Method of fabricating porous aluminum oxide mold having sub-micron structure and methods of imprinting to make LEDS using the mold

The present invention relates to fabricating a mold; more particularly, relates to obtaining a porous mold, aluminum oxide (Al 2 O 3 ) for mass-imprinting a sub-micron structure on a light emitting diode (LED), a laser diode or a substrate with a fast speed and a cheap cost.

A nano pattern imprinted on a semiconductor is mainly performed through electron beam lithography. This technology has a disadvantage of slow speed that does not meet a user's requirements. There is still another method for imprinting nano patterns, called laser interferometry lithography. Its disadvantage is that it is hard to imprint a pattern evenly on a large surface. Besides, producers usually use masks on imprinting nano pattern and thus the cost is high. Hence, the prior arts do not fulfill users' needs.

The main purpose of the present invention is to fabricate a porous aluminum oxide (Al 2 O 3 ) mold with pore size, pore space in between, and film thickness all controlled through process parameters.

Another purpose of the present invention is to quickly and cheaply mass-imprint a sub-micron structure on a large surface of a LED, a laser diode or a substrate to meet the needs of producers.

To achieve the above purpose, the present invention is a method of fabricating a porous Al 2 O 3 mold having a sub-micron structure, comprising steps of (a1) obtaining an aluminum pre-m old structure from an aluminum foil through annealing; (a2) cleansing the aluminum pre-mold structure and electrolytic polishing a surface of the aluminum pre-mold structure by an electrochemical method; (a3) anodizing the aluminum pre-mold structure and cleansing the aluminum pre-mold structure with a deionized water; (a4) fast-drying the aluminum pre-mold structure with ethanol and forming an oxidized layer; and, (a5) after being cleansed with a deionized water partially removing the oxidized layer by using a phosphoric acid to obtain a porous Al 2 O 3 mold having a sub-micron structure after drying the aluminum pre-mold structure in the air, where the porous Al 2 O 3 mold is used to imprint a sub-micron structure on a LED, a substrate, etc. and to further fabricate a p-side up LED or an n-side up LED. Accordingly, a novel method of fabricating a porous Al 2 O 3 mold having a sub-micron structure is obtained.

The present invention will be better understood from the following detailed description of the preferred embodiment according to the present invention, taken in con junction with the accompanying drawings, in which

FIG. 1 is the sectional view showing the porous Al 2 O 3 mold according to the preferred embodiment of the present invention;

FIG. 2A to FIG. 2E are views showing the first imprint method;

FIG. 3A to FIG. 3G are views showing the second imprint method;

FIG. 4A to FIG. 4G are views showing the third imprint method;

FIG. 5A to FIG. 5D a reviews showing fabricating the p-side up LED; and

FIG. 6A to FIG. 6E are views showing fabricating the n-side up LED;

The following description of the preferred embodiment is provided to understand the features and the structures of the present invention.

Please refer to FIG. 1 which is a sectional view showing a porous aluminum oxide (Al 2 O 3 ) mold according to a preferred embodiment of the present invention. As shown in the figure, the present invention is a method of fabricating a porous aluminum oxide mold having a sub-micron structure, comprising the following steps:

(a1) An aluminum foil is obtained to be processed through an annealing to obtain an aluminum pre-mold structure. Through the annealing, pores 11 in the aluminum pre-mold structure are arranged orderly and have even diameters.

(a2) After cleansing the aluminum pre-mold structure, the aluminum pre-mold structure is electrolytic polished on a surface by an electrochemical method, where impurities on the surface are removed and a smooth surface is obtained.

(a3) An anodizing is performed on the aluminum pre-mold structure and then the aluminum pre-mold structure is cleansed with a deionized water, where the aluminum pre-m old structure can be subjected to the anodizing process twice; the anodizing process uses a power supplier whose anode is connected with the aluminum pre-mold structure and whose cathode is connected with a graphite rod; the aluminum pre-mold structure is immersed in an electrolyte of a phosphoric acid, an oxalic acid or a sulfuric acid; and the electrolyte is stirred with a magnetic stirbar.

(a4) An ethanol is used to fast dry the aluminum pre-m old structure and an ivory-white film of an oxidized layer is formed on a surface.

(a5) A phosphoric acid is used to partially remove (e.g., by partially etching) the oxidized layer and then is washed with a deionized water to be dried in air to obtain a porous Al 2 O 3 mold 1 , where the porous Al 2 O 3 mold 1 is kept immersed in the phosphoric acid to obtain bigger pores having even diameters.

Pores obtained after anodizing are usually distributed into a difform pattern. A structure thus formed on a surface of a LED obtains a difform pattern to increase roughness which is in favor of light extraction. On the contrary, if a uniform pattern is preferred, the porous Al 2 O 3 mold needs to be pre-processed or be anodized again. Moreover, the pore-sizes and spaces between pores of the porous Al 2 O 3 mold are controlled by changing process parameters of the anodizing process, type of electrolyte used, voltage, time, etc.

