Method of plating and method of manufacturing a micro device
Granted 21 Dec 2010 · 1 office action
Assignee: TDK Corporation
Law firm: Law firm · Log in to unlock
Attorney: Attorney · Log in to unlock
Inventors: Akifumi Kamijima, Shingo Miyata, Souhei Horiuchi, Masahiro Saito +2 · Examiner: Nam X Nguyen · AU 1795 · TC 1700
Life of the application
8 dated eventsAbstract
A method of plating, which allows compositions of plating patterns of a plurality of layers to be uniform without any operational complexity, is provided. The area of the plating layer electrodeposited including plating patterns is constant in each of the plurality of layers. Accordingly, a value of plating-current density is easily maintained constant without any special operation. Consequently, the plating patterns in each of the plurality of layers is easily formed to have an uniform composition.
Description
9 parts›BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method of plating suitable for forming plating patterns of a plurality of layers, and relates to a method of manufacturing a micro device suitable for manufacturing one that includes the plating patterns of the plurality of layers.
2. Description of the Related Art
In producing various sorts of electronic circuit boards and semiconductor device substrates, plating patterns, which are formed in the shape of plurality of layers and having the same composition with each other, may be formed on a limited portion of the substrate (object to be plated). When configurations (occupation area) of the plating patterns of the plurality of layers differ mutually, plating-current density needs to be adjusted in each of the plurality of layers in the plating in spite of using a plating bath of the same component. For example, the plating-current density is adjusted by controlling electrode area as shown in Japanese Laid-Open Patent Publication (Kokai) No. H11-1799, and Japanese Laid-Open Patent Publication (Kokai) No. H2-228493.
›SUMMARY OF THE INVENTION
However, operation is very complicated if every formation of the plating patterns needs adjustment of the plating-current density in each of the plurality of layers. Moreover, in spite of using a plating bath of the uniform component, compositions of the formed plating patterns tend to be quite different from each other in each layer. Since such composition difference affects the property value of the plating pattern itself, such as magnetic property, it is expected to be minimized to a maximum extent.
The present invention has been devised in view of the above problem, and it is desirable to provide a method of plating, which allows the compositions of the plating patterns of a plurality of layers to be uniformed enough in each of the plurality of layers without any operational complexity. It is also desirable to provide a method of manufacturing a micro device that includes the plating patterns of a plurality of layers so that the compositions of the plating patterns may be uniformed enough in each of the plurality of layers without any operational complexity.
A method of plating and a method of manufacturing a micro device includes a step of forming a plating layer including the plating pattern in each of plurality of layers so that an area of the plating layer electrodeposited is constant in each of the plurality of layers. Here, “the plating layer including the plating pattern” means that the plating layer includes not only the aimed plating pattern but also other portions.
According to the method of plating and manufacturing the micro device of the present invention, the area of the plating layer electrodeposited is constant in each of the plurality of layers. As a result, plating-current density can be kept constant without any adjustment of plating current or electrode area.
Preferably, the method of plating and the method of manufacturing the micro device includes steps of: forming a plating foundation layer in each of the plurality of layers, forming a resist frame and an auxiliary resist pattern on the plating foundation layer in each of the plurality of layers, forming the plating layer selectively on the plating foundation layer other than portions covered with the resist frame and the auxiliary resist pattern in each of the plurality of layers, removing the resist frame and the auxiliary resist pattern in each of the plurality of layers, and removing the plating layer other than the plating pattern surrounded by the resist frame in each of the plurality of layers, and sum total of the area of the resist frame and the auxiliary resist patterns in each of the plurality of layers is constant. Preferably, at least one of geometry and the area of the plating pattern differs between the plurality of layers. Preferably, in the formation process for each of the plurality of layers, a common plating bath is used for forming the plating layer in each of the plurality of layers. Further, it is desirable to form a plurality of the auxiliary resist patterns symmetrically with respect to the resist frame. Further, preferably, the resist frame and the auxiliary resist pattern are formed to have a line width equal to each other. The line width here means a width of, a cross section orthogonal to a longitudinally-extending direction (longitudinal direction) of each of the resist frame and the auxiliary resist pattern.
According to the method of plating or method of manufacturing the micro device of the present invention, since the area of the plating layer electrodeposited, including the plating pattern, is made constant in each of the plurality of layers, the plating patterns, each having a composition uniformed enough in each of the plurality of layers, can be formed more easily, without changing any plating condition.
Other and further objects, features and advantages of the invention will appear more fully from the following description.
›BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a schematic sectional view showing a whole configuration of a plating device used for formation method of a layered film according to a first embodiment of the present invention.
FIG. 2A is a plan view and FIG. 2B is a partially enlarged view, each showing a configuration of a substrate appearing in FIG. 1 .
FIG. 3 is a sectional view showing a cross-sectional configuration of the layered film formed using the plating device appearing in FIG. 1 .
FIGS. 4A to 4C are plan views showing a configuration of each plating pattern in the layered film shown in FIG. 3 .
FIG. 5 is a sectional view showing one production process of the layered film shown in FIG. 3 using the plating device appearing in FIG. 1 .
FIG. 6 is a sectional view showing another production process subsequent to FIG. 5 .
FIG. 7 is a sectional view showing another production process subsequent to FIG. 6 .
