto. To the contrary, it is intended to cover various modifications and similar arrangements (as would be apparent to those skilled in the art). Therefore, the scope of the appended claims should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements.
›Tables in the description — 1
| A-2C1 | A-2C5 | A-2IC5 | A-2BC5 | A-C1C5 | A-2aBC1 | A-2CN | A-2CF3 | |
|---|---|---|---|---|---|---|---|---|
| HTP | 45 | 47 | 46 | 46 | 45 | 48 | 45 | 47 |
| (μm −1 ) | ||||||||
| dλ/dT | +0.03 | −0.19 | −0.16 | −0.11 | −0.2 | −0.14 | −0.12 | −0.17 |
| (nm/° C.) |
Claims as granted
4 claimsLog in to read the claims of this application.
Log in to unlockClassifications
15 codes- C07D493/04
- C09K19/58
- C09K19/54
- C07D241/04
Claim changes
SoonSee which claims were amended, added or cancelled during examination, with every added and removed word marked.
The published claims of this application are not paired with the granted ones in what we hold.
File wrapper
See the full prosecution history — every USPTO and applicant action on this file, in order.
Log in to unlockDocuments
Log in to open the documents of this file: the application as filed, every office action and response, the notice of allowance.
Log in to unlockChain of title
See the full assignment history — every owner this patent has passed through, with recordation dates and reel/frame numbers.
Log in to unlock