The present invention relates to a catalyst composition for ethylene oligomerization and the use thereof. Such catalyst composition includes chromium compound, ligand containing P and N, activator and accelerator; wherein the chromium compound is selected from the group consisting of acetyl acetone chromium, THF-chromium chloride and Cr(2-ethylhecanoate) 3 ; general formula of the ligand containing P and N is shown as: [structure] in which R 1 , R 2 , R 3 and R 4 are phenyl, benzyl, or naphthyl. R 5 is isopropyl, butyl, cyclopropyl, cyclopentyl, cyclohexyl or fluorenyl; the activatior is methyl aluminoxane, ethyl aluminoxane, propyl aluminoxane and/or butyl aluminoxane; the accelerator is selected from the group consisting of 1,1,2,2,-tetrachloroethane, 1,1,2,2-tetrabromoethane, 1,1,2,2-tetrafluoroethane, and compounds having a formula of X 1 R 6 X 2 , in which X 1 and X 2 are F, Cl, Br, I or alkoxyl, R 6 is alkylene or arylene group; the molar ratio of chromium compound, ligand containing P and N, activator and accelerator is 1:0.5Ëœ10:50Ëœ3000:0.5Ëœ10. After mixing the four components mentioned previously under nitrogen atmosphere for 10 minutes, they are incorporated to the reactor, or these four components are incorporated directly into the reactor. Then ethylene is introduced for oligomerization. Such catalyst can be used in producing 1-octene through ethylene oligomerization. It is advantageous in high catalysing activity, high 1-octene selectivity, etc. The catalytic activity is more than 1.0Ã—10 6 g productÂ·ma âˆ’1 CrÂ·h âˆ’1 , the fraction of C 8 linear Î±-olefin is more than 70% by mass.

Description

11 parts

›FIELD OF THE INVENTION

The present invention relates to a catalyst system, in particular to a catalyst composition for ethylene oligomerization and to the use thereof.

›BACKGROUND OF THE INVENTION

As it is known that linear α-olefins, such as 1-octene, 1-hexene, etc, are important chemical products and intermediates, they are widely applied in various fields such as comonomers of polyethylene, alcohols plasticizers, flavor additives, synthetic lubricant and additives of oil products. Employing 1-octene and 1-hexene as comonomers will significantly improve the density, and mechanical properties such as tear strength and tensile strength of polyethylene. When be used as alcohols to produce plasticizers, they could endue polyethylene articles better softness at low temperature, processing behavior, better outdoor weathering durability, particularly suitable for wires and cables, automobile accessories, decoration materials, etc.

Even though 1-octene is of great importance in chemical industry, now there is no synthesis technique to produce 1-octene through ethylene oligomerization with high selectivity. In traditional process of ethylene oligomerization, the carbon number of the products is accordant with Schulz-Flory Distribution that results to a lower concentration of 1-octene in the oligomer products. For example, U.S. Pat. No. 6,184,428 discloses a kind of nickel catalyst using boron compound as cocatalyst, which could catalyze ethylene oligomerization to obtain the mixture of linear α-olefins, wherein the amount of 1-octene is 19%. SHOP process (U.S. Pat. Nos. 3,676,523 and 3,635,937) uses a similar catalyst system, and the amount of 1-octene reaches to 11% of oligomer products. Other typical ethylene oligomerization processes, such as Chevron process (DE 1,443,927) of Gulf Research Development Co., and ethylene oligomerization process (BP/Amoco, U.S. Pat. No. 3,906,053) of Ethyl Corp., generally produce 1-octene with concentration of about 13˜25%. Chromium-based catalyst systems are mainly used in trimerization of ethylene, wherein the concentration of 1-octene is low (less than 3%). A iron-based catalyst reported recently (J. Am. Chem. Soc., 1998, 120:7143; Chem Commun. 1998,849; WO 99/02472) for ethylene oligomerization also results to oligomer products with wider distribution, in which the concentration of 1-octene is low (less than 20%) either. According to WO 2004/056478, tetramerization of ethylene produces 1-octene with concentration of no more than 69.3%.

›SUMMARY OF THE INVENTION

The present invention is to provide a new catalyst composition, particularly the invention relates to a kind of catalyst composition for ethylene oligomerization. The composition includes chromium compound, ligand containing P and N, activators and accelerators, wherein the chromium compound is selected from the group consisting of acetyl acetone chromium, THF-chromium chloride and/or Cr(2-ethylhecanoate) 3 .