FIG. 8 is a sectional view showing another production process subsequent to FIG. 7 .
FIGS. 9A to 9C are plan views of a resist pattern shown in FIG. 8 .
FIG. 10 is a sectional view showing another production process subsequent to FIG. 8 .
FIG. 11 is a sectional view showing another production process subsequent to FIG. 10 .
FIG. 12 is a sectional view showing another production process subsequent to FIG. 11 .
FIG. 13 is a sectional view showing another production process subsequent to FIG. 12 .
FIG. 14 is a sectional view showing another production process subsequent to FIG. 13 .
FIG. 15 is a sectional view showing another production process subsequent to FIG. 14 .
FIGS. 16A to 16C show a first modification with regard to a plan view configuration of the resist pattern shown in FIG. 9 .
FIGS. 17A to 17C show a second modification with regard to the plan view configuration of the resist pattern shown in FIG. 9 .
FIGS. 18A to 18C show a third modification with regard to the plan view configuration of the resist pattern shown in FIG. 9 .
FIGS. 19A to 19C show a fourth modification with regard to the plan view configuration of the resist pattern shown in FIG. 9 .
FIGS. 20A to 20C show a fifth modification with regard to the plan view configuration of the resist pattern shown in FIG. 9 .
FIG. 21 is an exploded perspective view showing a configuration of a thin film magnetic head, which is formed by a method of manufacturing the same according to a second embodiment of the present invention.
FIG. 22 is a sectional view showing a configuration taken along the line XXI-XXI of the thin film magnetic head shown in FIG. 21 , which is seen from the direction indicated by arrows.
FIG. 23 is a plan view showing one production process in the method of manufacturing the thin film magnetic head shown in FIG. 21 .
FIG. 24 is a plan view showing another production process subsequent to FIG. 23 .
FIG. 25 is a sectional view showing another production process subsequent to FIG. 24 .
FIG. 26 is a plan view showing another production process subsequent to FIG. 25 .
FIG. 27 is a sixth modification with regard to the plan view configuration of the resist pattern shown in FIG. 9 .
›DESCRIPTION OF THE PREFERRED EMBODIMENTS · 1 of 6
Embodiments of the invention will be described in detail hereinbelow with reference to the drawings.
First Embodiment
First, a plating device for implementing a formation method of a layered film as a first embodiment of the present invention, and an electrode assembly arranged therein will be described hereinbelow with reference to FIGS. 1 to 4 .
FIG. 1 is a schematic sectional view showing a configuration of the plating device. The plating device forms a plating layer on a surface 11 S (surface to be plated) of a substrate 11 , which is an object to be plated, and includes a plating liquid vessel 30 which contains a plating bath 31 , and a cathode electrode assembly 10 and an anode electrode assembly 20 disposed in the plating liquid vessel 30 , so as to be opposed to each other via the plating bath 31 . The cathode electrode assembly 10 is attached firmly to a bottom 32 of the plating liquid vessel 30 so that the plating bath 31 may not leak. The cathode electrode assembly 10 has an aperture 10 K, and the substrate 11 in the shape of a thin plate is disposed therein to cover the aperture 10 K. The substrate 11 is supported by a supporting body 50 which includes a stage 51 and a cylinder 52 so that the surface 11 S is in contact with the plating bath 31 . The plating bath 31 has a composition in accordance with a sort of plating layer to be obtained. The plating device further has a power unit 70 . The power unit 70 is electrically connected with the cathode electrode assembly 10 and the anode electrode assembly 20 by lead wires 71 and 72 respectively to apply direct current voltage between the electrodes. Although the power unit 70 of a type that applies direct current voltage is illustrated herein, it is not limited to this but what applies alternating voltage or pulse voltage can be used.
The anode electrode assembly 20 includes an anode 21 , an anode cylinder 22 having the anode 21 attached to one end thereof, and a supporter 23 for fixing the other end of the anode cylinder 22 to an upper portion 33 of the plating liquid vessel 30 . The anode 21 is arranged so as to face with the surface 11 S via the plating bath 31 , and is connected with the power unit 70 by the lead wire 72 passing through the anode cylinder 22 and the supporter 23 .
In this plating device, a plating seed layer covers the surface 11 S of the previously-formed substrate 11 to form the plating layer on the substrate, by applying direct current voltage between the cathode electrode assembly 10 and the anode electrode assembly 20 using the power unit 70 , when the plating liquid vessel 30 is filled with the plating bath 31 as shown in FIG. 1 .
Subsequently, the formation method of the layered film using this plating device will be explained with reference to FIGS. 2 to 15 .
Here, a case where layered film 1 (which will be described later) are formed on each of a plurality of element fields R 1 one-by-one on the substrate 11 as schematically shown in FIGS. 2A and 2B , is explained for example.
FIG. 2A illustrates a whole configuration of the substrate 11 . In FIG. 2A , each rectangular area R 3 , which is defined by dividing the substrate 11 into matrix, is equal to a range to be exposed by one operation of a stepper and so on (that is, an exposure region which can be exposed in one shot of the stepper), for example. FIG. 2B is an enlarged view of any one of the rectangular areas R 3 . The rectangular area R 3 includes a plurality of unit fields R 4 of a rectangular shape, that are defined by plurality of scribe lines L 1 and L 2 . Each unit field R 4 includes an element field R 1 and a gap field R 2 surrounding the element field R 1 . With such arrangement, the element fields R 1 are arranged in matrix and equally spaced at specified intervals.