When the porous Al 2 O 3 mold has pores forming a uniform pattern, the light extraction efficiency is improved by forming a photonic crystal structure, which has pores with proper sizes and a proper periodicity, on a surface of the n-type semi conductor and a surface of the p-type semiconductor. Besides, a proper mask can be deposed on a surface of the aluminum mold so that, in the process of anodizing, the area below the mask does not have any pores, which differs from the other porous structure of areas without the mask covered. Hence, the porous Al 2 O 3 mold can have photonic crystal resonant cavities and a special porous structure obtained with a mask.

Please refer to FIG. 2A to FIG. 2E which are views showing a first imprint method. As shown in the figures, a porous Al 2 O 3 mold according to the present invention has a first imprint method, comprising the following steps:

(b1) A polymer resist 22 is coated on a surface of an object, such as a first substrate 21 .

(b2) The object is imprinted by the porous Al 2 O 3 mold.

(b3) After cooling down the temperature, the polymer resist 22 is removed through etching, and an area on the surface of the object is thus revealed.

(b4) In the end, the object is etched on the area to obtain a sub-micron pattern

Please refer to FIG. 3A to FIG. 3G , which are views showing a second imprint method. As shown in the figures, a porous Al 2 O 3 mold according to the present invention is used in a second imprint method, comprising the following steps:

(c1) A protection layer 23 and then a polymer resist 22 are sequentially coated on a surface of an object, such as a first substrate 21 .

(c2) The object is imprinted by the porous Al 2 O 3 mold.

(c3) After lowering the temperature, the polymer resist 22 is removed through etching to reveal the protection layer 23 ; thus, after removing the polymer resist 22 , the protection layer 23 is used as an etching barrier.

(c4) Then, the protection layer 23 is etched to reveal an area on the surface of the object.

(c5) In the end, the object is etched on the area to obtain a sub-micron pattern.

Please refer to FIG. 4A to FIG. 4G which are views showing a third imprint method. As shown in the figures, a porous Al 2 O 3 mold according to the present invention has a third imprint method, comprising the following steps:

(d1) A polymer resist 22 is coated on a surface of an object, such as a first substrate 21 .

(d2) The object is imprinted by the porous Al 2 O 3 mold.

(d3) After lowering the temperature, a protection layer 23 is coated on the polymer resist and surface of the object.

(d4) Then through a process of lifting-off, the polymer resist 22 , together with portions of the protection layer 23 above the polymer resist 22 , is removed to reveal an area on the surface of the object.

(d5) In the end, the object is etched on the area to obtain a sub-micron pattern.

Please refer to FIG. 5A to FIG. 5D which are views showing fabricating a p-side up LED. As shown in the figures, at first, in step (e), a first substrate 31 is imprinted by a first, a second, or a third imprint method according to the present invention and then the first substrate 31 is sequentially grown with epitaxy layers of an n-type semiconductor 32 , an active layer 33 and a p-type semiconductor 34 . And then, in step (f), the p-type semiconductor 34 is imprinted by the first, the second or the third imprint method to obtain a sub-micron pattern. Hence, a p-side up LED is obtained.

Please refer to FIG. 6A to FIG. 6E , which are views showing fabricating an n-side up LED. As shown in the figures, at first, in step (g), a first substrate 31 is sequentially grown with epitaxy layers of an n-type semiconductor 32 , an active layer 33 and a p-type semiconductor 34 and then the p-type semiconductor 34 is imprinted by a first, a second or a third imprint method according to the present invention. Then, in step (h), a second substrate 35 is bonded on the p-type semiconductor 34 to obtain a bonded layer 36 . Then, in step (i), the first substrate 31 is removed to reveal the n-type semiconductor 32 . And then, in step (j), the n-type semiconductor 32 is imprinted by the first, the second or the third imprint method to obtain a sub-micron pattern. Hence, an n-side up LED is obtained.

Consequently, as is described above, a first, a second or a third imprint method according to the present invention is used at various layers of a LED and different patterns are obtained on the p-type semiconductor, the p-type semiconductor and the substrate.

In summary, the present invention is a method of fabricating a porous Al 2 O 3 mold having a sub-micron structure, where a porous Al 2 O 3 mold is fabricated with pore size, pore space in between, and film thickness all controlled through process parameters; the porous Al 2 O 3 mold fabricated has good mechanical and chemical characteristics; the fabrication requires no expensive equipment and is easy; and, a sub-micron structure is quickly and cheaply mass-imprinted on a large surface of a LED, a laser diode or a substrate, which meets the needs of producers.

The preferred embodiment herein disclosed is not intended to unnecessarily limit the scope of the invention. Therefore, simple modifications or variations belonging to the equivalent of the scope of the claims and the instructions disclosed herein for a patent are all within the scope of the present invention.