Silver halide photographic light-sensitive material

.Iadd.This application is a continuation of application Ser. No. 07/326,782 filed Mar. 21, 1989 now abandoned. .Iaddend.

The present invention relates to a silver halide photographic light-sensitive material, and more particularly to a silver halide photographic light-sensitive material which contains a cyan coupler excellent in the solubility as well as in the dispersion stability and which is capable of giving a satisfactorily color-reproducible and well-preservable dye image.

The formation of a dye image by use of a silver halide color photographic light-sensitive material is generally carried out in the manner that an aromatic primary amine color developing agent itself, when reducing the light-exposed silver halide particles of a silver halide color photographic light-sensitive material, is oxidized, and the oxidized product reacts with a coupler that is in advance contained in the silver halide color photographic light-sensitive material to thereby form a dye. And as the coupler, because the color reproduction is usually carried out by the color subtractive process, three different couplers; i.e., yellow, magenta and cyan couplers are used.

These couplers each is normally dissolved in a substantially water-insoluble high-boiling organic solvent or at need together with an auxiliary solvent, and the resulting solution is then adder to a silver halide emulsion.

Fundamental requirements for the nature of these couplers are that the coupler shall:

have large solubility in high-boiling organic solvents,

have no satisfactory dispersibility and dispersion stability that the coupler is hardly deposited,

be so excellent in the spectral absorption characteristics as well as in the color tone that a clear dye image can be formed in a wide color reproduction range, and

form a dye image which is highly resistant to light, heat and moisture. Especially, the cyan coupler should be improved on two points: one is that it should have litte or no absorption in the wavelength region other than its intrinsic spectral absorption wavelength region, and the other is that it should have higher resistance to light, heat and moisture.

Those conventionally known cyan couplers include 2,5-diacylaminophenol-type cyan couplers which are phenol compounds the second and fifth positions of which are substituted by acylamino radicals, as described in, e.g., U.S. Pat. No. 2,985,826, Japanese Patent Publication Open to Public Inspection (hereinafter referred to as Japanese Patent O.P.I. Publication) Nos. 112038/1975, 109630/1978 and 163537/1980. When such a 2,5-diacylaminophenol-type cyan coupler is used in a silver halide light-sensitive material, because of its very small secondary adsorption in the spectral wavelength range of from 400 to 450 nm, the light-sensitive material becomes better in the blue color reproduction as well as in the color restoration (cyan dye loss in prevented), and further becomes better improved on the dark discoloration resistance such as the resistance to heat and moisture, so that the light-sensitive material can be largely improved on the cyan dye image. However, the use of a 2,5-diacylaminophenol-type cyan coupler can not sufficiently satisfy the foregoing fundamental nature requirements because the coupler has the disadvantages that (1) its spectral minimum density in the wavelength range of from 450 to 480 nm is so high and its lightness is so low that its color reproducible range becomes narrow, while its absorption in the wavelength range of from 500 to 550 nm is so high that its green color reproduction becomes poor, (2) its resistance to light is insufficient, and (3) its solubility and dispersion ability are unsatisfactory.

It is therefore a first object of the present invention to provide a silver halide photographic light-sensitive material containing a cyan coupler which is excellent in the spectral absorption characteristic and capable of forming a clear dye image with good color tone in a wide color reproduction range.

It is a second object of the present invention to provide a silver halide photographic light-sensitive material which is improved so as to have well balanced resistances to light, heat and moisture, and capable of forming a well preservable dye image.

It is a third object of the present invention to provide a silver halide photographic light-sensitive material containing a cyan coupler which is excellent in the solubility, dispersibility and dispersion stability.

We have now found that the above objects of the present invention can be accomplished by a silver halide photographic light-sensitive material comprising a support having thereon at least one silver halide emulsion layer containing in combination at least one of those cyan couplers having the following Formula [I] and at least one of those cyan couplers having the following Formula [II], and thus we have completed the present invention. ##STR1## wherein R 1 represents an aryl radical, a cycloalkyl radical or a heterocyclic radical; R 2 represents an alkyl radical or a phenyl radical; R 3 is a hydrogen atom, a halogen atom, an alkyl radical or an alkoxy radical; and Z 1 is hydrogen atom, a halogen atom, or a radical that can be split off by the reaction of the coupler with the oxidized product of an aromatic primary amine-type color developing agent. ##STR2## wherein R 4 is an alkyl radical (such as methyl, ethyl, butyl, nonyl, etc.); R 5 is an alkyl radical (such as methyl, ethyl, etc.); R 6 is a hydrogen atom, a halogen atom (such as fluorine, chlorine, bromine, etc.) or an alkyl radical (such as methyl, ethyl, etc.); and Z 2 is a hydrogen atom, a halogen atom, or a radical that can be split off by the reaction of the coupler with the oxidized product of an aromatic primary amine-type color developing agent.