As shown in FIG. 3 , the layered film 1 are formed by layering in order a first layer L 1 that includes a plating pattern M 1 , a second layer L 2 that includes a plating pattern M 2 , and a third layer L 3 that includes a plating pattern M 3 . Peripheries of the plating patterns M 1 to M 3 are surrounded by insulating layers Z 1 to Z 3 , respectively. The surfaces of the plating pattern M 1 and the insulating layer Z 1 form a coplanar face, the surfaces of the plating pattern M 2 and the insulating layer Z 2 form a coplanar face F 2 , and the surfaces of the plating pattern M 3 and the insulating layer Z 3 form a coplanar face F 3 . As shown in FIGS. 4A to 4C for example, the plating patterns M 1 to M 3 are all rectangular in plan view, but have different dimensions from each other. Namely, occupation areas of the plating patterns M 1 to M 3 are different from each other. However, they all have a similar composition. FIG. 3 is a sectional view showing a layered structure of the layered film 1 , and FIGS. 4A to 4C are plan views showing configurations of the plating patterns M 1 to M 3 in plan view. Namely, FIG. 3 corresponds to cross sections taking along the lines III-III of FIGS. 4A to 4C .
Formation process of the plating pattern M 1 is as follows. As first shown in FIG. 5 , the substrate 11 is prepared as an object to be plated 4 . Then, as shown in FIG. 6 , a plating foundation layer 12 is formed to completely cover the surface 11 S of the substrate 11 . The plating foundation layer 12 is formed with component materials such as nickel iron alloy (NiFe) by vacuum deposition method such as sputtering, for example.
Subsequently, after forming a photoresist layer 13 Z so as to cover a surface of the plating foundation layer 12 completely, a photoresist pattern 13 A is formed using photolithographic technique, as shown in FIG. 7 . Specifically, first, a latent image portion 13 K is formed by selectively exposing the photoresist layer 13 Z via a photo mask 14 which has an aperture 14 K of a specified shape. Subsequently, after performing heat-treatment as necessary, it is developed by dissolving and removing the latent image portion 13 K using a specified developer, and further, is washed and dried. In this manner, the photoresist pattern 13 A of a specified shape is completed.
›DESCRIPTION OF THE PREFERRED EMBODIMENTS · 2 of 6
As shown in FIG. 9 (A), photoresist patterns 13 B to 13 G, as an auxiliary pattern, are formed together with the formation of the photoresist pattern 13 A. FIG. 9A is plan view showing a planar configuration and layout of the photoresist patterns 13 A to 13 G (hereinafter generically called photoresist pattern 13 ). Namely, FIG. 8 corresponds to a cross section taking along the line VIII-VIII of FIG. 9A , seen from the direction indicated by an arrow. The photoresist pattern 13 A is disposed so as to surround a portion R 13 A in which the plating pattern M 1 will be formed (hereinafter called formation portion) Meanwhile, it is preferred that the other photoresist patterns 13 B to 13 G are disposed symmetrically with respect to the photoresist pattern 13 A so that the photoresist pattern 13 A may be centered. In this case, it is desirable that geometries and dimensions of each pair of the mutually-symmetrically disposed photoresist patterns of the photoresist patterns 13 B to 13 G are equal to each other, and a part of the photoresist patterns 13 B to 13 G is W 1 , which is equal to a part of the width of the photoresist pattern 13 A. Here, it is defined that an auxiliary portion R 13 B is an area excluding the portions occupied by the photoresist pattern 13 and the formation portion R 13 A from the unit field R 4 . Accordingly, sum total of the formation portion R 13 A and the auxiliary portion R 13 B are taken as an area to be plated, denoted by a plating portion R 13 .
After forming the photoresist pattern 13 , plating is processed using the aforementioned plating device, and as shown in FIG. 10 , a plating layer 15 made of NiFe is formed. The plating layer 15 is formed so as to occupy the plating portion R 13 shown in FIG. 9A . At this time, the photoresist pattern 13 A works as a photoresist frame defining the outline of the plating pattern M 1 , which will be obtained eventually.
After the formation of the plating layer 15 , the plating foundation layer 12 is partially exposed by removing the photoresist pattern 13 using an organic solvent as shown in FIG. 11 . Further, an exposed portion R 12 of the plating foundation layer 12 is removed by milling or the like, using the plating layer 15 as an etching mask. In this manner, as shown in FIG. 12 , the surface 11 S of the substrate 11 is partially exposed.
Subsequently, after selectively forming a photoresist pattern 16 so as to cover the formation portion R 13 and the exposed surface 11 S as shown in FIG. 13 , the plating layer 15 that is not covered by the photoresist pattern 16 is removed by wet etching as shown in FIG. 14 . Finally, as shown in FIG. 15 , the plating pattern M 1 , which is formed on the formation portion R 13 constituted by the plating layer 15 and the plating foundation layer 12 A, appears by removing the photoresist pattern 16 with an organic solvent or the like.
