The invention provides a circuit connecting method that can satisfactorily reduce connection resistance between circuit electrodes electrically connected via an anisotropic conductive film for circuit connection. The circuit connecting method comprises a step of preparing a circuit member 12 having circuit electrodes 12 b formed on a glass substrate 12 a , a step of preparing a flexible wiring board 14 having circuit electrodes 14 b formed on a base 14 a and provided with a solder resist 18 at the sections of the circuit electrodes 14 b other than the sections that are connected to the circuit electrodes 12 b , and a step of bonding the circuit member 12 to the flexible wiring board 14 via an anisotropic conductive film for circuit connection 16 so that part of the anisotropic conductive film for circuit connection 16 overlaps with part of the solder resist 18 . The thickness h 3 of the anisotropic conductive film for circuit connection 16 is no greater than the total of the height h 1 of the circuit electrodes 12 b and the height h 2 of the circuit electrodes 14 b.

Description

33 parts

›This is a National Phase Application in the…

This is a National Phase Application in the United States of International Patent Application No. PCT/JP2008/051960 filed Feb. 6, 2008, which claims priority on Japanese Patent Application No. P2007-281611, filed Oct. 30, 2007. The entire disclosures of the above patent applications are hereby incorporated by reference.

›TECHNICAL FIELD

The present invention relates to a circuit connecting method.

›BACKGROUND ART

As circuit electrode widths and circuit electrode spacings have become extremely narrow with increasingly higher densities of circuits used in the field of precision electronic devices in recent years, circuit-bonding methods for such circuits have been desired that have reliability equivalent or superior to conventional reliability.

With circuit bonding, incidentally, and particularly with bonding of circuit electrodes formed on flexible wiring boards to circuit electrodes formed on other circuit members, folding of the flexible wiring boards has posed the risk of cracking the circuits on the flexible board, thus causing wire breakage. Circuit-bonding methods have therefore been developed wherein, on a flexible board with circuit bonded sections that are bonded using an anisotropic conductive film for circuit connection, a circuit-protecting member (solder resist) is provided at the sections of circuit electrodes outside of the circuit-bonded sections to protect those sections, and during circuit bonding between circuit electrodes on the flexible board and circuit electrodes on a glass substrate with an anisotropic conductive film for circuit connection, the anisotropic conductive film for circuit connection is also attached to a part of the circuit-protecting member in addition to the circuit-bonded sections (see Patent document 1, for example). According to this circuit-bonding method, the circuit electrodes on the flexible board are protected by the circuit-protecting member and anisotropic conductive film for circuit connection, thus helping to prevent wire breakage of the circuit electrodes on the flexible board and producing high bonding strength between the circuit electrodes.

[Patent document 1] Japanese Unexamined Patent Publication No. 2002-358026

›DISCLOSURE OF THE INVENTION

Problems to be Solved by the Invention

In the conventional circuit-bonding method described above, however, the circuit-protecting member and anisotropic conductive film for circuit connection overlap during circuit bonding between the circuit electrodes on the flexible board and the circuit electrodes on the glass substrate with an anisotropic conductive film for circuit connection, and therefore the anisotropic conductive film for circuit connection present near the circuit-protecting member is not easily eliminated between the circuit electrodes that are adjacent to each other, and the connection resistance between the circuit electrodes that are electrically connected by the anisotropic conductive film for circuit connection is increased.

It is an object of the present invention to provide a circuit connecting method that can sufficiently reduce connection resistance between circuit electrodes that are electrically connected via an anisotropic conductive film for circuit connection, even when a part of the circuit-protecting member is bonded with the anisotropic conductive film for circuit connection in addition to the circuit-bonded sections of the circuit electrodes.