In the present invention, the aryl radical represented by R 1 of Formula .[.[I].]. .Iadd.I .Iaddend.includes, e.g., phenyl, naphthyl, and preferably phenyl. The heterocyclic radical represented by R 1 includes, e.g., pyridyl, furan, etc. The cycloalkyl radical represented by R 1 includes, e.g., cyclopropyl, cyclohexyl, etc. These radicals represented by R 1 are allowed to have a single or a plurality of substituents; for example, those typical substituents introducible to the phenyl include halogens (such as fluorine, chlorine, bromine, etc.), alkyl radicals (such as, e.g., methyl, ethyl, propyl, butyl, dodecyl, etc.), hydroxy radical, cyano radical, nitro radical, alkoxy radicals (such as, e.g., methoxy, ethoxy, etc.), alkyl-sulfonamido radicals (such as, e.g., methyl-sulfonamido, octyl-sulfonamido, etc.), aryl-sulfonamido radicals.[.).]. .Iadd.(.Iaddend.such as, phenylsulfonamido, naphthylsufonamido, etc.), alkyl-sulfamoyl radicals (such as, e.g., butyl-sulfamoyl, etc.), aryl-sulfamoyl radicals (such as, e.g., phenyl-sulfamoyl, etc.), alkoxycarbonyl radicals (such as, e.g., methyloxycarbonyl, etc.), aryloxycarbonyl radicals (such as, e.g., phenyloxycarbonyl, etc.), aminosulfonamido radical, acylamino radicals, carbamoyl radical, sulfonyl radical, sulfinyl radical, sulfoxy radical, sulfo radical, aryloxy radicals, alkoxy radicals, carboxyl radical, alkyl-carbonyl radicals, aryl-carbonyl radicals, aminocarbonyl radical, and the like. Not less than two of these substituents may be introduced to the phenyl radical. The preferred radicals represented by R 1 include phenyl radical or .Iadd.phenyl radicals having a single or a plurality of substituents (which are typified by .Iaddend.halogens, alkyl-sulfonamido radicals, aryl-sulfonamido radicals, alkyl-sufamoyl radicals, aryl-sulfamoyl radicals, alkyl-sulfonyl radicals, aryl-sulfonyl radicals, alkyl-carbonyl radicals, aryl-carbonyl radicals, and .[.phenyl radicals having one or not less than two.]. cyano radicals .[.as substituents.]..Iadd.).Iaddend. .

The alkyl radical represented by R 2 includes those in the straight chain or branched chain form, such as methyl, ethyl, propyl, butyl, octyl, and the like radicals.

The preferred cyan couplers having Formula .[.[I].]. .Iadd.I .Iaddend.in the present invention include those compounds having the following Formula .[.[III].]..Iadd.III.Iaddend.: ##STR3## wherein R 7 represents a phenyl radical which is allowed to have a single or a plurality of substituents which are typified by a halogen atom (such as fluorine, chlorine, bromine, etc.), an alkyl radical (such as, e.g., methyl, ethyl, propyl, butyl, octyl, dodecyl, etc.), a hydroxy radical, a cyano radical, a nitro radical, an alkoxy radical (such as, e.g., methoxy, ethoxy, etc.), an alkyl-sulfonamido radical (such as, e.g., methyl-sulfonamido, octyl-sulfonamido, etc.), an aryl-sulfonamido radical (such as, e.g., phenyl-sulfonamido, .[.napththyl-sulfonamido.]. .Iadd.naphthyl-sulfonamido.Iaddend., etc.), an alkyl-sulfamoyl radical (such as, e.g., butyl-sulfamoyl, etc.), an aryl-sulfamoyl radical (such as, e.g., phenyl-sulfamoyl, etc.), an alkyloxycarbonyl radical (such as, e.g., methyloxycarbonyl, etc.), an aryloxycarbonyl radical (such as, e.g., phenyloxycarbonyl, etc.), and the like. Not less than two of these substituents may be introduced to the phenyl radical.

The preferred radical represented by R 7 is a phenyl radical .[.having such one substituent or not less than two substituents as phenyl radicals or.]. .Iadd.or phenyl radicals having a single or a plurality of substituents (which are typified by .Iaddend.halogens (preferably fluorine or bromine), alkyl-sulfonamido radicals (preferably O-methyl-sulfonamido, p-octyl-sulfonamido, o-dodecyl-sulfonamido), aryl-sulfonamido radicals (preferably phenyl-sulfonamido), alkyl-sulfamoyl radicals (preferably butyl-sulfamoyl), aryl-sulfamoyl radicals (preferably phenyl-sulfamoyl), alkyl radicals (preferably methyl, trifluoromethyl), or alkoxy radicals (preferably methoxy, ethoxy).Iadd.).Iaddend..

R 8 is an alkyl or aryl radical. The alkyl radical or the aryl radical is allowed to have a single or a plurality of substituents which may be typified by halogens (such as, e.g., fluorine, chlorine, bromine, etc.), hydroxyl radical, carboxyl radical, alkyl radicals (such as, e.g., methyl, .[.ethy.]. .Iadd.ethyl.Iaddend., propyl, butyl, octyl, dodecyl, etc.), aralkyl radicals, cyano radical, nitro radical, alkoxy radicals (such as e.g., methoxy, ethoxy, etc.), aryloxy radicals, alkyl-sulfonamido radicals (such as, e.g., methyl-sulfonamido, octyl-sulfonamido, etc.), aryl-sulfonamido radicals (such as, e.g., phenyl-sulfonamido, naphthyl-sulfonamido, etc.), alkyl-sulfamoyl radicals (such as, e.g., butyl-sulfamoyl, etc.), aryl-sulfamoyl radicals (such as, e.g., phenyl sulfamoyl, etc.), alkyloxycarbonyl radicals (such as, e.g., methyloxycarbonyl, etc.), aryloxycarbonyl radicals (such as e.g., phenyloxycarbonyl, etc.), aminosulfonamido radicals (such as, e.g., dimethylaminosulfonamido, etc.) alkyl-sulfonyl radicals, aryl-sulfonyl radicals, alkyl-carbonyl radicals, aryl-carbonyl radicals, aminocarbonylamido radical, carbamoyl radical, sulfinyl radical, and the like. Not less than two of these substituents may be introduced to the alkyl or aryl radical.