Formation process of each plating patterns M 1 -M 3 is substantially the same. Namely, the process of forming the plating pattern M 2 on the plating pattern M 1 is as follows. First, an electrical insulating material such as aluminium oxide (Al 2 O 3 ) is formed in the state of FIG. 15 so that the periphery of the plating pattern M 1 may be fully filled up, for example. Subsequently, flattening is performed until a surface of the plating pattern M 1 is exposed so that the coplanar face F 1 that is formed by the plating pattern M 1 and the insulating layer Z 1 is obtained. After this, the plating pattern M 2 is formed by repeating each formation process of FIGS. 6 to 15 . Similarly, the plating pattern M 3 is layered on the coplanar face F 2 formed by the plating pattern M 2 and the insulating layer Z 2 , thereby completing the layered film 1 shown in FIG. 3 .
In forming each of the plating patterns M 1 to M 3 , one or more photoresist patterns are formed so that a total occupation area of each of the plating patterns may be equal to each other, and plating process is selectively performed using the same plating bath 31 . More specifically, in forming the plating pattern M 2 , photoresist patterns 17 B to 17 G are formed as an auxiliary pattern, together with the formation of a photoresist pattern 17 A, as shown in FIG. 9B . The photoresist pattern 17 A is disposed so as to surround a portion R 17 A in which the plating pattern M 2 will be formed (hereinafter called as formation portion R 17 A), and works as a photoresist frame defining the outline of the plating pattern M 2 . FIG. 9B is a plan view showing a configuration of the photoresist patterns 17 A to 17 G (hereinafter generically called photoresist pattern 17 ) in plan view. Herein, sum total of the occupation areas of the photoresist pattern 17 is made equal to that of the photoresist pattern 13 . In other words, the occupation area of a plating portion R 17 , which is sum total of the formation portion R 17 A and an auxiliary portion R 17 B, is made equal to the occupation area of the plating portion R 13 .
Also, the plating pattern M 3 is formed in a similar way. As shown in FIG. 9C , photoresist patterns 18 B and 18 C as an auxiliary pattern are formed together with a photoresist pattern 18 A as a photoresist frame. The photoresist pattern 18 A is disposed so as to surround a portion (formation portion) R 18 A in which the plating pattern M 3 will be formed, and works as a photoresist frame defining the outline of the plating pattern M 3 . FIG. 9C is a plan view showing a configuration of the photoresist patterns 18 A to 18 C (hereinafter generically called photoresist pattern 18 ) in plan view. Herein, sum total of the occupation areas of the photoresist pattern 18 is made equal to that of the photoresist pattern 13 , and that of the photoresist pattern 17 , respectively. Namely, the occupation area of a plating portion R 18 , which is sum total of the formation portion R 18 A and an auxiliary portion R 18 B, is made equal to the occupation area of the plating portion R 13 , and the occupation area of the plating portion R 17 , respectively.
›DESCRIPTION OF THE PREFERRED EMBODIMENTS · 3 of 6
As described above, in the present embodiment, since the sum total of the occupation areas of the photoresist pattern 13 , the sum total of the occupation areas of the photoresist pattern 17 , and the sum total of the occupation areas of the photoresist pattern 18 are all equal to each other, an area of each of the plating portions R 13 , R 17 and R 18 , used for the plating process of the plating patterns M 1 to M 3 , that is, an electrodeposition area, is always made equal to each other. Accordingly, plating-current density can be easily kept constant without changing a current value. As a result, the plating patterns M 1 -M 3 of an almost identical composition can be formed quite efficiently. In particular, difference in composition can be suppressed substantially when the auxiliary patterns such as the photoresist patterns 13 B to 13 G are arranged evenly around the photoresist frame such as the photoresist pattern 13 A.
<Modification>
Layout of the photoresist patterns 13 , 17 and 18 are not limited to those shown in FIGS. 9A to 9C , and various modifications are available. Hereafter, some modifications of the present embodiment are shown.
A first modification shown in FIGS. 16A to 16C is that the photoresist patterns 13 and 17 are respectively formed on the basis of the photoresist pattern 18 A, which defines the outline of the largest plating pattern M 3 so that sum totals of the occupation areas of the photoresist patterns 13 and 17 may be equal to the occupation area of the photoresist pattern 18 A, respectively. Namely, in forming the plating pattern M 3 , only the photoresist pattern 18 A working as a photoresist frame is formed, and formation of the other portions corresponding to the photoresist patterns 18 B and 18 C shown in FIG. 9C is omitted. On the other hand, in the cases of FIGS. 16A and 16B , four photoresist patterns 13 B to 13 E (or 17 B to 17 E) are formed as an auxiliary pattern. Here, the photoresist patterns 13 B to 13 E are all identical in shape and dimension, and are arranged symmetrically with respect to the central photoresist-pattern 13 A as shown in FIG. 16A . Similarly, the photoresist patterns 17 B to 17 E are all identical in shape and dimension, and are arranged symmetrically with respect to the central photoresist-pattern 17 A as shown in FIG. 16B .
In a second modification shown in FIGS. 17A to 17C , the auxiliary pattern is provided in the gap field R 2 instead of the element field R 1 . Also in this case, the occupation area of the photoresist pattern 18 A is equal to sum total of the photoresist patterns 13 A to 13 E, and that of the photoresist patterns 17 A to 17 E, respectively.