Means for Solving the Problems

The circuit connecting method of the invention comprises a step of preparing a first circuit member having first circuit electrodes formed on the main surface of a first board, a step of preparing a second circuit member having second circuit electrodes formed on the main surface of a second board, with an insulating layer provided on the sections of the second circuit electrodes other that the sections that are connected to the first circuit electrodes and a step of bonding the first circuit member and second circuit member via an anisotropic conductive film for circuit connection so that part of the anisotropic conductive film for circuit connection overlaps part of the insulating layer, for electrical connection between the first circuit electrodes and second circuit electrodes, wherein the thickness of the anisotropic conductive film for circuit connection is no greater than the total of the height of the first circuit electrodes and the height of the second circuit electrodes.

In the circuit connecting method of the invention, the first circuit member and second circuit member are bonded via the anisotropic conductive film for circuit connection, and the thickness of the anisotropic conductive film for circuit connection is no greater than the total of the height of the first circuit electrodes and the height of the second circuit electrodes. When the first circuit member and second circuit member are bonded, therefore, the part of the anisotropic conductive film for circuit connection between the first circuit electrodes and second circuit electrodes remain between the first circuit electrodes and second circuit electrodes only in the amount required to electrically connect and bond the first circuit electrodes and second circuit electrodes, while the rest is eliminated between the adjacent electrodes among the first circuit electrodes and the adjacent electrodes among the second circuit electrodes. As a result, even if the first circuit member and second circuit member are bonded via the anisotropic conductive film for circuit connection so that part of the anisotropic conductive film for circuit connection overlaps a part of the insulating layer, it is possible to sufficiently reduce the connection resistance between the first circuit electrodes and second circuit electrodes that are electrically connected via the anisotropic conductive film for circuit connection. If the thickness of the anisotropic conductive film for circuit connection is greater than the total of the height of the first circuit electrodes and the height of the second circuit electrodes, the part of the anisotropic conductive film for circuit connection between the first circuit electrodes and second circuit electrodes will not be easily eliminated between the adjacent electrodes among the first circuit electrodes and the adjacent electrodes among the second circuit electrodes.

Preferably, the thickness of the anisotropic conductive film for circuit connection is no greater than 70% of the total of the height of the first circuit electrodes and the height of the second circuit electrodes. This will further promote elimination of the part of the anisotropic conductive film for circuit connection between the first circuit electrodes and second circuit electrodes, for between the adjacent electrodes among the first circuit electrodes and the adjacent electrodes among the second circuit electrodes.

Preferably, the thickness of the anisotropic conductive film for circuit connection is at least 50% of the total of the height of the first circuit electrodes and the height of the second circuit electrodes. If the thickness of the anisotropic conductive film for circuit connection is less than 50% of the total of the height of the first circuit electrodes and the height of the second circuit electrodes, the anisotropic conductive film for circuit connection will not sufficiently fill between the adjacent electrodes among the first circuit electrodes and the adjacent electrodes among the second circuit electrodes, thus lowering the bonding strength between the first circuit member and second circuit member while also tending to reduce the electrical insulating property between the adjacent electrodes among the first circuit electrodes and the electrical insulating property between the adjacent electrodes among the second circuit electrodes.

Preferably, at least one of the first circuit member and second circuit member is flexible wiring boards.

Also preferably, the first board material is glass and the second circuit member is a flexible wiring board.

Effect of the Invention

According to the invention it is possible to provide a circuit connecting method that can sufficiently reduce connection resistance between circuit electrodes that are electrically connected via an anisotropic conductive film for circuit connection, even when a part of the circuit-protecting member is bonded with the anisotropic conductive film for circuit connection in addition to the circuit-bonded sections of the circuit electrodes.

›BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view of a liquid crystal display device.

FIG. 2 is a cross-sectional view of FIG. 1 along line II-II.

FIG. 3 is an illustration of a method for producing a liquid crystal display device.

FIG. 4 is a table showing the conditions, and connection resistance and insulation resistance values for Example 1-1 to 12-2 and Comparative Example 1-1 to 4-2.

›EXPLANATION OF SYMBOLS

10 : Liquid crystal display device, 12 : circuit member (first circuit member), 12 a : first board, 12 b : first circuit electrode, 14 : flexible wiring board (second circuit member), 14 a : second board, 14 b : second circuit electrode, 16 : anisotropic conductive film for circuit connection, 18 : solder resist (insulating layer).