The preferred radical represented by R 8 , when the n is equal to 0, is an alkyl and, when the n is equal to more than 1, is an aryl. The further preferred radical represented by R 8 is a phenyl radical having .[.such one substituent or not less than two.]. substituents as, when the n is equal to 0, alkyl radicals having from 1 to 22 carbon atoms (preferably methyl, ethyl, propyl, butyl, octyl, dodecyl) and, when the n is equal to one or more than 1, phenyl, or alkyl radicals (preferably t-butyl, t-amyl, octyl), alkyl-sulfonamido radicals (preferably butyl-sulfonamido, octyl-sulfonamido, dodecyl-sulfonamido), aryl-sulfonamido radicals (preferably phenyl-sulfonamido), aminosulfonamido radicals (preferably dimethylaminosulfonamido), or alkyloxycarbonyl radicals (preferably methyloxycarbonyl, butyloxycarbonyl.Iadd.).Iaddend..

.Iadd.R 9 represents an alkylene radical. .Iaddend.R 9 represents a straight-chain or branched-chain alkylene having from 1 to 20 carbon atoms, and more preferably from 1 to 12 carbon atoms.

R 10 is a hydrogen atom or a halogen atom (fluorine, chlorine or bromine), and preferably a hydrogen atom.

n is 0 or .[.an.]. .Iadd.a .Iaddend.positive integer and preferably 0 to 5, more preferably 0 to 1.

X is a divalent radical such as --O--, --CO--, --COO--, --OCO--, --SO 2 NR'--, NR'SO 2 NR"--, --S--, --SO-- or --SO 2 -- wherein R' and R" each is a substituted or unsubstituted alkyl radical, and preferably --O--, --S--, --SO-- and --SO 2 --.

Z 3 is a hydrogen atom, a halogen atom, or a radical that can be split off by the reaction of the coupler with the oxidized product of an aromatic primary amine-type color developing agent, the radical being preferably a chlorine atom or a fluorine atom.

The following are typical examples of the cyan coupler having Formula .[.[I].]. .Iadd.I.Iaddend., but the present invention is not limited thereto. ##STR4##

The cyan couplers having Formula [II] in the present invention are more preferably those compounds having the following Formula [IV]: ##STR5## wherein R 11 and R 12 may be either the same or different from each other and each is a hydrogen atom, an alkyl radical (such as, e.g., methyl, ethyl, propyl, butyl, amyl, octyl, dodecyl, etc.) or an alkoxy radical (such as, e.g., methoxy, ethoxy, etc.), provided that the sum of the carbon atoms of R 11 and R 12 is from 8 to 16, and more preferably R 11 and R 12 each is a butyl or amyl radical; R 13 is a hydrogen atom or an alkyl radical (such as, e.g., methyl, ethyl, propyl, butyl, octyl, etc.), and preferably a hydrogen atom, ethyl or butyl radical; m is an integer of up to 2; and Z 4 is a hydrogen atom, a halogen atom, or a radical that can be split off by the reaction of the coupler with the oxidized product of an aromatic primary amine-type color developing agent.

In Formulas [I], [II], [III] and [IV], the radicals that can be split off by the reaction of these couplers with the oxidized product of the aromatic primary amine-type color developing agents represented by Z 1 , Z 2 , Z 3 and Z 4 are all known to those skilled in the art. Any of these radicals changes the reactivity of the coupler or is split from the coupler to fulfill its development-inhibiting, bleach-inhibiting and color-compensation functions to thereby advantageously act in the coupler-containing layers or other layers of the silver halide color photographic light-sensitive material. Typical examples of such radicals include, for example, alkoxy radicals, aryloxy radicals, arylazo radicals, thioether, carbamoyloxy radical, acyloxy radicals, imido radical, sulfonamido radical, thiocyano radical or heterocyclic radicals (such as, e.g., oxazolyl, diazolyl, triazolyl, tetrazolyl, etc.), and the like. The particularly preferred examples represented by Z are a hydrogen atom or a chlorine atom.

The following are typical examples of those cyan couplers having Formula [II], but the present invention is not limited thereto. ##STR6##

In the case of using in combination the cyan coupler having Formula [I] of the invention and the cyan coupler having Formula [II] of the invention, there may be used at least one of these cyan couplers having Formula [I] and at least one of these cyan couplers having Formula [II] in an arbitrary proportion in the combination thereof, but it is desirable that of the total amount of the cyan couplers the cyan coupler having Formula [II] be used in the quantity so as to account for from 30 to 90 mole%, and more preferably from 50 to 90 mole%.

The silver halide color photographic light-sensitive material of the present invention is allowed to be of any construction as long as it comprises a support having thereon at least one silver halide emulsion layer, and no particular restrictions are placed on the number of and the coating order of silver halide emulsion layers and non-light-sensitive layers. Typical examples of the light-sensitive material include color positive or negative films, color photographic printing papers, color slides, and those light-sensitive materials for special use such as for graphic arts use, radiography use, and high-resolution applications, and the like, and particularly suitable for use as color photographic printing papers. Most of the foregoing silver halide emulsion layers and non-light-sensitive layers are usually comprised of hydrophilic binder-containing hydrophilic colloidal layers. As the hydrophilic binder, there may be preferably used gelatin or gelatin derivatives such as acylated gelatin, guanidylated gelatin, carbamylated gelatin, cyanoethanolated gelatin, esterified gelatin, and the like.