Similarly, in a third modification thereof shown in FIGS. 18A to 18C , the auxiliary pattern is provided in the gap field R 2 . Also in this case, sum total of the occupation areas of the photoresist patterns 13 A to 13 K, that of the photoresist patterns 17 A to 17 G, and that of the photoresist patterns 18 A to 18 C, are all equal to each other.
In a fourth modification shown in FIGS. 19A to 19C and a fifth modification shown in FIG. 20A to 20C , the auxiliary pattern is provided in both of the element field R 1 and the gap field R 2 . Also in these cases, sum total of the occupation areas of the photoresist pattern 13 , that of the photoresist pattern 17 , and that of the photoresist pattern 18 , are all equal to each other.
Second Embodiment
Subsequently, a thin film magnetic head and method of manufacturing the same will be described with reference to FIGS. 21 to 26 , according to a second embodiment of the present invention.
The thin film magnetic head of the second embodiment includes a plurality of plating patterns such as a lower shielding layer and an upper shielding layer, respectively formed in layers different from each other. First, a schematic configuration of the thin film magnetic head is explained hereinbelow, and detailed description of the shielding layers will be given later.
FIG. 21 is an exploded perspective view showing a configuration of a thin film magnetic head 110 formed on one side of a slider in a magnetic head device. FIG. 22 is a sectional view showing a configuration taken along the line XXI-XXI of FIG. 21 , seen from the direction indicated by the arrow. As shown in FIGS. 21 and 22 , the thin film magnetic head 110 is formed by layering a read head portion 110 A and a write head portion 110 B in order from a side close to a substrate 100 of the slider. The write head portion 110 B writes magnetic information on a magnetic recording medium, and the read head portion 110 A reproduces the magnetic information written on the magnetic recording medium.
As shown in FIGS. 21 and 22 , the read head portion 110 A is configured in such a manner that, on a side exposed to an air bearing surface (hereinafter called ABS) 100 F, a lower shielding layer 111 , a lower gap layer 112 , a magnetoresistive (hereinafter called MR) element 110 C, an upper gap layer 120 and an upper shielding layer 121 are layered in order on the substrate 100 , for example.
The MR element 110 C includes a magnetoresistive film pattern (hereinafter called MR film pattern) 114 , a pair of magnetic domain controlling layers 115 L and 115 R extending on the both sides of the MR film pattern 114 , and a pair of conductive lead layers 116 L and 116 R formed on the pairs of magnetic domain controlling layers 115 L and 115 respectively. The MR film pattern 114 has a spin valve structure, which is typically configured in such a manner that a foundation layer, a pinning layer, a pinned layer, a non-magnetic layer, a free layer and a cap layer and so on are layered in order on the lower gap layer 112 . The MR film pattern 114 functions as a sensor for reading the information written on the magnetic recording medium. The pair of magnetic domain controlling layers 115 L and 115 R and the pair of conductive lead layers 116 L and 116 R are arranged so that they may be opposed to each other on both sides of the MR film pattern 114 along a direction corresponding to a direction of a write track width of the magnetic recording medium (that is, X-direction). The magnetic domain controlling layers 115 L and 115 R, which are typically formed by a hard magnetic material containing a cobalt platinum alloy (CoPt) or the like, arrange magnetic domain directions of free layers included in the MR film pattern 114 into a single domain so as to suppress generation of a Barkhausen noise. The conductive lead layers 116 L and 116 R, which are typically made of copper (Cu) or the like, work as a current path sending a sensing current to the MR film pattern 114 in a direction orthogonal to the layered direction (that is, X-direction), and, as shown in FIG. 21 , are connected to electrodes 116 LP and 116 RP, respectively.
›DESCRIPTION OF THE PREFERRED EMBODIMENTS · 4 of 6
The lower shielding layer 111 is typically made of a magnetic material such as a nickel iron alloy (NiFe), and works so that the MR film pattern 114 may not be affected by unnecessary magnetic field. The lower gap layer 112 is made of an electrical insulating material such as aluminium oxide (Al 2 O 3 ) and aluminum nitride (AlN), and is intended for electrical insulation between the lower shielding layer 111 and the MR film pattern 114 . Upper gap layer 120 is also made of an electrical insulating material as with the lower gap layer 112 , and is intended for electrical insulation between the upper shielding layer 121 and the MR film patterns 114 . The upper shielding layer 121 is made of a magnetic material such as a nickel iron alloy (NiFe) as with the lower shielding layer 111 , and works so that the MR film pattern 114 may not be affected by unnecessary magnetic field. The upper shielding layer 121 also works as a lower magnetic pole in the write head portion 110 B. It is to be noted that another lower magnetic pole may be provided separately from the upper shielding layer 121 .
In the read head portion 110 A configured in this manner, a magnetization direction of the free layer of the MR film pattern 114 changes in accordance with a signal magnetic field applied from the magnetic recording medium. Accordingly, a magnetization direction of the pinned layer included in the MR film pattern 114 changes relatively. In this case, variation of magnetization directions is expressed by variation of electric resistance by sending the sensing current to the MR film pattern 114 via the pair of conductive lead layers 116 L and 116 R. With this, the signal magnetic field is detected to read magnetic information.