›BEST MODE FOR CARRYING OUT THE INVENTION · 1 of 2

Preferred embodiments of the invention will now be explained with reference to the accompanying drawings. Throughout the explanation, identical or similarly functioning elements will be referred to by like reference numerals and will be explained only once.

(Construction of Liquid Crystal Display Device)

The construction of a liquid crystal display device 10 in which the circuit connecting method of the invention was applied will be explained first, with reference to FIG. 1 and FIG. 2 . The liquid crystal display device 10 comprises a circuit member (first circuit member) 12 , a flexible wiring board (second circuit member) 14 , and an anisotropic conductive film for circuit connection 16 .

The circuit member 12 comprises a glass substrate (first board) 12 a and circuit electrodes (first circuit electrodes) 12 b . The glass substrate 12 a , together with another glass substrate (not shown), sandwiches the liquid crystal layer to form a liquid crystal panel.

The circuit electrodes 12 b are a transparent electrode made of ITO (indium tin oxide), for example, and they are formed on the main surface of the glass substrate 12 a . The circuit electrodes 12 b have the function of applying a voltage to the liquid crystals in the liquid crystal layer to drive the liquid crystals. The height h 1 of the circuit electrodes 12 b may be about 0.05 μm-0.7 μm, for example.

The flexible wiring board 14 comprises a base (second board) 14 a and circuit electrodes (second circuit electrodes) 14 b . The base 14 a may be a polyimide film, for example. The circuit electrodes 14 b are composed of Cu with a Sn plating, for example, and they are formed on the main surface of the base 14 a.

On the flexible wiring board 14 , on the sections of the circuit electrodes 14 b other than the section that is connected to the circuit electrodes 12 b , there is provided a solder resist (insulating layer) 18 as a protecting member to protect the circuit electrodes 14 b . The height h 2 of the circuit electrodes 14 b may be about 5 μm-100 μm, for example.

The anisotropic conductive film for circuit connection 16 has conductive particles 16 b evenly dispersed in a thermosetting adhesive 16 a . The anisotropic conductive film for circuit connection 16 has anisotropic conductivity such that it exhibits conductivity in the thickness direction in which force is applied, but exhibits no conductivity in the in-plane direction. The anisotropic conductive film for circuit connection 16 may be any adhesive film containing conductive particles 16 b , without any particular restrictions, and using the thermosetting adhesive 16 a as mentioned above results in a more notable effect of the invention with higher temperature and shorter time for the circuit connection conditions.

The anisotropic conductive film for circuit connection 16 bonds the circuit member 12 and flexible wiring board 14 . Specifically, the anisotropic conductive film for circuit connection 16 is disposed between the circuit member 12 and part of the flexible wiring board 14 connected to the circuit member 12 and part of the solder resist 18 , with a part of the anisotropic conductive film for circuit connection 16 overlapping a part of the solder resist 18 .

As shown in detail in FIG. 2 , the section of the anisotropic conductive film for circuit connection 16 other than the section that is between the circuit electrodes 12 b and circuit electrodes 14 b fills the area between the adjacent electrodes among each of the circuit electrodes 12 b and the adjacent electrodes among each of the circuit electrodes 14 b , so that the circuit electrodes 12 b and circuit electrodes 14 b become electrically connected by the conductive particles 16 b.

(Method for Producing Liquid Crystal Display Device)

A method for producing the liquid crystal display device 10 will now be explained with reference to FIG. 3 .

First, a circuit member 12 (liquid crystal panel) having a circuit electrode 12 b formed on the main surface of a glass substrate 12 a is prepared. A flexible wiring board 14 is also prepared having circuit electrodes 14 b formed on the main surface of a base 14 a and having a solder resist 18 provided on the sections of the circuit electrodes 14 b other than the section that are connected to the circuit electrodes 12 b.