These cyan couplers having Formulas [I] and [II] (hereinafter referred to as the cyan coupler(s) of the present invention) may be incorporated by the application of the method for use in ordinary cyan dye-forming couplers thereto into silver halide emulsion layers, the layers being coated on a support, thereby forming a photographic element. The photographic element is allowed to be either a monochromatic element or multicolor element. In the case of the multicolor element, the cyan coupler of the present invention is usually incorporated into the red-sensitive silver halide emulsion layer, but may be allowed in a nonlight-sensitive emulsion layer or emulsion layer that is sensitive to three-primary-color regions excluding the red. Each component unit capable of forming a dye image in the present invention is a single or one of a plurality of emulsion layers, having sensitivity to each given spectral region.

The cyan coupler of the present invention may be incorporated into an emulsion in accordance with any of conventionally known methods. For example, the cyan coupler is dissolved separately into such a single high-boiling organic solvent as a phthalate (dibutyl phthalate, etc.), a phosphate (tricresyl phosphate, etc.) or a N,N-dialkyl-substituted amide (N,N-diethyl-laurylamide, etc.) and into such a single low-boiling organic solvent as butyl acetate or butyl propionate, or dissolved into, if necessary, a mixture of the high-boiling and low-boiling organic solvents. After that, the solution is mixed with an aqueous gelatin solution containing a surfactant, and then emulsified to be dispersed by use of a high-speed mixer, a colloid mill or a ultrasonic disperser. The resulting dispersed liquid is subsequently added to a silver halide, whereby a silver halide emulsion for use in the present invention can be prepared.

The cyan coupler of the present invention may be added to the silver halide emulsion usually within the quantity range of from about 0.05 to about 2 moles per mole of silver halide, and preferably from 0.1 to 1 mole per mole of silver halide.

In the case where the silver halide color photographic light-sensitive material of the present invention is a multicolor element, all the layers including the above image forming component unit layers required for the photographic element may be coated in various orders as is known to those skilled in the art. The typical multicolor photographic element is one that comprises a support having thereon a cyan dye image-formable component unit consisting of at least one red-sensitive silver halide emulsion layer containing a cyan dye forming coupler (at least one of the cyan dye forming couplers is the cyan coupler of the present invention having Formula [I] and at least further one of the cyan couplers is the cyan coupler of the present invention having Formula [III]); a magenta dye image-formable component unit consisting of at least one green-sensitive silver halide emulsion layer containing at least one magenta dye forming coupler; and a yellow dye image-formable component unit consisting of at least one blue-sensitive silver halide emulsion layer containing at least one yellow dye forming coupler.

The photographic element may have additional layers; such nonlight-sensitive layers as filter layers, interlayers, a protective layer, an antihalation layer, a subbing layer, and the like.

As the yellow dye forming coupler usable in the present invention there may be suitably used those compounds having the following Formula [V]: ##STR7##

wherein R 14 represents an alkyl radical (such as, e.g., methyl, ethyl, propyl, butyl, etc.) or an aryl radical (such as, e.g., phenyl, p-methoxyphenyl, etc.); R 15 represents an aryl radical; and Y represents a hydrogen atom or a radical which can be split off during the course of a color developing reaction).

Further, particularly preferred as the yellow coupler capable of forming a dye image in the present invention are those compounds having the following Formula [VI]: ##STR8## wherein R 16 is a halogen atom, an alkoxy radical or an aryloxy radical; R 17 , R 18 and R 19 each is a hydrogen atom, a halogen atom, an alkyl radical, an alkenyl radical, an alkoxy radical, an aryl radical, an aryloxy radical, a carbonyl radical, a sulfonyl radical, a carbonyl radical, an alkoxycarbonyl radical, a carbonyl radical, a sulfone radical, a sulfamyl radical, a sulfonamido radical, an acylamido radical, an ureido radical or an amido radical; and Y is as defined previously.

These are as described in, for example, U.S. Pat. Nos. 2,778,658, 2,875,057, 2,908,573, 3,227,155, 3,227,550, 3,253,924, ,265,506, 3,277,155, 3,341,331, 3,369,895, 3,384,657, 3,408,194, 3,415,652, 3,447,928, 3,551,155, 3,582,322, 3,725,072, 3,894,875, West German OLS Patent Nos. 1,547,868, 2,057,941, 2,162,899, 2,163,812, 2,213,461, 2,219,917, 2,261,361, 2,263,875, Japanese Patent Examined Publication No. 13576/1974, Japanese Patent O.P.I. Publication Nos. 29432/1973, 66834/1973, 10736/1974, 122335/1975, 28834/1975 and 132926/1975, and the like.

As the magenta dye image forming coupler, there may be preferably used those couplers having the following Formula [VII]: ##STR9## wherein Ar is an aryl radical; R 20 is a hydrogen atom, a halogen atom, an alkyl radical or an alkoxy radical; R 21 is an alkyl radical, an amido radical, an imido radical, an N-alkylcarbamoyl radical, an N-alkyl-sulfamoyl radical, an alkyloxycarbonyl radical, an acyloxy radical, a sulfonamido radical, or an urethane radical; Y is as defined in Formula [V]; and W is --NH--, --NHCO-- (wherein the N atom is bonded with the carbon atom of pyrazolone nucleus) or --NHCONH--.

These are as described in, e.g., U.S. Pat. Nos. 2,600,788, 3,061,432, 3,062,653, 3,127,269, 3,311,476, 3,152,896, 3,419,391, 3,519,429, 3,555,318, 3,684,514, 3,888,680, 3,907,571, 3,928,044, 3,930,861, 3,930,866, 3,933,500, Japanese Patent O.P.I. Publication Nos. 29639/1974, 111631/1974, 129538/1974, 13041/1975, 58922/1977, 62454/1980, 118034/1980, 38043/1981, British Pat. No. 1,247,493, Belgian Pat. Nos. 769,116 and 792,525, West German Pat. No. 2,156,111, Japanese Patent Examined Publication No. 60479/1971, and the like.