The write head portion 110 B includes the upper shielding layer 121 , a write gap layer 141 , a pole chip 142 , a coil 143 , a photoresist layer 144 , a connecting portion 145 and an upper magnetic pole 146 , as shown in FIGS. 21 and 22 .
The write gap layer 141 is made of an electrical insulating material such as Al 2 O 3 and AlN, and is formed on the upper shielding layer 121 . The write gap layer 141 has an aperture 141 A for formation of a magnetic path in a position corresponding to the center of the coil 143 in the XY-plane (refer to FIG. 21 ). The coil 143 is formed in the shape of a spiral in plan view around the aperture 141 A on the write gap layer 141 . Further, the photoresist layer 144 is formed in a specified pattern so as to cover the coil 143 . Here, the photoresist layer 144 has been cured in advance by heat-treatment. Terminals of the coil 143 are connected to electrodes 143 S and 143 E, respectively. The pole chip 142 is arranged between the coil 143 covered with the photoresist layer 144 on the write gap layer 141 and the ABS 100 F. The connecting portion 145 is arranged so as to cover the aperture 141 A.
The upper magnetic pole 146 , which is made of a magnetic material having a high saturation magnetic flux density such as a NiFe alloy or iron nitride (FeN), is formed so as to cover the pole chip 142 , the photoresist layer 144 and the connecting portion 145 . The upper magnetic pole 146 connects the pole chip 142 and the connecting portion 145 magnetically, and further, is in contact with the upper shielding layer 121 via the connecting portion 145 to be magnetically connected therewith. Although not illustrated, it is to be noted that an overcoat layer made of Al 2 O 3 and so on covers the whole upper surface of the write head portion 110 B.
The write head portion 110 B with such configuration writes information in such a manner as follows. Magnetic flux is generated by currents flowing through the coil 143 in the magnetic path constructed mainly by the upper shielding layer 121 and the upper magnetic pole 146 . The magnetic flux then produces a signal magnetic field around the write gap layer 141 , and the signal magnetic field magnetizes the magnetic recording medium to write information thereon.
Next, method of manufacturing the thin film magnetic head 110 will be explained.
First, whole picture of the method of manufacturing the thin film magnetic head 110 is explained with reference to FIGS. 21 and 22 .
First, after forming the lower shielding layer 111 which is typically made of NiFe by electroplating on the substrate 100 , the lower gap layer 112 is formed by sputtering or the like on the lower shielding layer 111 . Next, a multilayer film which will become the MR film pattern 114 is formed on the lower gap layer 112 . Specifically, the foundation layer, the pinning layer, the pinned layer, the non-magnetic layer, the free layer and the cap layer, all of which are not illustrated, are layered in order by sputtering or the like. Then, the multilayer film is selectively etched by photolithographical patterning, ion milling and the like, to form the MR film pattern 114 . After this, the pair of magnetic domain controlling layers 115 L and 115 R are formed on the lower gap layer 112 so that they may be opposed to each other on both sides of the MR film pattern 114 . Further, the conductive lead layers 116 L and 116 R are formed on the magnetic domain controlling layers 115 L and 115 R, respectively. Subsequently, the upper gap layer 120 is formed by sputtering for example so as to cover the whole body. Finally, the upper shielding layer 121 , which is typically made of NiFe, is selectively formed by electroplating on the upper gap layer 120 , and formation of the read head portion 110 A is generally completed.
Subsequently, the write head portion 10 B is formed on the read head portion 110 A.
Specifically, first, the write gap layer 141 is selectively formed on the upper shielding layer 121 by sputtering or the like, and is partially etched to form the aperture 141 A for forming the magnetic path. Next, the pole chip 142 is formed on the write gap layer 141 on the ABS 100 F side by electroplating, and the connecting portion 145 is formed by electroplating so that the aperture 141 A may be covered. Further, the coil 143 of a spiral shape is formed around the aperture 141 A, then the photoresist layer 144 is formed in a specified pattern so that the coil 143 may be covered, and is cured by heat-treatment. After forming the photoresist layer 144 , the upper magnetic pole 146 is selectively formed so as to connect the pole chip 142 and the connecting portion 145 . In this manner, formation of the write head portion 110 B is generally completed.
›DESCRIPTION OF THE PREFERRED EMBODIMENTS · 5 of 6
Finally, the overcoat layer which is not illustrated is formed so as to cover all the foregoing structures including the upper magnetic pole 146 . In this manner, formation of the thin film magnetic head 110 which is constituted by the read head portion 110 A and the write head portion 110 B is completed.
Subsequently, formation process of the lower shielding layer 111 and the upper shielding layer 121 is explained in detail with reference to FIGS. 23 to 26 . FIGS. 23 to 26 is a plan view showing each production process when the lower shielding layer 111 and the upper shielding layer 121 are formed.
In forming the lower shielding layer 111 , s plating foundation layer (not shown) which is made of NiFe is formed so that a surface of the substrate 100 may be covered. Subsequently, after forming a resist layer (not shown) so that the whole plating foundation layer may be covered, a photoresist pattern 113 A of a specified shape as shown in FIG. 23 is formed by photolithography.