The general formula of the Ligand containing P and N is shown as follow:

wherein R 1 , R 2 , R 3 and R 4 are phenyl, benzyl, fluorenyl or naphthyl. R 5 is isopropyl, butyl, cyclopropyl, cyclopentyl, cyclohexyl or fluorenyl;

The activator is methylaluminoxane, ethylaluminoxane, propylaluminoxane and/or butylaluminoxane.

The accelerator is selected from the group consisting of 1,1,2,2-tetrachloroethane, 1,1,2,2-tetrabromoethane, 1,1,2,2,-tetrafluoroethane, and compounds having a formula of X 1 R 6 X 2 , in which X 1 and X 2 are F, Cl, Br, I or alkoxyl, R 6 is alkylene or arylene group.

The molar ratio of the chromium compound:the ligand containing P and N:the activator:the accelerator is 1:0.5˜10:50˜3000:0.5˜10.

In one aspect of the invention, four components, i.e. chromium compound, ligand containing P and N, activator and accelerator, can be mixed under nitrogen atmosphere for at least 10 minutes before being added to a reactor, then ethylene is introduced for oligomerization. In another embodiment of the invention, the four components, i.e., the chromium compound, the ligand containing P and N, the activator and the accelerator are added directly to the reactor respectively, then ethylene is introduced for oligomerization. The reaction temperature is between 30° C. and 200° C., preferably between 30° C. and 90° C., more preferably between 30° C. and 70° C. The reaction pressure is between 0.5 MPa and 20.0 MPa, preferably between 1 MPa and 10 MPa, more preferably between 2 MPa and 6 MPa. The reaction time is between 0.1 hour and 2 hours, preferably between 0.3 hour and 1 hour, more preferably between 0.5 hour and 0.7 hour.

The present invention also relates to a preparation process of catalyst composition useful for ethylene oligomerization. The process includes sequentially mixing and reacting the activator, the Ligand containing P and N, the chromium compound and the accelerator in inert solvent under nitrogen atmosphere, wherein the molar ratio of the chromium compound:the ligand containing P and N:the activator:the accelerator is 1:0.5˜10:50˜3000:0.5˜10. Preferably the inert solvent includes cyclohexane, xylene or isopropylbenzene.

The ethylene oligomerization mainly carries out in inert solvent. A suitable solvent can be selected from the group consisting of alkanes, arenes, halohydrocarbons or alkenes. The typical solvent is, but not limited to, benzene, toluene, xylene, isopropylbenzene, n-heptane, n-hexane, methyl cyclohexane, cyclohexane, 1-hexene, 1-octene, ionic liquid, etc.

The chief advantages and effects of the present invention lie in chromium-based catalyst of the invention because of the action of the accelerator, it is easily for four ethylene molecules to coordinate on four coordination bonds of chromium atom that are perpendicularly to each other. It is thus advantageous for self-polymerization of the four ethylene molecules to produce 1-octene selectively. Therefore, the catalyst has advantages of high activity, good selectivity to producing 1-octene and less by-product of polyethylene. The catalyst has activity of more than 1.0×10 6 g product·mol −1 Cr·h −1 , while fraction of C 8 linear α-alkene is more than 70% by mass.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

›Examples7

›EXAMPLE 1

1. Preparation of (diphenyl)phosphorous-nitrogen(cyclopropyl)phosphorous(diphenyl) ligand

Dehydrated dichloromethane (20 mL), triethylamine (3.75 mL) and diphenyl phosphorus chloride (1.326 mL, 7.2 mmol) were added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. The temperature was reduced to 0° C. Cyclopropylamine (3.6 mmol) was added gradually. The reaction system was agitated for 30 min, then heated to room temperature to keep reaction for another 12 hours. The product was obtained by filtering and drying (0.87 g, 56.6%).

2. Preparation of the Catalyst

Dehydrated toluene (10 mL) was added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. Then 1.4 mol/L of solution of methylaluminoxane in toluene (c), (diphenyl)phosphorous-nitrogen(cyclopropyl)phosphorous(diphenyl) ligand (b) obtained previously, Cr(2-ethylhecanoate) 3 (a) and 1,1,2,2-tetrachloroethane (d) were added sequentially according to the ratio of a:b:c:d=1:0.5:300:1. The reaction was conducted at room temperature for 10 minutes, and then the product was removed for further application.