An anisotropic conductive film for circuit connection 16 is also prepared. The anisotropic conductive film for circuit connection 16 has a thickness h 3 before connection of the circuit member 12 and flexible wiring board 14 , which is no greater than the total of the height h 1 of the circuit electrodes 12 b and the height h 2 of the circuit electrodes 14 b , and it may be 5.05 μm-100.7 μm, for example.

The thickness h 3 of the anisotropic conductive film for circuit connection 16 is preferably no greater than 70% of the total of the height h 1 of the circuit electrodes 12 b and the height h 2 of the circuit electrodes 14 b . This will further promote elimination of the part of the anisotropic conductive film for circuit connection 16 between the first circuit electrodes 12 b and second circuit electrodes 14 b , for between the adjacent electrodes among each of the first circuit electrodes 12 b and the adjacent electrodes among each of the second circuit electrodes 14 b.

Also, the thickness h 3 of the anisotropic conductive film for circuit connection 16 is preferably at least 50% of the total of the height h 1 of the circuit electrodes 12 b and the height h 2 of the circuit electrodes 14 b . If the thickness h 3 of the anisotropic conductive film for circuit connection 16 is less than 50% of the total of the height h 1 of the first circuit electrodes 12 b and the height h 2 of the second circuit electrodes 14 b , the anisotropic conductive film for circuit connection 16 will not sufficiently fill between the adjacent electrodes among each of the first circuit electrodes 12 b and the adjacent electrodes among each of the second circuit electrodes 14 b , thus lowering the bonding strength between the first circuit member 12 b and second circuit member 14 b while also tending to reduce the electrical insulating property between the adjacent electrodes among each of the first circuit electrodes 12 b and the electrical insulating property between the adjacent electrodes among each of the second circuit electrodes 14 b.

›BEST MODE FOR CARRYING OUT THE INVENTION · 2 of 2

Next, the anisotropic conductive film for circuit connection 16 is disposed between the circuit member 12 and flexible wiring board 14 , and the anisotropic conductive film for circuit connection 16 is sandwiched by the circuit member 12 and flexible wiring board 14 so that part of the anisotropic conductive film for circuit connection 16 overlaps with part of the solder resist 18 . Specifically, the circuit member 12 and flexible wiring board 14 are bonded via the anisotropic conductive film for circuit connection 16 in this manner to complete the liquid crystal display device.

According to this embodiment, the circuit member 12 and flexible wiring board 14 are bonded via the anisotropic conductive film for circuit connection 16 , and the thickness h 3 of the anisotropic conductive film for circuit connection 16 is no greater than the total of the height h 1 of the circuit electrodes 12 b and the height h 2 of the circuit electrodes 14 b . Thus, when the circuit member 12 and flexible wiring board 14 are bonded, the part of the anisotropic conductive film for circuit connection 16 between the circuit electrodes 12 b and circuit electrodes 14 b remain between the circuit electrodes 12 b and circuit electrodes 14 b only in the amount required to electrically connect and bond the circuit electrodes 12 b and circuit electrodes 14 b , while the rest is eliminated between the adjacent electrodes among each of the circuit electrodes 12 b and the adjacent electrodes among each of the circuit electrodes 14 b . As a result, even if the circuit member 12 and flexible wiring board 14 are bonded via the anisotropic conductive film for circuit connection 16 so that part of the anisotropic conductive film for circuit connection 16 overlaps a part of the solder resist 18 , it is possible to sufficiently reduce the connection resistance between the circuit electrodes 12 b and circuit electrodes 14 b that are electrically connected via the anisotropic conductive film for circuit connection 16 .

The above detailed explanation of a preferred embodiment of the invention is not intended to restrict the scope of the invention to this particular embodiment. For example, the invention can also be applied to display devices other than liquid crystal display devices (such as plasma displays or organic EL displays).

Also, although the circuit member 12 (glass substrate 12 a ) and flexible wiring board 14 are bonded by the anisotropic conductive film for circuit connection 16 in this embodiment, two glass substrates may be bonded instead, or two flexible wiring boards may be bonded instead. Different circuit members other than these may also be bonded together.