Photoresist patterns 113 B to 113 I, which are configured and arranged as shown in FIG. 23 , are formed simultaneously with the formation of the photoresist pattern 113 A. The photoresist pattern 113 A as a photoresist frame is disposed so as to surround a portion R 113 A in which the lower shielding layer 111 will be formed (hereinafter called formation portion). The photoresist patterns 113 B to 113 I as an auxiliary pattern are desirably disposed symmetrically each other with respect to the photoresist pattern 113 A. In FIG. 23 , the photoresist pattern 113 B vs. the photoresist pattern 113 I, the photoresist pattern 113 C vs. the photoresist pattern 113 H, the photoresist pattern 113 D vs. the photoresist pattern 113 G, and the photoresist pattern 113 E vs. the photoresist pattern 113 F are arranged symmetrically, respectively. It is further desirable that configurations and dimensions of the photoresist patterns 113 B to 113 I are all equal to each other, and a part of the width thereof is equal to a part of the width of the photoresist pattern 113 A. Here, it is defined that an auxiliary portion R 113 B is an area excluding the areas occupied by the photoresist pattern 113 (photoresist patterns 113 A to 113 I) and the formation portion R 113 A from the unit field R 4 . Accordingly, sum total of the formation portion R 113 A and the auxiliary portion R 113 B are taken as an area to be plated, denoted by the plating portion R 113 .
After forming the photoresist pattern 113 , plating is performed using the foregoing plating device to form a plating layer (not shown) made of NiFe so that the plating portion R 113 may be occupied therewith. Then the lower shielding layer 111 of a specified shape, which is formed by the plating layer and the plating foundation layer and formed on the formation portion R 113 A, is obtained as with the above-mentioned first embodiment (refer to FIG. 24 ).
The upper shielding layer 121 can be formed as with the case of the lower shielding layer 111 . Namely, after forming a plating foundation layer (not shown) made of NiFe so that the surface of the upper gap layer 120 may be covered, photoresist patterns 117 A to 117 K (hereinafter generically called photoresist pattern 117 ) of a specified shape are arranged in a specified position as shown in FIG. 25 . The photoresist pattern 117 A is disposed so as to surround a portion R 117 A in which the upper shielding layer 121 will be formed (formation portion), and works as a photoresist frame for defining the outline of the upper shielding layer 121 . On the other hand, photoresist patterns 117 B to 117 K works as an auxiliary pattern. After forming the photoresist pattern 117 , the upper shielding layer 121 of the specified shape, which is formed by the plating layer and the plating foundation layer and formed in the formation portion R 117 A, is obtained as with the case of the lower shielding layer 111 (refer to FIG. 26 ).
Here, it is defined that an auxiliary portion R 117 B is an area excluding the areas occupied by the photoresist pattern 117 and the formation portion R 117 A from the unit field R 4 . Herein, sum total occupation area of the photoresist pattern 117 is made equal to that of the photoresist pattern 113 ; In other words, the occupation area of a plating portion R 117 , which is the sum total of the formation portion R 117 A and the auxiliary portion R 117 B, is made equal to the occupation area of the plating portion R 113 .
In the second embodiment of the present invention, as described above, since sum total of the occupation area of the photoresist pattern 113 and that of the photoresist pattern 117 are equal to each other, an electrodeposition area, which is an area to be plated with plating layer, is also equal in each layer of the thin film magnetic head. Accordingly, a value of plating-current density can be kept constant easily without changing a current value. As a result, the lower shielding layer 111 and the upper shielding layer 121 , which have an almost same composition each other, can be formed very efficiently.
First Example
A detailed example of the present invention will be explained hereinbelow.
In the following example (a first example) of the present invention, a layered film was produced by plating technique with use of a photoresist pattern corresponding to that shown in the fifth modification ( FIGS. 20A to 20C ) of the above-mentioned first embodiment.
Specifically, the plating patterns M 1 to M 3 made of NiFe were respectively formed to have an average thickness of 2 μm respectively, in a specified region R 1 of 900 μm×400 μm on a silicon substrate (plated substrate) of 6 inches in diameter. Plane sizes of the plating patterns M 1 to M 3 will be indicated later in Table 1. Width of each gap field R 2 was 200 μm. The plating foundation layer 12 was formed to have an average thickness of 0.03 μm by sputtering. In forming the photoresist layer, “AZ5105P” of AZ Electronic Materials' product was used as a photoresist material and applied, then was heat-treated for 90 seconds at 100 degrees C. Further, the latent image portion was formed using “NSR-EX 14C (DUV)”, an exposure product of NIKON CORP. The exposing condition was set to: numerical aperture (NA): 0.6, diaphragm σ (ratio of illumination to lens NA): 0.6. After exposure, development was accomplished using an aqueous alkaline solution (2.38% aqueous tetramethylammonium hydroxide (TMAH)). Width W 1 of each photoresist patterns 13 A, 17 A and 18 A as a photoresist frame was 20 μm. Surface ratio of each plating portion (R 13 , R 17 , R 18 ) to the unit field R 4 was set to 85.6% in each of the first to third layers L 1 to L 3 , as shown in Table 1. A Watts-type nickel (Ni) bath, added by iron ion, was used as the plating bath 31 . The unnecessary plating layer 15 formed in each of the auxiliary portions R 13 B, R 17 B, and R 18 B was removed by wet etching with use of a ferric chloride solution as etching solution. Further, each photoresist pattern was removed with use of acetone or N-methylpyrrolidone (NMP).