3. Ethylene Oligomerization

Referring to table 1, a 500 mL autoclave was heated to be vacuated for 2 hours. After being substituted with nitrogen gas several times, the autoclave was charged with ethylene. The temperature was reduced to a predetermined temperature, then dehydrated toluene (200 mL) and the catalyst produced previously was added. Oligomerization was conducted at 40° C., 5.0 MPa. After 30 minutes reaction, the temperature was lowed by ice bath and the pressure was removed. The reaction was terminated with 10% by mass of acidified ethanol. The oligomer obtained was 22.8 g. The activity of the catalyst was 2.13×10 6 g oligomer/mol Cr.h.

›EXAMPLE 2

1. Preparation of N-cyclopentylbis(diphenylphosphino) ligand

Dehydrated dichloromethane (20 mL), triethylamine (3.75 mL) and diphenyl phosphorus chloride (1.326 mL, 7.2 mmol) were added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. The temperature was reduced to 0° C. Cyclopentylamine (0.415 ml, 3.5 mmol) was added gradually. The reaction system was agitated for 30 min, and then heated to room temperature to keep reaction for another 12 hours. The product was obtained by filtering and drying (0.55 g, 32.68%).

2. Preparation of the Catalyst

Dehydrated cyclohexane (10 mL) was added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. Then 1.4 mol/L of solution of methylaluminoxane in toluene (c), (diphenyl)phosphorous-nitrogen (cyclopentyl)phosphorous(diphenyl) ligand N-cyclopentylbis(diphenylphosphino) (b) obtained previously, tetrahydrofuran chromium chloride (a) and 1,1,2,2-tetrabromoethane (d) were added sequentially according to the ratio of a:b:c:d=1:0.5:50:0.5. The reaction was conducted at room temperature for 5 minutes, then the product was removed for further application.

3. Ethylene Oligomerization

Referring to table 1, a 500 mL autoclave was heated to be vacuated for 2 h. After being substituted with nitrogen gas several times, the autoclave was charged with ethylene. The temperature was reduced to a predetermined temperature, and then dehydrated cyclohexane (200 mL) and the catalyst produced previously were added. Oligomerization was conducted at 30° C., 6.0 MPa. After 20 minutes reaction, the temperature was lowed by ice bath and the pressure was removed. The reaction was terminated with 10% by mass of acidified ethanol. The oligomer obtained was 49.4 g. The activity of the catalyst was 1.70×10 6 g oligomer/mol Cr.h.

›EXAMPLE 3

1. Preparation of (diphenyl)phosphrous-nitrogen(fluorenyl)phosphorous(diphenyl) ligand

Dehydrated dichloromethane (20 mL), triethylamine (3.75 mL) and diphenyl phosphorus chloride (1.326 mL, 7.2 mol) were added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. The temperature was reduced to 0° C. Fluorenamine (0.652 g, 3.6 mmol) was added gradually. The reaction system was agitated for 30 min, and then heated to room temperature to keep reaction for another 12 hours. The product was obtained by Filtering and drying (0.48 g, 24.3%).

2. Preparation of the Catalyst

Dehydrated cyclohexane (10 mL) was added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. Then Propyl aluminoxane (c), (diphenyl)phosphorous-nitrogen (fluorenyl) phosphorous(diphenyl) ligand (b) obtained previously, acetylactone chromium (a) and 1,2-dimethoxyl ethane (d) were added sequentially according to the ratio of a:b:c:d=1:1:200:3. The reaction was conducted at room temperature for 5 minutes, then the product was removed for further application.

3. Ethylene Oligomerization

Referring to table 1, a 500 mL autoclave was heated to be vacuated for 2 h. After being substituted with nitrogen gas several times, the autoclave was charged with ethylene. The temperature was reduced to a predetermined temperature, then dehydrated benzene (200 mL) and the catalyst produced previously were added. Oligomerization was conducted at 200° C., 2.0 MPa. After 40 minutes reaction, the temperature was lowed by ice bath and the pressure was removed. The reaction was terminated with 10% by mass of acidified ethanol. The oligomer obtained was 47.9 g. The activity of the catalyst was 1.64×10 6 g oligomer/mol Cr.h.