›EXAMPLES

The present invention will now be explained in greater detail based on Examples 1-1 to 12-2 and Comparative Examples 1-1 to 4-2, with the understanding that these examples are in no way limitative on the invention.

›Examples24

›Example 1-1

First, a circuit member 12 was prepared having ITO circuit electrodes 12 b (film thickness: h 1 =50 nm, surface resistance: <20Ω) formed on the surface of a glass substrate 12 a (thickness: 1.1 mm). The line widths of the circuit electrodes 12 b were 25 μm and the pitch was 50 μm.

There was also prepared a flexible wiring board 14 having Sn-plated Cu foil circuit electrodes 14 b (thickness: h 2 =8 μm) formed on the surface of a polyimide film base 14 a (thickness: 38 μm). The line widths of the circuit electrodes 14 b were 18 μm and the pitch was 50 μm. Also, a solder resist 18 (“SN-9000” solder resist by Hitachi Chemical Co., Ltd.) was provided as a protecting member to protect the circuit electrodes 14 b , on the sections of the circuit electrodes 14 b other than the sections that are connected to the circuit electrodes 12 b . The thickness of the solder resist 18 was 30 μm and the width was 10 mm.

There was additionally prepared an anisotropic conductive film for circuit connection 16 with a thickness h 3 of 8 μm (“ANISOLM: AC-7206U-8” anisotropic conductive film by Hitachi Chemical Co., Ltd.).

The circuit member 12 and flexible wiring board 14 were positioned at a circuit bonding width of 1.5 mm and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 15 seconds to obtain a liquid crystal display device 10 for Example 1-1. The anisotropic conductive film for circuit connection 16 and solder resist 18 had an overlap of 0.5 mm.

›Example 1-2

A liquid crystal display device 10 for Example 1-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 15 seconds.

›Example 2-1

A liquid crystal display device 10 for Example 2-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 6 μm (“ANISOLM: AC-7206U-6” anisotropic conductive film by Hitachi Chemical Co., Ltd.).

›Example 2-2

A liquid crystal display device 10 for Example 2-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 6 μm (“ANISOLM: AC-7206U-6” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 15 seconds.

›Example 3-1

A liquid crystal display device 10 for Example 3-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 8 μm (“ANISOLM: AC-11000Y-8” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 5 seconds.

›Example 3-2

A liquid crystal display device 10 for Example 3-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 8 μm (“ANISOLM: AC-11000Y-8” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 5 seconds.

›Example 4-1

A liquid crystal display device 10 for Example 4-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 6 μm (“ANISOLM: AC-11000Y-6” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 5 seconds.

›Example 4-2

A liquid crystal display device 10 for Example 4-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 6 μm (“ANISOLM: AC-11000Y-6” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 5 seconds.

›Example 5-1

There was also prepared a flexible wiring board 14 having Sn-plated Cu foil circuit electrodes 14 b (thickness: h 2 =12 μm) formed on the surface of a polyimide film base 14 a (thickness: 38 μm). The line widths of the circuit electrodes 14 b were 18 μm and the pitch was 50 μm. Also, a solder resist 18 (“SN-9000” solder resist by Hitachi Chemical Co., Ltd.) was provided as a protecting member to protect the circuit electrodes 14 b , on the sections of the circuit electrodes 14 b other than the sections that are connected to the circuit electrodes 12 b . The thickness of the solder resist 18 was 30 μm and the width was 10 mm.

There was additionally prepared an anisotropic conductive film for circuit connection 16 with a thickness h 3 of 12 μm (“ANISOLM: AC-7206U-12” anisotropic conductive film by Hitachi Chemical Co., Ltd.).

The circuit member 12 and flexible wiring board 14 were positioned at a circuit bonding width of 1.5 mm and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 15 seconds to obtain a liquid crystal display device 10 for Example 5-1. The anisotropic conductive film for circuit connection 16 and solder resist 18 had an overlap of 0.5 mm.

›Example 5-2

A liquid crystal display device 10 for Example 5-2 was obtained in the same manner as Example 5-1, except that the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 15 seconds.