›DESCRIPTION OF THE PREFERRED EMBODIMENTS · 6 of 6
Composition of the layered film, which was produced in the first example on the aforementioned condition, was confirmed in comparison with that of a first comparative example using a microscopic fluorescent-X-ray-spectrographic-analysis apparatus “JSM-6600F” of JEOL Co., Ltd. Here, the average content of nickel element in five arbitrary places was measured in each of the plating patterns M 1 to M 3 . Results are shown in Table 1 with manufacturing conditions. In addition, a case where layered film including the plurality of plating patterns were produced by plating only with use of the photoresist frame and without any auxiliary pattern at all, is shown as the first comparative example in Table 1. Set current of power supply was set to 2.8 A in the first example, and 3.0 A in the first comparative example.
First Example
As shown by Table 1, it was confirmed that, in the case of the first comparative example, the nickel content decreased according to the reduction of the surface ratio of each of the Plating portions (electrodeposition areas). On the other hand, in the case of the first example, it was confirmed that the nickel content was equal in each of the Plating patterns (namely, the composition ratio of Ni to Fe was equal in each pattern) because surface ratio of the Plating portion (electrodeposition area) was uniformed in each of the first to the third layers. Thus, it proves that the plating method of the present invention is effective when the planar configuration and occupation area of the plating pattern is different in each layer.
As mentioned above, although the present invention has been explained with reference to some embodiments and examples (hereinafter generically called embodiments), the present invention is not limited to the embodiments, and various kinds of modifications are available. For example, although the above-mentioned embodiments explain the cases where the plating patterns M 1 to M 3 are layered continuously, it is not limited to this. For example, an arbitrary intervening layer, which is formed by a method other than the electroplating method, such as sputtering, may be disposed therebetween. In that case, the intervening layer may be a plating layer or may be an insulating layer. Besides, in the above-mentioned embodiments, although one plating pattern is formed in each layer, a plurality of plating patterns may be formed collectively in each layer. For example, the present invention is also applicable to a case where a photoresist frame 19 A surrounding a formation portion R 19 A of a rectangular shape and a photoresist frame 19 B surrounding a formation portion R 19 B of an elliptical shape are formed in the same layer to collectively produce a plating pattern of the rectangular shape and a plating pattern of the elliptical shape with use of the photoresist frames 19 A and 19 B, as shown in a sixth modification shown in FIG. 27 .
Besides, in the above-mentioned embodiments, although the case is explained where the plating pattern of each layer is different from each other in configuration and dimension, it is not limited to this. For example, the present invention is also effective when only the configuration of the plating pattern mutually differs in each layer and the area thereof is all equal. Namely, when the plating pattern in each layer has a remarkably different configuration from each other, growing difference thereof may cause a considerable difference in the composition thereof even if the area of the plating pattern is equal to each other. In the present invention, even if the plating pattern in each layer has a different configuration from each other, difference in composition thereof can be suppressed very small by forming the layers so as to include other auxiliary plating layers thereon in addition to the plating patterns, respectively.
In the second embodiment as described above, although the case of forming a plurality of magnetic shielding layers all having the same composition to be used in a thin film magnetic head is explained, the present invention is not limited to this. For example, it is also suitable for formation of various plating patterns included in other electronic and magnetic micro devices, such as a thin film inductor, a common mode filter or a magnetic random-access memory (MRAM).
It should be understood by those skilled in the art that various modifications, combinations, sub-combinations and alterations may occur depending on design requirements and other factors insofar as they are within the scope of the appended claims or the equivalents thereof.
›Tables in the description — 1
| Plane Size | Width of | of | Ni Content | ||
| of Plating | Photoresist | Metal-plated | of Plating | ||
| Layers | Pattern | Frame | Portion | Pattern | |
| Example 1 | First | 50 μm × 50 μm | 20 μm | 85.6% | 81.5% |
| layer | |||||
| Second | 50 μm × 100 μm | 20 μm | 85.6% | 81.5% | |
| layer | |||||
| Third | 50 μm × 150 μm | 20 μm | 85.6% | 81.5% | |
| layer | |||||
| Comparative | First | 50 μm × 50 μm | 20 μm | 91.7% | 81.5% |
| Example 1 | layer | ||||
| Second | 50 μm × 100 μm | 20 μm | 88.7% | 81.2% | |
| layer | |||||
| Third | 50 μm × 150 μm | 20 μm | 85.8% | 80.9% | |
| layer |
Claims as granted
8 claimsLog in to read the claims of this application.
Log in to unlockClassifications
3 codes- C25D5/02
Claim changes
SoonSee which claims were amended, added or cancelled during examination, with every added and removed word marked.
The published claims of this application are not paired with the granted ones in what we hold.
File wrapper
See the full prosecution history — every USPTO and applicant action on this file, in order.
Log in to unlockDocuments
Log in to open the documents of this file: the application as filed, every office action and response, the notice of allowance.
Log in to unlockChain of title
See the full assignment history — every owner this patent has passed through, with recordation dates and reel/frame numbers.
Log in to unlock