›EXAMPLE 4

1. Preparation of 1,4-di(N(P(phenyl) 2 ) 2 )-benzene ligand

Dehydrated dichloromethane (20 mL), triethylamine (3.75 mL) and diphenyl phosphorus chloride (1.326 mL, 7.2 mmol) were added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. The temperature was reduced to 0° C. 1,4-phenylenediamine (0.19 g, 1.8 mmol) was added gradually. The reaction system was agitated for 30 min, and then heated to room temperature to keep reaction for another 12 hours. The product was obtained by filtering and drying (0.8 g, 52.3%).

2. Preparation of the Catalyst

Dehydrated cyclohexane (10 mL) was added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. Then 1.4 mol/L of solution of methyl aluminoxane in toluene (c), 1,4-di(N(P(phenyl) 2 ) 2 )-benzene ligand (b) obtained previously, Cr(2-ethylhecanoate) 3 (a) and 1,2-dichloroethane (d) were added sequentially according to the ratio of a:b:c:d=1:10:300:10. The reaction was conducted at room temperature for 10 minutes, then the product was removed for further application.

3. Ethylene Oligomerization

A 500 mL autoclave was heated to be vacuated for two hours. After being substituted with nitrogen gas several times, the autoclave was charged with ethylene. The temperature was reduced to a predetermined temperature, then dehydrated heptane (200 mL) and the catalyst produced previously were added. Oligomerization was conducted at 90° C., 7.0 MPa. After 20 minutes reaction, the temperature was lowed by ice bath and the pressure was removed. The reaction was terminated with 10% by mass of acidified ethanol. The activity of the catalyst was 8.23×10 6 g oligomer/mol Cr.h. The distribution of oligomerization product is shown in table 1.

›EXAMPLE 5

1. Preparation of (diphenyl)phosphorous-nitrogen(cyclohexyl)phosphorous(diphenyl) ligand

Dehydrated dichloromethane (20 mL), cyclohexyamine (3.75 mL) and diphenyl phosphorus chloride (1.326 mL, 7.2 mmol) were added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. The temperature was reduced to 0° C. 1,4-phenylenediamine (0.19 g, 1.8 mmol) was added gradually. The reaction system was agitated for 30 min, and then heated to room temperature to keep reaction for another 12 hours. The product was obtained by filtering and drying (0.8 g, 52.3%).

2. Preparation of the Catalyst

Dehydrated xylene (10 mL) was added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. Then 1.4mol/L of solution of methylaluminoxane in toluene (c), (diphenyl)phosphorous-nitrogen (cyclohexyl)phosphorous(diphenyl) ligand (b) obtained previously, tetrahydrofuran chromium chloride (a) and 1,4-dichlorobenzene (d) were added sequentially according to the ratio of a:b:c:d=1:5:2000:8. The reaction was conducted at room temperature for 5 minutes, then the product was removed for further application.

3. Ethylene Oligomerization

A 500 mL autoclave was heated to be vacuated for two hours. After being substituted with nitrogen gas several times, the autoclave was charged with ethylene. The temperature was reduced to a predetermined temperature, then dehydrated xylene (200 mL) and the catalyst produced previously were added. Oligomerization was conducted at 150° C., 5.0 MPa. After 50 minutes reaction, the temperature was lowed by ice bath and the pressure was removed. The reaction was terminated with 10% by mass of acidified ethanol. The oligomer obtained was 24.1 g. The activity of the catalyst was 2.28×10 6 g oligomer/mol Cr.h. The distribution of oligomerization product is shown in table 1.

›EXAMPLE 6

1. Preparation of (diphenyl)phosphrous-nitrogen(isopropyl)phosphorous(diphenyl) ligand

Dehydrated dichloromethane (20 mL), isopropylamine (5.5 mL) and diphenyl phosphorus chloride (1.326 mL, 7.2 mmol) were added to a 100 mL reactor equipped with agitator and substituted with N 2 completely. The temperature was reduced to 0° C. 1,4-phenylenediamine (0.19 g, 1.8 mmol) was added gradually. The reaction system was agitated for 30 min, and then heated to room temperature to keep reaction for another 12 hours. The product b was obtained by filtering and drying (0.8 g, 52.3%).