›Example 6-1

A liquid crystal display device 10 for Example 6-1 was obtained in the same manner as Example 5-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 8 μm (“ANISOLM: AC-7206U-8” anisotropic conductive film by Hitachi Chemical Co., Ltd.).

›Example 6-2

A liquid crystal display device 10 for Example 6-2 was obtained in the same manner as Example 5-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 8 μm (“ANISOLM: AC-7206U-8” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 15 seconds.

›Example 7-1

A liquid crystal display device 10 for Example 7-1 was obtained in the same manner as Example 5-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 12 μm (“ANISOLM: AC-11000Y-12” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 5 seconds.

›Example 7-2

A liquid crystal display device 10 for Example 7-2 was obtained in the same manner as Example 5-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 12 μm (“ANISOLM: AC-11000Y-12” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 5 seconds.

›Example 8-1

A liquid crystal display device 10 for Example 8-1 was obtained in the same manner as Example 5-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 8 μm (“ANISOLM: AC-11000Y-8” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 5 seconds.

›Example 8-2

A liquid crystal display device 10 for Example 8-2 was obtained in the same manner as Example 5-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 8 μm (“ANISOLM: AC-11000Y-8” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 5 seconds.

›Example 9-1

A liquid crystal display device 10 for Example 9-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 3 μm (“ANISOLM: AC-7206U-3” anisotropic conductive film by Hitachi Chemical Co., Ltd.).

›Example 9-2

A liquid crystal display device 10 for Example 9-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 3 μm (“ANISOLM: AC-7206U-3” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 15 seconds.

›Example 10-1

A liquid crystal display device 10 for Example 10-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 3 μm (“ANISOLM: AC-11000Y-3” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 5 seconds.

›Example 10-2

A liquid crystal display device 10 for Example 10-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 3 μm (“ANISOLM: AC-11000Y-3” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 5 seconds.

›Example 11-1

A liquid crystal display device 10 for Example 11-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 4 μm (“ANISOLM: AC-7206U-4” anisotropic conductive film by Hitachi Chemical Co., Ltd.).

›Example 11-2

A liquid crystal display device 10 for Example 11-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 4 μm (“ANISOLM: AC-7206U-4” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 15 seconds.

›Example 12-1

A liquid crystal display device 10 for Example 12-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 4 μm (“ANISOLM: AC-11000Y-14” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 5 seconds.

›Example 12-2

A liquid crystal display device 10 for Example 12-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 14 μm (“ANISOLM: AC-11000Y-14” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 5 seconds.

Comparative Example 1-1

A liquid crystal display device for Comparative Example 1-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 12 μm (“ANISOLM: AC-7206U-12” anisotropic conductive film by Hitachi Chemical Co., Ltd.).

Comparative Example 1-2

A liquid crystal display device for Comparative Example 1-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 12 μm (“ANISOLM: AC-7206U-12” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 15 seconds.

Comparative Example 2-1

A liquid crystal display device for Comparative Example 2-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 12 μm (“ANISOLM: AC-11000Y-12” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 5 seconds.

Comparative Example 2-2

A liquid crystal display device for Comparative Example 2-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 12 μm (“ANISOLM: AC-11000Y-12” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 5 seconds.

Comparative Example 3-1

A liquid crystal display device for Comparative Example 3-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 14 μm (“ANISOLM: AC-7206U-14” anisotropic conductive film by Hitachi Chemical Co., Ltd.).

Comparative Example 3-2

A liquid crystal display device for Comparative Example 3-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 14 μm (“ANISOLM: AC-7206U-14” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 15 seconds.

Comparative Example 4-1

A liquid crystal display device for Comparative Example 4-1 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 4 μm (“ANISOLM: AC-11000Y-4” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 180° C., 3 MPa for 5 seconds.