The following are typical examples of the yellow and magenta dye image forming couplers which are suitably usable in the present invention, but the present invention is not limited thereto.

Yellow Couplers

(Y-1) α-benzoyl-2-chloro-5-[α-(dodecyloxycarbonyl)ethoxycarbonyl]-acetanilide.

(Y-2) α-benzoyl-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)butylamido]-acetanilide.

(Y-3) α-fluoro-α-pivalyl-2-chloro-5-[α-(2,4-di-t-amylphenoxy)butylamido]-acetanilide.

(Y-4) α-pivalyl-α-stearoyloxy-4-sulfamoyl-acetanilide.

(Y-5) α-pivalyl-α-[4-(4-benzyloxyphenyl-sulfonyl)phenoxy]-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)butylamido]-acetanilide.

(Y-6) α-(2-methoxybenzoyl)-α-(4-acetoxyphenoxy)-4-chloro-2-(4-t-octylphenoxy)-acetanilide.

(Y-7) α-pivalyl-α-(3,3-dipropyl-2,4-dioxo-acetidin-1-yl)-2-chloro-5-[α-(dodecyloxycarbonyl)-ethoxycarbonyl]-acetanilide.

(Y-8) α-pivalyl-α-succinimido-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)butylamido]-acetanilide.

(Y-9) α-pivalyl-α-(3-tetradecyl-1-succinimido)-acetanilide.

(Y-10) Dipotassium α-(4-dodecyloxybenzoyl)-α-(3-methoxy-1-succinimido)-3,5-dicarboxyacetanilide.

(Y-11) α-pivalyl-α-phthalimido-2-chloro-5-[α-2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-12) α-2-furyl-60-phthalimido-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-13) α-3-[α-(2,4-di-t-amylphenoxy)-butylamido]-benzoyl-α-succinimido-2-methoxyacetanilide.

(Y-14) α-phthalimido-α-pivalyl-2-methoxy-4-[(N-methyl-N-octadecyl)-sulfamoyl]-acetanilide.

(Y-15) α-acetyl-α-succinimido-2-methoxy-4-[(N-methyl-N-octadecyl)-sulfamoyl]-acetanilide.

(Y-16) α-cyclobutyryl-α-(3-methyl-3-ethyl-1-succinimido)-2-chloro-5-[(2,5-di-t-amylphenoxy)acetamido]-acetanilide.

(Y-17) α-(3-octadecyl-1-succinimido)-α-propanoyl-acetanilide.

(Y-18) α-(2,6-di-oxo-3-n-propyl-piperidine-1-yl)-α-pivalyl-2-chloro-5-[α-(2,4-di-t-amylphenoxy)-butyl-carbamoyl]-acetanilide.

(Y-19) α-(1-benzyl-2,4-dioxo-imidazolidine-3-yl)-α-pivalyl-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-20) α-(1-benzyl-2-phenyl-3,5-dioxo-1,2,4-triazine-4-yl)-α-pivalyl-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)-butylamido]acetanilide.

(Y-21) α-(3,3-dimethyl-1-succinimido)-α-pivalyl-2-chloro-5-[α-(2,4-di-t-amylphenoxy)-butylamido]acetanilide.

(Y-22) α-[3-(p-chlorophenyl)-4,4-dimethyl-2,5-dioxo-1-imidazolyl]-α-pivalyl-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-23) α-pivalyl-α-(2,5-dioxo-1,3,4-triazine-1-yl)-2-methoxy-5-[.alpha.-(2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-24) α-(5-benzyl-2,4-dioxo-3-oxazoyl)-α-pivalyl-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-25) α-(5,5-dimethyl-2,4-dioxo-3-oxazoyl)-α-pivalyl-2-chloro-5-[.alpha.-(2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-26) α-(3,5-dioxo-4-oxadinyl)-α-pivalyl-2-chloro-5-γ-(2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-27) α-pivalyl-α-(2,4-dioxo-5-methyl-3-thiazolyl)-2-chloro-5-[.gamma.-(2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-28) α-[3-(2H)-pyridazone-2-yl]-α-pivalyl-2-chloro-5-[γ-2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-29) α-[4,5-dichloro-3(2H)-pyridazone-2-yl]-α-benzoyl-2-chloro-5-[.alpha.-(dodecyloxycarbonyl)-ethoxycarbonyl]-acetanilide.

(Y-30) α-(1-phenyl-tetrazole-5-oxy)-α-pivalyl-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)-butylamido]-acetanilide.

(Y-31) 4,4'-di-(acetacetamino)-3,3-dimethyl-diphenylmethane.

(Y-32) P,P'-di-(acetacetamino)-diphenyl-methane.

Magenta Couplers

(M-1) 1-(2,4,6-trichlorophenyl)-3-(2-chloro-5-octadecyl-carbamoyl-anilino)-5-pyrazolone.

(M-2) 1-(2,4,6-trichlorophenyl)-3-(2-chloro-5-tetradecanamidoanilino)-5-pyrazolone.

(M-3) 1-(2,4,6-trichlorophenyl)-3-[2-chloro-5-γ-(2,4-di-t-amylphenoxy)-butyl-carbamoyl]-anilino-5-pyrazolone.