2. Ethylene Oligomerization

A 500 mL autoclave was heated to be vacuated for 2 h. After being substituted with nitrogen gas several times, the autoclave was charged with ethylene. The temperature was reduced to a predetermined temperature, then dehydrated isopropyl benzene (200 mL) was added. Then 1.4 mol/L of solution of methyl aluminoxane in toluene (c), (diphenyl) phosphorous-nitrogen(isopropyl)phosphorous(diphenyl) (b) obtained previously, tetrahydrofuran chromium chloride (a) and 1,4-dichlorobenzene (d) were added sequentially according to the ratio of a:b:c:d=1:2:300:3. Oligomerization was conducted at 50° C., 7.0 MPa. After 30 minutes reaction, the temperature was lowed by ice bath and the pressure was removed. The reaction was terminated with 10% by mass of acidified ethanol. The oligomer obtained was 6.32 g. The activity of the catalyst was 2.30×10 6 g oligomer/mol Cr.h. As is shown in table 1.

›EXAMPLE 7

1. Preparation of (dinaphthyl)phosphorous-nitrogen(butyl)phosphorous(dinaphthyl) ligand

Dehydrated dichloromethane (20 mL), isopropylamine (5.5 mL) and diphenyl phosphorus chloride (1.326 mL, 7.2 mmol) were added to 100 mL reactor equipped with agitator and substituted with N 2 completely. The temperature was reduced to 0° C. 1,4-phenylenediamine (0.19 g, 1.8 mmol) was added gradually. The reaction system was agitated for 30 min, and then heated to room temperature to keep reaction for another 12 hours. The product was obtained by filtering and drying (0.8 g, 52.3%).

2. Ethylene Oligomerization

A 500 mL autoclave was heated to be vacuated for 2 h. After being substituted with nitrogen several times, the autoclave was charged with ethylene. The temperature was reduced to a predetermined temperature, and then dehydrated cyclohexane (200 mL) was added. The 1.4 mol/L of solution of methylaluminoxane in toluene (c), (diphenyl) phosphorous-nitrogen(butyl)phosphorous(diphenyl) (b) obtained previously, tetrahydrofuran chromium chloride (a) and 1,1,2,2-tetrafluoroethane(d) were added sequentially according to the ratio of a:b:c:d=1:1:200:3. Oligomerization was conducted at 50° C., 8.0 MPa. After 20 minutes reaction, the temperature was lowed by ice bath and the pressure was removed. The reaction was terminated with 10% by mass of acidified ethanol. The oligomer obtained was 43.2 g. The activity of the catalyst was 1.51×10 6 g oligomer/mol h. As is shown in table 1.

›Tables in the description — 1

TABLE 1 — a refers to the percentage of 1-C 8 = in C 8 .

	Example 1	Example 2	Example 3	Example 4	Example 5	Example 6	Example 7
Activity of catalyst (g oligomer/mol Cr · h) × 10 6	2.13	1.70	2.64	8.23	2.28	2.30	1.51
Selectivity to 1-C 4 = (wt %)	0.54	0.32	0.73	0.45	0.01	0.69	0.73
Selectivity to 1-C 6 = (wt %)	11.03	12.52	18.31	19.40	33.81	21.65	21.82
Selectivity to 1-C 8 = (wt %)	73.40	71.13	70.15	75.84	69.34.	70.20	72.06
Purity a to 1-C 8 = (%)	99.24	98.70	98.71	98.81	96.07	96.03	98.01
Polymer	0.2%	0.1%	0.2%	0.1%	0.1%	0.02%	0.06%

Claims as granted

8 claims

Classifications

13 codes

IPC · International Patent Classification

Section B — Performing operations; transporting

B01J31/14
B01J31/18
B01J31/22

Section C — Chemistry; metallurgy

C07C2/26
C07C2/32

USPC · US Patent Classification

585/513502/128502/103502/123585/520585/527502/121585/514

Claim changes

Soon

Coming soonHow the claims changed between publication and grant

See which claims were amended, added or cancelled during examination, with every added and removed word marked.

AmendedAddedCancelledUnchanged

The published claims of this application are not paired with the granted ones in what we hold.

File wrapper

⤢ drag to zoom

USPTOApplicanthover for detail · click to open

Pendency

3.5 y

1,271 days filing → grant

Office actions

non-final + final

Responses

no RCE

Examiner

Caixia Lu

art unit 1796 · TC 1700

Law firm

Law firm · Log in to unlock

Citations: 12 back · 12 forward

See the full prosecution history — every USPTO and applicant action on this file, in order.

Documents

Log in to open the documents of this file: the application as filed, every office action and response, the notice of allowance.

Chain of title

⤢ drag to zoom

Titlehover for detail · click to open

See the full assignment history — every owner this patent has passed through, with recordation dates and reel/frame numbers.