Comparative Example 4-2

A liquid crystal display device for Comparative Example 4-2 was obtained in the same manner as Example 1-1, except that the anisotropic conductive film for circuit connection 16 had a thickness h 3 of 4 μm (“ANISOLM: AC-11000Y-4” anisotropic conductive film by Hitachi Chemical Co., Ltd.), and the anisotropic conductive film for circuit connection 16 was sandwiched by the circuit member 12 and flexible wiring board 14 and hot pressed at 210° C., 3 MPa for 5 seconds.

(Measurement of Connection Resistance Value)

For the liquid crystal display device 10 of each of Examples 1-1 to 12-2 and the liquid crystal display device of each of Comparative Examples 1-1 to 4-2, obtained as described above, the connection resistance value between the circuit electrodes 12 b and 14 b was measured using a Digital Multimeter. The results of the connection resistance measurement are shown in FIG. 4 .

(Measurement of Insulation Resistance Between Adjacent Circuits)

For the liquid crystal display device 10 of each of Examples 1-1 to 12-2 and the liquid crystal display device of each of Comparative Examples 1-1 to 4-2, obtained as described above, the insulation resistance between adjacent electrodes among the circuit electrodes 12 b and between adjacent electrodes among the circuit electrodes 14 b were measured with an insulation resistance meter 500 hours after high-temperature, high-humidity test treatment at 85° C./85% RH. The results of the insulation resistance measurement are shown in FIG. 4 .

(Evaluation Results)

In Examples 1-1 to 4-2, the connection resistance values were all 30±2Ω and the insulation resistance values were all 10 8 Ω or greater. In Examples 5-1 to 8-2, the connection resistance values were all no greater than 30Ω and the insulation resistance values were all 10 8 Ω or greater. In Examples 9-1 and 9-2, the connection resistance values were both 30±2Ω and the insulation resistance values were both on the order of 10 5 Ω. In Examples 10-1 to 12-2, the connection resistance values were all no greater than 30Ω and the insulation resistance values were all on the order of 10 4 -10 5 Ω.

In Comparative Examples 1-1 to 4-2, however, the connection resistance values were all no less than 10 8 Ω while the insulation resistance values were all 35Ω or greater.

With the liquid crystal display devices 10 of Examples 1-1 to 8-2, the connection resistance between the circuit electrodes 12 b and 14 b was sufficiently low and the insulation resistance between adjacent electrodes among the circuit electrodes 12 b and between adjacent electrodes among the circuit electrodes 14 b was sufficiently high, even 500 hours after the high-temperature, high-humidity test treatment, thus confirming that long-term reliability was assured. With the liquid crystal display devices 10 of Examples 9-1 to 12-2, the connection resistance between the circuit electrodes 12 b and 14 b was sufficiently low, but the insulation resistance between adjacent electrodes among the circuit electrodes 12 b and between adjacent electrodes among the circuit electrodes 14 b was too low 500 hours after the high-temperature, high-humidity test treatment, thus confirming that the long-term reliability was inferior.

1 of 33 part labels are ours — the grant heads the rest

Claims as granted

12 claims

Classifications

4 codes

IPC · International Patent Classification

Section H — Electricity

H05K3/30

USPC · US Patent Classification

29/83229/83029/840

Claim changes

Soon

Coming soonHow the claims changed between publication and grant

See which claims were amended, added or cancelled during examination, with every added and removed word marked.

AmendedAddedCancelledUnchanged

The published claims of this application are not paired with the granted ones in what we hold.

File wrapper

⤢ drag to zoom

USPTOApplicanthover for detail · click to open

Pendency

4.1 y

1,497 days filing → grant

Office actions

non-final + final

Responses

no RCE

Examiner

Carl Arbes

art unit 3729 · TC 3700

Law firm

Law firm · Log in to unlock

Citations: 25 back · 1 forward

See the full prosecution history — every USPTO and applicant action on this file, in order.

Documents

Log in to open the documents of this file: the application as filed, every office action and response, the notice of allowance.

Chain of title

⤢ drag to zoom

Titlehover for detail · click to open

See the full assignment history — every owner this patent has passed through, with recordation dates and reel/frame numbers.