(M-4) 1-(2,4,6-trichlorophenyl)-4-chloro-3-[2-chloro-5-γ-(2,4-di-t-amylphenoxy)-butyl-carbamoyl]-anilino-5-pyrazolone.

(M-5) 1-(2,4,6-trichlorophenyl)-4-diphenyl-methyl-3-[2-chloro-5-(γ-octadecenylsuccinimido)-propyl-sulfamoyl]-anilino-5-pyrazolone.

(M-6) 1-(2,4,6-trichlorophenyl)-4-acetoxy-5-(2-chloro-5-tetradecaneamido)-anilino-5-pyrazolone.

(M-7) 1-[γ-(3-pentadecylphenoxy)-butylamido]-phenyl-3-anilino-4-(1-phenyl-tetrazole-5-thio)-5-pyrazolone.

(M-8) 1-(2,4,6-trichlorophenyl)-3-(2-chloro-5-octadecylsuccinimido)-anilino-5-pyrazolone.

(M-9) 1-(2,4,6-trichlorophenyl)-3-(2-chloro-5-octadecenylsuccinimido)-anilino-5-pyrazolone.

(M-10) 1-(2,4,6-trichlorophenyl)-3-[2-chloro-5-(N-phenyl-N-octyl-carbamoyl)]-anilino-5-pyrazolone.

(M-11) 1-(2,4,6-trichlorophenyl)-3-[2-chloro-5-(N-butyl-carbonyl)-pyrazinyl-carbonyl]-anilino-5-pyrazolone.

(M-12) 1-(2,4,6-trichlorophenyl)-3-[2-chloro-5-(2,4-dicarboxy-5-phenyl-carbamoyl)-benzylamido]-anilino-5-pyrazolone.

(M-13) 1-(2,4,6-trichlorophenyl)-3-(4-tetradecyl-thiomethylsuccinimido)-anilino-5-pyrazolone.

(M-14) 1-(2,4,6-trichlorophenyl)-3-[2-chloro-4-(2-benzofurylcarboxyamido)]-anilino-5-pyrazolone.

(M-15) 1-(2,4,6-trichlorophenyl)-3-{2-chloro-4-[γ-(2,2-dimethyl-6-octadecyl-7-hydroxy-chroman-4-yl)-propionamido]}-anilino-5-pyrazolone.

(M-16) 1-(2,4,6-trichlorophenyl)-3-[2-chloro-5-(3-pentadecylphenyl)-phenylcarboamido]-anilino-5-pyrazolone.

(M-17) 1-(2,4,6-trichlorophenyl)-3-{2-chloro-5-[2-(3-t-butyl-4-hydroxyphenoxy)-tetradecanamido]-anilino}-5-pyrazolone.

(M-18) 1-(2,6-dichloro-4-methoxyphenyl)-3-(2-methyl-5-tetradecanamido)-anilino-5-pyrazolone.

(M-19) 4,4'-benzylidene-bis-[1-(2,4,6-trichlorophenyl)-3-{2-chloro-4-[γ-(2,4-di-t-amylphenoxy)-butylamido]-anilino}-5-pyrazolone.

(M-20) 4,4'-benzylidene-bis[1-(2,3,4,5,6-pentachlorophenyl-3-2-chloro-5-[γ-(2,4-di-t-amylphenoxy)-butylamido]-anilino]-5-pyrazolone.

(M-21) 4,4'-(2-chloro)-benzylidene-bis-[1-(2,4,6-trichlorophenyl)-3-(2-chloro-5-dodecylsuccinimido)-anilino]-5-pyrazolone.

(M-22) 4,4'-benzylidene-bis-[1-(2-chlorophenyl)-3-(2-methoxy-4-hexadecanamido)-anilino-5-pyrazolone].

(M-23) 4,4'-methylene-bis[1-(2,4,6-trichlorophenyl)-3-(2-chloro-5-dodecenylsuccinimido)-anilino-5-pyrazolone)].

(M-24) 1-(2,4,6-trichlorophenyl)-3-[3-(2,4-di-t-amylphenoxyacetamido)-benzamido]-5-pyrazolone.

(M-25) 3-ethoxy-1-4-[α-(3-pentadecenylphenoxy)-butylamido]-phenyl-5-pyrazolone.

(M-26) 1-(2,4,6-trichlorophenyl)-3-[2-chloro-5-{α-(3-t-butyl-4-hydroxy)-phenyl}-tetradecanamido]-anilino-5-pyrazolone.

(M-27) 1-(2,4,6-trichlorophenyl)-3,3-nitriloanilino-5-pyrazolone.

Any of these yellow dye forming couplers and magenta dye forming couplers may be incorporated into a silver halide emulsion layer within the quantity range of from 0.05 to 2 moles per mole of silver halide.

For the support of the light-sensitive material of the present invention, any of those materials may be used such as, for example, baryta paper, polyethylene-coated paper, polypropylene-synthetic paper, a transparent support material provided with a reflective layer or material, a glass plate, cellulose acetate, cellulose nitrate, polyester film such as polyethylene terephthalate, polyamide film, polycarbonate film, polystyrene film, and the like. These support materials may be arbitrarily selected according to the purpose for which is used the silver halide photographic light-sensitive material of the present invention.

The coating process for use in coating the silver halide emulsion layers and nonlight-sensitive layers of the light-sensitive material of the present invention includes such various processes as the dipping coating process, air-doctor coating process, curtain coating process, hopper coating process, and the like.

The silver halide used for the silver halide emulsion of the present invention includes those arbitrarily used for ordinary silver halide emulsions: silver bromide, silver chloride, silver iodobromide, silver chlorobromide, silver chloroidobromide, and the like. The particles of these silver halides are allowed to be either coarse-grained or fine-grained, and be of either wide or narrow particle-size distribution.

The crystal of these silver halide particles may be either regular or twin, and those having an arbitrary proportion of its [100] face to [111] face can be used. Further the crystal structure of these silver halide particles may be either homogeneous from the inside to the outside thereof or heterogeneous between the inside and the outside thereof. Furthermore, these silver halides may be either of the type of forming a latent image mainly on the surface of the particles thereof or of the type of forming it inside the particles thereof. In addition, these silver halides may be prepared by any of the neutral method, ammoniacal method and acid method, and silver halide particles produced by any of the simultaneous mixing method, sequential mixing method and conversion method may be applied.

The silver halide emulsion of the present invention can be chemically sensitized by the single or combined use of sulfur sensitizers such as, e.g., aryl-thiocarbamide, thiourea, cystine, etc.; active or insert selenium sensitizers; reduction sensitizers such as, e.g., stannous salts, polyamides, etc.; noble-metallic sensitizers including such gold sensitizers as sodium aurithiocyanate, potassium chloroaurate, 2-aurosulfobenzothiazolemethyl chloride, etc., water-soluble-salt sensitizers such as of ruthenium, rhodium, iridium, etc., and ammonium chloropalladate, potassium chloropalladate, sodium chloropalladite, and the like.

Into the silver halide emulsion of the invention may be incorporated various known photographic additives such as those described in, e.g., Research Disclosure No. 17643, December 1978.

The silver halide emulsion of the invention, in order to be provided with sensitivity to the necessary wavelength region for a red-sensitive emulsion is spectrally sensitized by the addition thereto of an appropriately selected sensitizing dye. As the spectral sensitizer, various sensitizing dyes may be used singly or in combination.

Advantageously applicable spectral sensitizers to the invention include such typical cyanine dyes, merocyanine dyes, and complex cyanine dyes as described in U.S. Pat. Nos. 2,269,234, 2,270,378, 2,442,710 and 2,454,620.

Other additives may also be arbitrarily incorporated into the silver halide emulsion layers and nonlight-sensitive layers of the silver halide photographic light-sensitive material of the present invention, the additives including antifoggants, antistain agents, brightening agents, antistatic agents, hardening agents, plasticizers, wetting agents, ultraviolet absorbing agents, and the like, as described in Research Disclosure No. 17643.

The thus constructed silver halide photographic light-sensitive material of the present invention, after being exposed to light, is then developed by the color development process including various photographic processing procedures. The preferred color developer liquid usable in the invention is one that contains an aromatic primary amine-type color developing agent as the principal component thereof, the color developing agent being typified by p-phenylenediamine-type compounds including, for example, diethyl-p-phenylenediamine hydrochloride, monomethyl-p-phenylenediamine hydrochloride, dimethyl-p-phenylenediamine hydrochloride, 2-amino-5-diethylaminotoluene hydrochloride, 2-amino-5-(N-ethyl-N-dodecylamino)-toluene, 2-amino-5-(N-ethyl-N-β-methanesulfonamidoethyl)aminotoluene sulfate, 4-(N-ethyl-N-β-methanesulfonamidoethylamino)-aniline, 4-(N-ethyl-N-β-hydroxyethylamino)aniline, 2-amino-5-(N-ethyl-β-methoxyethyl)aminotoluene, and the like.

These color developing agents may be used singly or in combination, or used together with hydroquinone or the like. Further, the color developer liquid contains generally alkali agents such as sodium hydroxide, ammonium hydroxide, sodium carbonate, sodium sulfite or the like, and may also contains various additives including such halogenated alkaline metals as, e.g., potassium bromide, and development control agents such as, e.g., hydrazinic acid, and the like.

The silver halide photographic light-sensitive material of the present invention may contain in the hydrophilic colloidal layers thereof the foregoing color developing agent as it is or in the form of the precursor thereof. The color developing agent precursor is a compound capable of producing a color developing agent under an alkaline condition, the precursor including aromatic aldehyde derivative-Schiff's base-type precursors, multivalent metallic ion complex precursors, phthalic acid imide derivative precursors, phosphoric acid imide derivative precursors, sugar-amine reaction product precursors and urethane-type precursors. These aromatic primary amine color developing agent precursors are as described in, e.g., U.S. Pat. Nos. 3,342,599, 2,507,114, 2,695,234, 3,719,493, British Pat. No. 803,783, Japanese Patent O.P.I. Publication Nos. 135628/1978 and 79035/1979, and Research Disclosure Nos. 15,159, 12,146 and 13,924. Any of these aromatic primary amine color developing agents or precursors thereof should be added in a quantity enough to obtain a sufficient color formation during the development process. The quantity largely differs according to the kind of the light-sensitive material used, but is used within the range of from about 0.1 mole to 5 moles, and preferably from 0.5 mole to 3 moles per mole of light-sensitive silver halide. These color developing agents or precursors may be used singly or in combination. Into the photographic light-sensitive material may be incorporated any of the foregoing compounds in the form of a solution of it dissolved into an appropriate solvent such as water, methanol, ethanol, acetone or the like, or in the form of a dispersed liquid of it with use of a high-boiling organic solvent such as dibutyl phthalate, dioctyl phthalate, tricresyl phosphate or the like, or in the form of it impregnated into a latex polymer as described in Research Disclosure No. 14850.

The silver halide photographic light-sensitive material of the present invention, after color development, is usually subjected to a bleach-fix bath processing or to separate bleaching and fixing treatments and then washed in water. As the bleaching agent, there may be used many compounds, among which multivalent metallic compounds such as of iron(III), cobalt(III), tin(II), and the like, especially complex salts of these metallic cations with organic acids, such as, for example, metallic complex salts, ferricyanates or dichromates of ethylenediamine-tetraacetic acid, nitrilotriacetic acid, aminopolycarboxylic acids such as N-hydroxyethylethylenediamine-diacetic acid, malonic acid, tartaric acid, malic acid, diglycolic acid, dithioglycolic acid, and the like, may be used singly or in combination.

According to the silver halide photographic light-sensitive material of the present invention, the solubility, dispersibility and dispersion stability of the cyan coupler of the invention contained in the silver halide emulsion layer are so good that no such trouble as deposition of the coupler will occur. The cyan coupler is excellent in the spectral absorbing characteristic as well as in the color tone and capable of forming a clear dye image in an extensive color reproduction range; particularly a cyan dye image having the maximum absorption in the wavelength range of form 640 to 660 nm and having little or no absorption in the regions of from 400 to 450 nm, from 450 to 480 nm, and from 500 to 550 nm, so that the coupler produces very excellent blue and green color reproductions with very satisfactory lightness with no trouble at all. Besides, the formed dye image is also excellent in the resistance to light, heat and moisture as well as in its preservability.

The present invention will be illustrated further in detail in reference to examples below, but embodiments of the present invention are not limited thereto.

__________________________________________________________________________

29 I-5, 100

-- -- 102 122

84 100

0.77

0.89

0.88

0.98

0.99

0.98

Comparative

Invention

30 I-5, 80

II-3, 20

-- 112 121

98 100

0.87

0.88

0.88

0.97

0.98

0.97

Comparative

Invention

31 I-5, 60

II-3, 40

-- 114 120

99 100

0.90

0.90

0.87

0.95

0.99

0.97

Comparative

Invention

32 I-5, 80

II-1, 20

-- 112 121

98 100

0.89

0.89

0.88

0.96

0.99

0.98

Comparative

Invention

33 I-37, 100

-- -- 95 118

83 100

0.40

0.88

0.87

0.99

0.98

0.98

Comparative

Invention

34 I-37, 80

II-3, 20

-- 109 117

99 100

0.80

0.90

0.88

0.97

0.99

0.98

Comparative

Invention

35 I-4, 100

-- -- 99 120

85 100

0.62

0.89

0.89

0.98

0.99

0.97

Comparative

Invention

36 I-4, 60

II-3, 40

-- 111 119

100 100

0.85

0.90

0.89

0.97

0.99

0.98

Comparative

Invention

37 -- II-3, 100

-- 100 100

100 100

0.90

0.91

0.88

0.64

0.98

0.97

Comparative

Invention

38 -- II-1, 100

-- 100 100

100 100

0.90

0.90

0.88

0.65

0.98

0.97

Comparative

Invention

39 -- -- C-1, 100

92 95

91 100

0.71

0.88

0.88

0.62

0.99

0.99

Comparative

Invention

40 I-5, 60

-- C-1, 40

93 97

87 100

0.71

0.88

0.88

0.84

0.98

0.97

Comparative

Invention

41 -- -- C-2, 100

90 95

90 100

0.74

0.88

0.89

0.60

0.98

0.98

Comparative

Invention

42 I-5, 60

-- C-2, 40

92 98

86 100

0.73

0.88

0.89

0.86

0.99

0.98

Comparative

Invention

43 -- -- C-3, 100

91 96

91 100

0.44

0.85

0.88

0.81

0.99

0.98

Comparative

Invention

44 I-5, 60

-- C-3, 40

93 103

84 100

0.52

0.86

0.87

0.88

0.99

0.98

Comparative

Invention

__________________________________________________________________________

As apparent from Table 3, the multicolor photographic elements which use the cyan couplers of the present invention show much improved blue color reproductions with clear dye images formed in a wide color reproduction region without any adverse effect on the green color reproduction, and further show well-balanced degree of cyan-magenta-yellow discoloration, thus showing much improved dye image stability on the whole.

Monochromatic photographic element samples were prepared in the same manners as in previous examples with the exception that Exemplified Couplers I-16, I-36, I-33, II-4 and II-5 were used in place of the I-5, I-37, I-4, II-3 and II-1, respectively, and Comparative Couplers-4, -5 and -6 in place of the Comparative Couplers-1, -2 and -3.

The thus obtained 14 different samples were used for the same tests as in Example 1. As a result, the silver halide color photographic light-sensitive material samples of the present invention have less undesirable absorptions in 550 nm and 420 nm and lower reflection minimum densities than do the silver halide color photographic light-sensitive material samples containing those of Formula [I] alone, so that the samples of the present invention form high lightness and satisfactory spectral reflection characteristics--having dye images. And the formed dye images display very satisfactory light stability and dark stability characteristics. ##STR12##

Similar multicolor photographic element samples to the multicolor photographic element samples of Example 3 were prepared in the same manners as in Example 3 with the exception that the exemplified couplers were replaced by those used in Example 4, respectively, and the YC-1, MC-1 and UV-1 were replaced by the following YC-2, MC-2 and UV-2, respectively.

The thus obtained 14 different samples were subjected to the same tests as in Example 3. As a result, the cyan couplers of the present invention--used multicolor photographic element samples show improved red, green and blue color reproductions, particularly the conspicuous improvement on the blue-color reproduction, with clear dye image formed in a wide color reproduction region, and also show well-balanced degree of cyan-magenta-yellow discoloration, thus showing much improved image preservability on the whole.